Green-emission iridium phosphors complex and preparation method thereof

A technology of phosphorescent complexes and synthesis methods, applied in the field of synthesis of electrophosphorescent materials for organic light-emitting diodes

Inactive Publication Date: 2015-05-20
KUNMING INST OF PRECIOUS METALS
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The maximum emission wavelength and luminous efficiency of the iridium phosphorescent complex can be adjusted by changing the structure of the cyclometal ligand and the auxiliary ligand. The current research is mainly focused on the structural modification of the cyclometal ligand, and there is no evidence based on 2,2,6 ,Report of this kind of iridium phosphorescent complexes with 6-tetramethylgenandione as ancillary ligand

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Green-emission iridium phosphors complex and preparation method thereof
  • Green-emission iridium phosphors complex and preparation method thereof
  • Green-emission iridium phosphors complex and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] (1) Dimer (dppy) 2 Ir 2 Cl 2 (dppy) 2 Synthesis

[0015] Add 16.33g (70.7mmol) dppy to a 500mL round bottom flask, dissolve it in 120mL ethylene glycol monoethyl ether, then add 9.96g (28.3mmol) iridium trichloride and 80mL deionized water, repeatedly charge and discharge N 2 After three times, N 2 Under atmosphere, it was heated to reflux at 120°C for 24h, and the mixture was cooled to room temperature. After filtration, the filter cake was washed with 30 mL of acetone, 40×2 mL of water, and 30×2 mL of acetone, and dried in vacuum to obtain 17.3 grams of crude product, which was directly used in the next reaction.

[0016] (2) Complex Ir(dppy) 2 Synthesis of (tmd)

[0017] 8.38g (6.09mmol) iridium chloride bridge dimer (dppy) 2 Ir 2 Cl 2 (dppy) 2 Add to a 250mL three-necked bottle, add 3.23g (30.5mmol) of anhydrous Na 2 CO 3 and 210mL ethylene glycol monoethyl ether, and add 5.6g (30.4mmol) 2,2,6,6-tetramethyl-3,5-heptanedione, repeatedly charge and discha...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a green-emission iridium phosphors complex and a preparation method thereof. The iridium phosphors complex is that 2-(xenyl) pyridine is used as a cyclometalated ligand, and 2, 2, 6, 6-tetramethyl-3, 5-heptadione (tmd) is used as an auxiliary ligand; the maximum emission wavelength of (Ir(bppy)2(tmd)) is 533nm, which is the typical green-light emission wavelength; iridium chloride hydrate is used as a raw material to synthesize iridium-chloride bridged dimer (dppy)2Ir2Cl2(dppy)2 which reacts with tmd under an alkaline condition to obtain (Ir(bppy)2(tmd)); and the yield is up to 85%, and the purity is up to 99.5%.

Description

technical field [0001] The invention relates to the technical field of synthesis of electrophosphorescent materials for organic light-emitting diodes (OLEDs), in particular to a green light-emitting iridium phosphorescent complex and a preparation method thereof. Background technique [0002] OLED has the characteristics of high contrast, ultra-thin, wide viewing angle, low energy consumption, fast response, colorful, flexible, etc. It is regarded as the latest generation of "green energy-saving" display technology and the most competitive new generation of solid-state light source. [0003] Luminescent material is one of the core key materials of OLED, and its luminescent performance directly determines the performance of OLED devices. In the development of OLEDs, phosphorescent complexes are introduced into the light-emitting layer of OLEDs as light-emitting materials, so that the maximum internal quantum efficiency of the device is increased from 25% of the original fluor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C07F15/00H01L51/54
CPCC09K11/06C07F15/0033C09K2211/185H10K85/342
Inventor 常桥稳李杰刘伟平姜婧晏彩先叶青松余娟陈家林
Owner KUNMING INST OF PRECIOUS METALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap