Ru porcelain tea-dust glaze and preparation technology thereof

A production process and technology of tea powder, which is applied in the field of Ruci tea powder glaze and its production process, to improve the strength and thermal stability, prevent the glaze layer from bursting, and avoid the effects of cracking

Active Publication Date: 2015-08-05
姚瑞平
View PDF3 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But this kind of glaze color is relatively rare in Ru porcelain

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The production process of Ru porcelain tea powder glaze color uses white feldspar, calcite, quartz stone, Ru medicine, bone powder and talcum powder as glaze raw materials. The weight parts of each raw material are: white feldspar accounts for 28 parts, and calcite accounts for 12 parts. 8 parts, 8 parts of quartz stone, 50 parts of Ru medicine, 1.0 part of bone powder and 0.5 parts of talcum powder; said Ru medicine is yellow kaolin from Mangchuan Township, Ruzhou City, Henan Province.

[0029] Ru porcelain tea powder glaze is made the manufacturing process of Ru porcelain, and described preparation method is:

[0030] Step 1. After crushing the glaze raw materials, mix them into a ball mill according to the above ratio, add 29% water of the total weight of the mixed raw materials, start the wet mill for 14 hours, pass the wet milled slurry through a 300-mesh sieve, and let it stand For 24 hours, use a moisture meter to detect the water content of the slurry, and adjus...

Embodiment 2

[0034]The production process of Ru porcelain tea powder glaze color uses white feldspar, calcite, quartz stone, Ru medicine, bone meal and talcum powder as glaze raw materials. The weight parts of each raw material are: white feldspar accounts for 29 parts, and calcite accounts for 13 parts. 9 parts, 9 parts of quartz stone, 51 parts of Ru medicine, 1.2 parts of bone powder and 0.7 parts of talcum powder; said Ru medicine is yellow kaolin from Mangchuan Township, Ruzhou City, Henan Province.

[0035] Ru porcelain tea powder glaze is made the manufacturing process of Ru porcelain, and described preparation method is:

[0036] Step 1. After crushing the glaze raw materials, mix them into a ball mill according to the above ratio, add 30% water of the total weight of the mixed raw materials, start the wet mill for 15 hours, pass the wet milled slurry through a 300-mesh sieve, and let it stand For 24 hours, use a moisture meter to detect the water content of the slurry, and adjust ...

Embodiment 3

[0040] The production process of Ru porcelain tea powder glaze color uses white feldspar, calcite, quartz stone, Ru medicine, bone meal and talcum powder as glaze raw materials. The weight parts of each raw material are: white feldspar accounts for 30 parts, calcite accounts for 14 parts 10 parts, 10 parts of quartz stone, 52 parts of Ru medicine, 1.3 parts of bone meal and 0.8 parts of talcum powder; the said Ru medicine is yellow kaolin from Mangchuan Township, Ruzhou City, Henan Province.

[0041] Ru porcelain tea powder glaze is made the manufacturing process of Ru porcelain, and described preparation method is:

[0042] Step 1. After crushing the glaze raw materials, mix them into a ball mill according to the above ratio, add 31% water of the total weight of the mixed raw materials, start the wet mill for 16 hours, pass the wet milled slurry through a 300-mesh sieve, and let it stand For 24 hours, use a moisture meter to detect the water content of the slurry, and adjust ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a Ru porcelain tea-dust glaze and a preparation technology thereof. The Ru porcelain tea-dust glaze comprises, by weight, 28-32 parts of white feldspar, 12-14 parts of calcite, 8-10 parts of quartz stone, 50-53 parts of Ru drug, 1.0-1.5 parts of bone meal and 0.5-1.0 part of talcum powder, and the Ru drug is kaolin from Mangchuan Country in Ruzhou City in Henan Province. The glaze color of the Ru porcelain tea-dust glaze is a tea-dust color, and tea-dust-like tawny fine points flash on the background color of ochre color, so the glaze is unsophisticated, elegant, beautiful and interesting, and porcelains sintered by using the glaze are beautiful, thereby the glaze increases a new glaze color for Ru porcelain, and improves the economic benefit of the Ru porcelain.

Description

technical field [0001] The invention relates to a Ru porcelain glaze and a production process thereof, in particular to a Ru porcelain tea powder glaze and a production process thereof. Background technique [0002] Ru Porcelain is one of the five famous porcelains in my country. Its manufacturing process was lost for a time, but after hard research by technicians, production has now resumed. The basic color of Ru kiln enamel is a kind of light sky blue, commonly known as "duck eggshell blue", the glaze layer is not thick, and changes with the turning of the shape, showing layered changes in shades and depths. The cracked pieces on the glaze surface are mostly scattered and very fine grained pieces, commonly known as "crab claws". The glaze color changes with the light, and the glaze surface has a clear feeling of ghee. The glaze is slightly translucent, mostly milky or crystallized, just like the beauty of "after the rain, the sky is clear and the clouds are broken", warm ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/86
Inventor 姚瑞平王静麻益民马银隆
Owner 姚瑞平
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com