Spray-free ABS composition with special aesthetic effect, preparation method and application thereof
A special effect powder, spray-free technology, applied in the field of polymer materials, can solve the problems of uneven distribution of special effect powder, unstable flow rate, poor compatibility, etc., to improve the market application range, obvious metal texture, improve shear resistance cut effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1-6
[0044] Example 1-6 Preparation of polymer-coated special effect powder microspheres:
[0045] According to the formula in Table 1, firstly, add anti-oxidation and corrosion inhibitor to the water-based polymer dispersion at room temperature, stir and disperse for 15 minutes to obtain the dispersion; while stirring, slowly add special effect powder, or water-based Special effect powder slurry, then add curing agent while stirring, and continue to stir for 30-120 minutes, so that the special effect powder is fully dispersed and covered by the dispersion liquid, and finally a composite dispersion liquid of polymer-coated special effect powder is obtained; The composite dispersion liquid is spray-dried to obtain polymer-coated special-effect powder microspheres. The temperature of the air inlet during the spray-drying process is 150-300°C, and the temperature of the air outlet is 50-130°C.
Embodiment 1
[0048]In Example 1: the water-based polymer dispersion is a polyurethane emulsion, and its solid content is 10wt%; the metal powder is a surface-treated flake aluminum powder, and the content of the Al element in the aluminum powder is 60wt%, containing Zn and Sn at the same time; The particle size is 100μm; the anti-oxidation and corrosion inhibitor is pyrogallic acid; the curing agent is polyisocyanate.
Embodiment 2
[0049] In Example 2: the water-based polymer dispersion is an acrylate emulsion, and its solid content is 60wt%; the metal powder is a surface-treated flake copper powder, and the content of the Cu element in the copper powder is 70wt%, containing Zn and Sn ; The particle size is 5 μm; the anti-oxidant corrosion inhibitor is benzotriazole; the curing agent is polycarbodiimide.
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com