Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Preparation method for synthesizing artificial leather by nano bamboo charcoal UV

A technology of artificial leather and nano-bamboo carbon, applied in chemical instruments and methods, textiles and papermaking, lamination, etc., can solve problems such as no research, and achieve the effect of environmental protection function and simple process

Active Publication Date: 2015-04-08
杭州苏威家居科技有限公司
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Combining bamboo with artificial leather is still relatively rare at present, and how to combine bamboo with people's extensive demand for artificial leather is still unresearched

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0064] The preparation method of the adopted nano-bamboo powder is as follows: the natural bamboo and bamboo chips are first impregnated in an alkaline solution, then the fibers are softened after 1-10 days, then ground by a high-speed grinder, and then filtered through an 80-mesh filter screen, and then Dry, remove the water, and grind again into 100-500nm ultrafine powder by nano-grinding equipment.

[0065] The preparation method of the nano-bamboo charcoal powder used is as follows: natural bamboo is first dried, then calcined at high temperature and high pressure to become bamboo charcoal, then ground by a high-speed grinder, filtered through an 80-mesh filter, and ground again into 100- 500nm ultrafine powder.

Embodiment 1

[0067] A kind of preparation method of colored nanometer bamboo carbon water-based PU synthetic artificial leather, comprises the following steps:

[0068] (1) Dosing room: prepare the first layer of compounding liquid, the second layer of compounding liquid and the third layer of compounding liquid respectively for use; among them, in the following formulas, each portion is 1kg;

[0069] The water-based formulation of the first layer of compounding solution is calculated in parts by weight: 100 parts of water-based PU resin, 50 parts of nano-bamboo charcoal powder or nano-bamboo powder, 0 parts of wear-resistant agent, thickener: 2 parts of polyethylene glycol, dispersed Agent: 1 part of block polymer dispersant, flame retardant: 1 part of fluorinated polymer;

[0070] The formula of the second layer of compounding solution is calculated in parts by weight: 100 parts of water-based PU resin, 50 parts of nano bamboo charcoal powder or nano bamboo powder, dispersant: 1 part of ...

Embodiment 2

[0084] A kind of preparation method of colored nanometer bamboo carbon water-based PU synthetic artificial leather, comprises the following steps:

[0085] (1) Dosing room: prepare the first layer of compounding liquid, the second layer of compounding liquid and the third layer of compounding liquid respectively for use; among them, in the following formulas, each portion is 1kg;

[0086] The oily formulation of the first layer of compounding liquid is calculated in parts by weight: 150 parts of durable oily PU resin, 10 parts of nano-bamboo charcoal powder, 2 parts of wear-resistant agent, 0 part of dispersant, flame retardant: 5 parts of magnesium hydroxide, Solvent: 20 parts of cyclohexanone or dimethylacetyl.

[0087] The formula of the second layer of compounding solution is calculated in parts by weight: 100 parts of water-based PU resin, 50 parts of nano bamboo charcoal powder or nano bamboo powder, dispersant: 1 part of polycarboxylate sodium salt, thickener: polyethyl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the artificial leather field, and concretely relates to a preparation method for synthesizing artificial leather by nano bamboo charcoal UV. The artificial leather is prepared by polyurethane and nano bamboo powder or nano bamboo charcoal powder. The artificial leather has the advantages of simple process, emission reduction and energy saving environmental protection, excellent function, chemical resistance, antibiosis and disinfection.

Description

technical field [0001] The invention relates to the field of artificial leather, in particular to a preparation method of nano bamboo carbon PU synthetic artificial leather. Background technique [0002] Natural leather is widely used in the production of daily necessities and industrial products due to its excellent natural characteristics. However, with the growth of the world population, the human demand for leather has doubled, and the limited amount of natural leather has long been unable to meet this demand. In order to solve this contradiction, scientists began to research and develop artificial leather and synthetic leather decades ago to make up for the deficiency of natural leather. The research history of more than 50 years is the process of artificial leather and synthetic leather challenging natural leather. Scientists started from the research and analysis of the chemical composition and organizational structure of natural leather, started from nitrocellulose ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/14B32B37/02B32B37/26B32B38/16B32B38/18
CPCD06N3/0043D06N3/0059D06N3/0061D06N3/0095D06N3/145D06N2205/10D06N2209/1671D06N2211/28D06N2213/02D06N2213/03
Inventor 何昌华林锦露
Owner 杭州苏威家居科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com