A jointing agent and ceramic tile technology, which is applied in the field of building materials, can solve the problems of efflorescence, unsightly appearance, and weak adhesion on the surface of building joints, and achieve the effects of inhibiting efflorescence, improving flexibility, and not easy to fall off
Inactive Publication Date: 2015-05-06
XIAN ZEHUA BUILDING DECORATION ENG
View PDF0 Cites 6 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] At present, after the existing tile jointing agent is used, because the cement mortar material contains a lot of free calcium hydroxide, it can cause the surface of the building joint to be blotted with alkali, and there will be an unsightly phenomenon; in addition, the existing jointing agent cannot Effectively prevent the erosion of microorganisms such as mold and algae; the joint agent has poor flexibility, weak adhesion, low water resistance and impermeability
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0016] A grout for white tiles comprising the following components:
[0017] 32.5 10-20 parts of white cement;
[0018] 20-40 parts of 400 mesh heavy calcium powder;
[0019] 0.42-0.84 parts of 1# colloidal crystal;
[0020] 1-2 parts of highly active silicon dioxide;
[0021] 1-2 parts of fungicide;
[0022] 1-3 parts of adsorbent;
[0023] 108 glue 2-4 parts.
Embodiment 2
[0025] A grout for white tiles comprising the following components:
[0026] 32.5 10-20 parts of white cement;
[0027] 20-40 parts of 400 mesh heavy calcium powder;
[0028] 0.42-0.84 parts of 1# colloidal crystal;
[0029] 1-2 parts of highly active silicon dioxide;
[0030] 1-2 parts of fungicide;
[0031] 1-3 parts of adsorbent;
[0032] 108 glue 2-4 parts.
Embodiment 3
[0034] A grout for white tiles comprising the following components:
[0035] 32.5 10-20 parts of white cement;
[0036] 20-40 parts of 400 mesh heavy calcium powder;
[0037] 0.42-0.84 parts of 1# colloidal crystal;
[0038] 1-2 parts of highly active silicon dioxide;
[0039] 1-2 parts of fungicide;
[0040] 1-3 parts of adsorbent;
[0041] 108 glue 2-4 parts.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
A crack sealer for white ceramic tiles comprises 10-20 parts of parts of 32.5 white cement, 20-40 parts of 400 mesh heavy calcium powder, 0.42-0.84 parts of 1# colloidal crystal, 1-2 parts of highly active silica, 1-2 parts of a bactericide, 1-3 parts of an adsorbent and 2-4 parts of a 108 adhesive. The crack sealer has the characteristics of effective prevention of erosion of molds, algae and other microbes, strong bonding force, simple components and low cost.
Description
technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a grouting agent for white ceramic tiles. Background technique [0002] At present, after the existing tile jointing agent is used, because the cement mortar material contains a lot of free calcium hydroxide, it may cause the surface of the building joint to be blotted with alkali, and there will be an unsightly phenomenon; in addition, the existing jointing agent cannot Effectively prevent the erosion of microorganisms such as mold and algae; the jointing agent has poor flexibility, weak adhesion, low water resistance and impermeability. Contents of the invention [0003] In order to overcome the deficiencies of the above-mentioned prior art, the object of the present invention is to provide a jointing agent for white ceramic tiles, which can effectively prevent the erosion of microorganisms such as mold and algae, has strong adhesion, and has simple co...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more