selective catalytic reduction catalyst

A catalyst, selective technology, used in physical/chemical process catalysts, molecular sieve catalysts, catalyst activation/preparation, etc.

Active Publication Date: 2019-08-06
FORD GLOBAL TECH LLC
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

SCR technology in the diesel engine NO x Effective in reducing emissions to levels required by many future emissions standards, but needs improved systems and processes

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • selective catalytic reduction catalyst
  • selective catalytic reduction catalyst
  • selective catalytic reduction catalyst

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0074] Interestingly, referring to figure 1 , by replacing a part of Cu / CHA with Cu / β, the ammonia storage capacity of the SCR system is reduced. refer to figure 1 , will be at 200°C and 30,000 h -1 NO x The conversion of is plotted as a function of the amount of ammonia stored on the catalyst in g / L. The line for conversion terminates at the point where ammonia slips through the system. The Cu / β sample itself is conversion limited and starts leaking very early. The Cu / CHA sample had the highest storage capacity and achieved the highest NO x conversion rate and leaked at the latest. Combining Cu / β with Cu / CHA reduces the ammonia storage capacity of the system and limits NO at this very low temperature x transforming ability. Without being bound by any theory, it is believed that the combination of Cu / CHA in layered form with Cu / β improves the NO x Conversion rates. The Cu / β catalyst alone stored about 0.14 g / L of NH 3 has ammonia slip at low levels of , and has a lo...

example 2

[0076] The next part of the improvement is NO at filter regeneration conditions (>500°C) x conversion rate. refer to figure 2 , experimented with different amounts of Cu / β and Cu / CHA in the system. Data were collected under steady state conditions utilizing a space velocity of 30000 / h of a flowing gas containing 14% oxygen, 5% water, 5% carbon dioxide, 350ppm NO, 350ppm NH 3 , the balance being nitrogen. Under similar conditions at 800°C (no NO x and NH 3 ) under hydrothermal aging of the catalyst for a total of 80 h. The aging is considered to represent 150,000 miles. Data shown with diamonds are for all Cu / CHA systems. High NO at 200-400°C is ideal for most driving conditions x The operating window for the conversion rate. Data shown as squares are for all Cu / β regimes. For the entire operating window, very poor conversion rates were obtained. However, the NO at 650°C x The conversion rate of is better than that of Cu / CHA sample. Replacing 1 / 4 of Cu / CHA with Cu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
Login to View More

Abstract

A selective catalytic reduction (SCR) catalyst includes a support layer. A copper-loaded chabazite (Cu / CHA) layer is supported on the support layer. Copper-loaded beta zeolite (Cu / β) was supported on the Cu / CHA layer. Cu / β can be hydrothermally aged prior to utilizing the SCR catalyst in the vehicle. Pre-aged Cu / β is substantially free of phosphorus (P), calcium (Ca), zinc (Zn), sodium (Na), potassium (K), magnesium (Mg), iron (Fe), CaSO 4 , Ca 19 Zn 2 (PO 4 ) 14 、CaZn 2 (PO 4 ) 2 , ash and / or soot.

Description

technical field [0001] One aspect of the present invention relates to an SCR catalyst, and in particular, to a supported layer having a layer of copper-loaded zeolite beta and a layer of copper-loaded chabazite. Background technique [0002] Vehicle exhaust emissions of regulatory concern include oxides of nitrogen. Nitrogen oxides include, but are not limited to, nitric oxide (NO) and nitrogen dioxide (NO 2 ). These compounds are usually referred to as NO x . The reduction of NO by nitrogen compounds such as ammonia or urea has been developed for various industrial applications x selective catalytic reduction (SCR) system. The application of SCRs for mobile diesel engines needs to overcome several issues, including but not limited to NO x reduction, NO over a wide temperature range x conversion, ammonia storage and ammonia leakage. Ammonia emissions from SCR systems are known as ammonia slip. Ammonia leakage at higher NH 3 / NO x increase over time. SCR technolog...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J29/80B01D53/56B01D53/94
CPCB01J29/7615B01J29/763B01D53/9418B01D2255/20761B01D2255/50B01D2255/502B01D2255/9022B01D2255/9032B01J29/80Y02A50/20Y02T10/12F01N3/2066B01J35/04B01J37/0246B01J37/0244B01J35/0006B01D2255/904B01D53/8628
Inventor 克里斯汀·凯·兰伯特贾斯汀·安东尼·尤拉吉奥瓦尼·卡维塔欧
Owner FORD GLOBAL TECH LLC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com