Manufacturing method of high-strength thermosetting resin high-pressure laminated board
A manufacturing method and thermosetting technology, applied in the field of building materials, can solve problems such as easy cracking and low strength, and achieve the effects of not easy cracking, improved mechanical properties, and strong impact resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0014] A method for manufacturing a high-strength thermosetting resin high-pressure laminate, the manufacturing steps are as follows:
[0015] 1) Immerse the surface paper in melamine formaldehyde resin for 1.5 hours;
[0016] 2) Dissolve triglycidyl isocyanate in a mixed solution of acetone and propionic acid at 50°C, and soak the decorative paper in it for 30 minutes;
[0017] 3) Laminate the impregnated surface paper and decorative paper with the bottom paper impregnated with phenolic resin, and heat press at 135°C for 45min under a pressure of 7MPa.
[0018] In the above-mentioned manufacturing method of high-strength thermosetting resin high-pressure laminated board, the molar ratio of triglycidyl isocyanurate, acetone, and propionic acid is 3:1:0.02.
[0019] The thickness of the laminate is 3mm, and the impact resistance test is carried out according to the method in GB17657-2013. A polished steel ball with a non-destructive surface, a diameter of 50mm, and a mass of 4...
Embodiment 2
[0021] A method for manufacturing a high-strength thermosetting resin high-pressure laminate, the manufacturing steps are as follows:
[0022] 1) Immerse the surface paper in melamine formaldehyde resin for 1.5 hours;
[0023] 2) Dissolve triglycidyl isocyanate in a mixed solution of acetone and propionic acid at 50°C, and soak the decorative paper in it for 30 minutes;
[0024] 3) Lay the impregnated surface paper and decorative paper with the bottom paper impregnated with phenolic resin, and heat press at 140°C for 45min under a pressure of 10MPa.
[0025] In the above-mentioned manufacturing method of high-strength thermosetting resin high-pressure laminated board, the molar ratio of triglycidyl isocyanurate, acetone, and propionic acid is 3.5:1:0.04.
[0026] The thickness of the laminate is 4mm, and the impact resistance test is carried out according to the method in GB17657-2013. A polished steel ball with a diameter of 50mm and a mass of 400g is selected without damage...
Embodiment 3
[0028] A method for manufacturing a high-strength thermosetting resin high-pressure laminate, the manufacturing steps are as follows:
[0029] 1) Immerse the surface paper in melamine formaldehyde resin for 2 hours;
[0030] 2) Dissolve triglycidyl isocyanate in a mixed solution of acetone and propionic acid at 50°C, and soak the decorative paper in it for 30 minutes;
[0031] 3) Laminate the impregnated surface paper and decorative paper with the bottom paper impregnated with phenolic resin, and heat press at 145°C for 50min under a pressure of 9MPa.
[0032] In the above-mentioned manufacturing method of high-strength thermosetting resin high-pressure laminated board, the molar ratio of triglycidyl isocyanurate, acetone, and propionic acid is 4:1:0.03.
[0033] The thickness of the laminate is 3mm, and the impact resistance test is carried out according to the method in GB17657-2013. A polished steel ball with a non-destructive surface, a diameter of 50mm, and a mass of 400...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com