Hot-melt pressure-sensitive adhesive, preparation method of hot-melt pressure-sensitive adhesive and waterproof roll

A technology of hot-melt pressure-sensitive adhesives and raw materials, applied in the direction of adhesives, adhesive types, mineral oil hydrocarbon copolymer adhesives, etc., can solve the problems of waterproof membranes being unsuitable for use, and achieve excellent adhesion and firmness The effect of high lap joint and peel strength

Inactive Publication Date: 2015-06-10
BEIJING ORIENTAL YUHONG WATERPROOF TECH CO LTD
View PDF3 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The present invention aims at the problem that the existing pre-paved anti-adhesive construction can only be carried out in the climate environment above -4°C, so that the waterproof coiled material is not sui

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hot-melt pressure-sensitive adhesive, preparation method of hot-melt pressure-sensitive adhesive and waterproof roll
  • Hot-melt pressure-sensitive adhesive, preparation method of hot-melt pressure-sensitive adhesive and waterproof roll
  • Hot-melt pressure-sensitive adhesive, preparation method of hot-melt pressure-sensitive adhesive and waterproof roll

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029] In order to enable those skilled in the art to better understand the technical solutions of the present invention, the present invention will be further described in detail below in conjunction with specific embodiments.

[0030] The invention provides a hot-melt pressure-sensitive adhesive for high-density polyethylene self-adhesive film waterproof membrane that can be firmly overlapped at -10°C. The hot-melt pressure-sensitive adhesive is composed of elastomer, polyisobutylene, Made from raw materials of the first carbon five petroleum resin and the second carbon five petroleum resin, wherein the first carbon five petroleum resin is a solid light-colored alicyclic hydrocarbon hydrogenated petroleum resin with a softening point of 80°C to 127°C and an initial color The number is less than or equal to 2; the second carbon five petroleum resin is a liquid petroleum resin, the softening point is less than or equal to 15°C, and the initial Gardner color number is less than ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a hot-melt pressure-sensitive adhesive and a preparation method of the hot-melt pressure-sensitive adhesive. The hot-melt pressure-sensitive adhesive belongs to the technical field of waterproof rolls. The problem that the waterproof roll is unsuitable to be used in winter or tundra because the conventional pre-paving anti-adhesion construction only can be performed in a climatic environment of over 4 DEG C below zero can be solved. The hot-melt pressure-sensitive adhesive disclosed by the invention is prepared from raw materials comprising an elastomer, polyisobutene, a first C5 petroleum resin and a second C5 petroleum resin, wherein the first C5 petroleum resin refers to a solid alicyclic hydrocarbon type hydrogenated petroleum resin and has the softening point of 80-127 DEG C; and the second C5 petroleum resin refers to a liquid petroleum resin and has the softening point of less than or equal to 15 DEG C. According to the hot-melt pressure-sensitive adhesive disclosed by the invention, a high density polyethylene self-adhered film waterproof roll can be firmly overlapped under the condition of 10 DEG C below zero, and the hot-melt pressure-sensitive adhesive can be applied to sealing tapes, double sided tapes and the like.

Description

technical field [0001] The invention belongs to the technical field of waterproof coiled material, and in particular relates to a hot-melt pressure-sensitive adhesive, a preparation method thereof, and a waterproof coiled material. Background technique [0002] The traditional overlapping method of waterproofing membranes for various underground civil engineering projects is to paste or empty the membranes on the base layer, so that there is a bonding gap between the waterproofing material layer and the structural concrete, or it is not permanently firm and fully bonded. . Based on the above-mentioned construction method, when the base layer is subsidence or deformed, the waterproof layer will be destroyed, and the static pressure water in the ground will flow everywhere between the waterproof layer and the structural concrete, making it difficult to find the exact location when leakage occurs. At the point of leakage, maintenance becomes very difficult, and even in extreme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J123/20C09J153/02C09J157/02C09J11/06
Inventor 张正波田凤兰段文峰
Owner BEIJING ORIENTAL YUHONG WATERPROOF TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap