Method of regulating and controlling lengths of silver nanorods in polyhydric alcohol reduction method through hydrogen peroxide

A silver nanorod, hydrogen peroxide technology, applied in nanotechnology, nanotechnology, nanotechnology for materials and surface science, etc., can solve the problem that the length cannot be easily adjusted, and achieve uniqueness, low cost and simple process. Effect

Active Publication Date: 2015-05-13
山东利特纳米技术有限公司
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a method for regulating the length of silver nanorods that is simple in process, low in cost and does not require a special reaction device in view of the problem that the length cannot be conveniently regulated in the current polyol reduction preparation method of silver nanorods

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method of regulating and controlling lengths of silver nanorods in polyhydric alcohol reduction method through hydrogen peroxide
  • Method of regulating and controlling lengths of silver nanorods in polyhydric alcohol reduction method through hydrogen peroxide
  • Method of regulating and controlling lengths of silver nanorods in polyhydric alcohol reduction method through hydrogen peroxide

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] (1) Mix 1.0g silver nitrate and 1mL (1.3g) glycerol at room temperature, stir and dissolve to obtain solution A;

[0030] (2) Add 10mg of sodium chloride, 10g of polyvinylpyrrolidone, 59mL (77g) of glycerol and 10μL (0.00001g) of hydrogen peroxide into a three-necked round-bottomed flask in sequence, cover the three-necked round-bottomed flask with a stopper, and suspend in In an oil bath at 180°C, stir and react for 1 hour to obtain solution B;

[0031] (3) Add solution A to solution B, the mass ratio of solution A to solution B is 1:39.6, then stir and react at 180°C for 15 minutes, centrifuge the reaction solution, remove the lower precipitate, wash with water, and obtain a length of 2.10± 0.28 µm silver nanorods.

Embodiment 2

[0033] (1) Mix 1.0g silver nitrate and 1mL (1.3g) glycerol at room temperature, stir and dissolve to obtain solution A;

[0034] (2) Add 10mg of sodium chloride, 10g of polyvinylpyrrolidone, 59mL (77g) of glycerol and 100μL (0.0001g) of hydrogen peroxide into the three-necked round-bottomed flask in turn, cover the three-necked round-bottomed flask with a stopper, and suspend in In an oil bath at 180°C, stir and react for 1 hour to obtain solution B;

[0035] (3) Add solution A to solution B, the mass ratio of solution A to solution B is 1:39.6, then stir and react at 180°C for 15 minutes, centrifuge the reaction solution, remove the lower precipitate, wash with water, and obtain a length of 1.35± 0.22 µm silver nanorods.

Embodiment 3

[0037] (1) Mix 1.0g silver nitrate and 1mL (1.3g) glycerol at room temperature, stir and dissolve to obtain solution A;

[0038] (2) Add 10mg of sodium chloride, 10g of polyvinylpyrrolidone, 59mL (77g) of glycerol and 400μL (0.0004g) of hydrogen peroxide into the three-necked round-bottomed flask in sequence, cover the three-necked round-bottomed flask with a stopper, and suspend in In an oil bath at 180°C, stir and react for 1 hour to obtain solution B;

[0039] (3) Add solution A to solution B, the mass ratio of solution A to solution B is 1:39.6, then stir and react at 180°C for 15 minutes, centrifuge the reaction solution, remove the lower precipitate, wash with water, and obtain a length of 1.12± 0.23 micron silver nanorods.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a method of regulating and controlling lengths of silver nanorods in a polyhydric alcohol reduction method through hydrogen peroxide. The method comprises the following steps that silver nitrate and glycerol are blended and stirred and dissolved to obtain a solution A; sodium chloride, polyvinylpyrrolidone, the glycerol and the hydrogen peroxide are blended and stirred and reacted at the temperature which ranges from 160 DEG C to 200 DEG C for 15 minutes to 4 hours to obtain a solution B; the solution A is mixed in the solution B and reacted at the temperature which ranges from 160 DEG C to 200 DEG C for 15 minutes to 4 hours, a centrifugal separation of a reaction solution is conducted, a lower layer sediment is obtained and washed, and the silver nanorods with different lengths are obtained. The method is simple in technology, low in cost, the lengths of the silver nanorods can be changed only by adding the hydrogen peroxide, the lengths of the silver nanorods can be regulated and controlled according to the adding amount of the hydrogen peroxide, the diameter of the silver nanorods has no obvious changes while the lengths are changing, the uniqueness of regulation and control is guaranteed, and the method is incapable of introducing impurities and is suitable for large-scale industrial production.

Description

technical field [0001] The invention belongs to the technical field of nanometer materials, and relates to a method for regulating the length of silver nanorods through hydrogen peroxide. Background technique [0002] Metal nanomaterials have special properties different from macroscopic bulk materials, and the shape also has a very important influence on their physical and chemical properties. For silver nanomaterials, common shapes include cubes, octahedrons, spheres, rods, wires, disks, and so on. Among them, rod-shaped silver nanocrystals have attracted much attention due to their structural anisotropy (different lengths in the xy direction and z direction), and their optical properties have attracted much attention. This characteristic has been used in ion detection, molecular dyeing, and surface-enhanced Raman spectroscopy (SERS ), surface fluorescence enhancement, biomedicine and other fields have shown important application value. [0003] The current methods for r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B22F9/24B82Y30/00B82Y40/00
Inventor 郑逸群姚茂茂
Owner 山东利特纳米技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap