Aluminum-zinc-silicon-antimony-rare earth alloy ingot for continuous hot dipping and manufacturing method of aluminum-zinc-silicon-antimony-rare earth alloy ingot

A rare earth alloy and manufacturing method technology, applied in hot dip plating process, metal material coating process, coating and other directions, can solve the problems of short anti-corrosion years, different anti-corrosion years, etc., achieve reliable durability, and overcome the inconspicuous spangles , the effect of prolonging the service life

Inactive Publication Date: 2015-05-06
ANHUI DONGMAO ALLOY MATERIAL TECH
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] With the development of the times, people have higher and higher requirements for the coating. The alloy materials used in the existing hot-dip galvanizing have a short anti-corrosion life, and the anti-corrosion life in different environments is different.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029] In order to make the technical means, creative features, goals and effects achieved by the present invention easy to understand, the present invention will be further described below in conjunction with specific embodiments.

[0030] An aluminum-zinc-silicon-antimony rare-earth alloy ingot for continuous hot-dip coating is composed of the following components in weight percentage:

[0031] Aluminum 5%, zinc 94.64%, silicon 0.15%, antimony 0.15%, rare earth 0.06%.

[0032] Among them, aluminum is AOO aluminum, zinc is 0# zinc, silicon is 553# oxygen metal silicon, antimony is metal antimony ingot, and rare earth is lanthanum-cerium synthetic rare earth, wherein the content of lanthanum is 35% and that of cerium is 65%.

[0033] AOO represents the composition of aluminum ingots, and its indicators are: aluminum ≥ 99.70, iron ≤ 0.16%, silicon ≤ 0.13%, copper ≤ 0.01%, and total impurities 0.3%.

[0034] 0# represents zinc ingots containing more than 99.995% zinc.

[0035]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an aluminum-zinc-silicon-antimony-rare earth alloy ingot for continuous hot dipping and a manufacturing method of the aluminum-zinc-silicon-antimony-rare earth alloy ingot and relates to the technical field of alloy materials. The aluminum-zinc-silicon-antimony-rare earth alloy ingot is prepared from the following components in percentage by weight: 5 percent of aluminum, 94.64 percent of zinc, 0.15 percent of silicon, 0.15 percent of antimony and 0.06 percent of rare earth. The prepared aluminum-zinc-silicon-antimony-rare earth alloy coating has the characteristics of good adhesion performance, reliability in durability, oxidative resistance and acid and alkaline resistance and is capable of prolonging the service life of a coating product, solving the problems in the prior art that spangles are not obvious and consistent and enabling the product to be beautiful; color coating can not be needed by applying the product produced by the alloy, and the product can be directly used for appliances, vehicles or plates for decoration.

Description

Technical field: [0001] The invention relates to the technical field of alloy materials, in particular to an aluminum-zinc-silicon-antimony rare earth alloy ingot for continuous hot dip coating and a manufacturing method thereof. Background technique: [0002] Hot-dip galvanizing is the most common and effective anti-corrosion treatment method, which is widely used in the environment. At present, it has been widely used in the anti-corrosion treatment of steel structures such as electric power, communication, national defense, transportation and industrial and civil buildings. The main method is Including improved Sendzimir method, Sharon method and subsequent improved method, Galavalume and Calfan method. [0003] The improved Sendzimir method is a process method for continuous hot-dip galvanizing. It connects the independent oxidation furnace and reduction furnace in the Sendzimir method by a passage with a smaller cross-sectional area, which includes preheating furnace, r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C18/04C22C1/02C23C2/06
Inventor 孙士富蔡登俊孙士华
Owner ANHUI DONGMAO ALLOY MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap