Crystallizer internal surface electroplating production line and electroplating method thereof

Abstract

The invention discloses a crystallizer internal surface electroplating production line, which includes a washing section, an electroplating section, a hoisting device and an electrolyte solution circulating fluid supply system. The electroplating section is provided with a crystallizer fixed base, a tubular crystallizer and an anode titanium basket. The crystallizer fixed base is provided with an electrolyte solution feed pipe, a sealing pad and an anode lead-out device. The anode titanium basket is arranged on the base, is mounted vertically and is equipped with an upper electrode lead-out terminal and a lower electrode lead-out terminal. The crystallizer is vertically arranged on the sealing pad of the base, and is sleeved outside the anode titanium basket. The upper side of the crystallizer is provided with a seal hanging basket and a sealing pad, the seal hanging basket is equipped with a drain pipe, the seal hanging basket is provided with a mechanical compression device, the seal hanging basket is in compressed sealing connection with the crystallizer upper end through the sealing pad. An electroplating cathode is in compressed electric connection with the crystallizer. The hoisting device is equipped with a crane and a workpiece fixture. And the washing section consists of a washing liquid cleaning tank, an acid liquid cleaning tank, a clear water cleaning tank, and a pure water cleaning tank.

Description

technical field [0001] The invention relates to an electroplating production line equipment, in particular to an electroplating production line equipment used for the inner surface of a tubular body, which is mainly applied to the inner surface treatment process of a crystallizer used in steelmaking. [0002] The present invention also relates to an electroplating method for the above-mentioned electroplating production line equipment. Background technique [0003] In the steelmaking process, copper crystallizers are widely used to make steel billets. Existing iron and steel production enterprises use crystallizers to form steel billets in the process from molten steel to steel billets. The general structure of the crystallizer is a square copper tube, and the inner wall of the copper tube is plated with chromium or nickel-cobalt alloy. When the molten steel from the melting furnace is introduced into the crystallizer, it will solidify into a square billet inside. In order...

AI Technical Summary

Problems solved by technology

There are several shortcomings in this method: first, it is labor-intensive, and at least two people are required to coat the copper tube surface of each crystallizer before electroplating, and the labor intensity of the workers is high and time-consuming; second, the coated film In the process of handling and hoisting, it is easy to be damaged due to bumping. The plating solution penetrates into the film and causes the outer surface to be plated, which wastes electrolyte and increases power consumption. The concentration of the bath solution is not easy to control; the sixth is that the electroplating solution is wasteful, which has a great impact on environmental pollution and personnel health; the seventh is that the current, time, temperature, etc. are not easy to control

However, there are still the following defects that are difficult to overcome: first, because of manual operation, the upper and lower racks before and after the electroplating of the crystallizer are all carried by workers, and the labor intensity of the workers is still high; the second is the sealing method, which is tightened by the tension of the bolts at the upper and lower ends of the mold The upper and lower cover plates, the upper and lower cover plates may be unbalanced in force, resulting in poor sealing, resulting in the omission of the electroplating solution, which cannot realize clean production, a large waste of the plating solution, and great pollution to the environment; the third is that the internal plating method is that the anode is installed in the copper tube , and one end of the anode is connected to electricity, and the other end is not connected to electricity. Due to the existence of potential difference, the thickness of the coating on the upper and lower ends of the workpiece after plating is quite different. service life

[0013] 6. The crystallizer is manually installed before and after electroplating, which is labor-intensive

[0014] 7. The concentration of the electroplating solution cannot be controlled, the addition is not timely and the addition metering cannot be controlled