Precise casting medium temperature modulated wax and preparation method thereof

A technology of precision casting and medium temperature, which is applied in the direction of casting molding equipment, casting molds, manufacturing tools, etc. It can solve the problems of difficult production of high-quality mold materials, and achieve the advantages of improving production efficiency, easy demoulding, and strong dimensional stability. Effect

Active Publication Date: 2015-08-19
青岛新诺科新材料科技发展有限公司 +1
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Obviously, the self-sufficient mold material production mode of investment casting production enterprises is difficult to produce high-quality mold materials, which is in contradiction with the development plan of the enterprise

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Precise casting medium temperature modulated wax and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A medium-temperature modulation wax for precision casting, which includes the following raw materials in parts by mass: 44-46 parts of microcrystalline wax, 2.5-3.5 parts of montan wax, 34-36 parts of rosin resin, ethylene-vinyl acetate copolymer 3.5-4.5 parts of compound, 12-14 parts of pure monomer resin.

[0032] The preparation method of the above-mentioned medium temperature modulation wax for precision casting comprises the following steps:

[0033] (1) Divide the rosin resin into two parts, heat one part at 120° C., keep stirring until melting, then add another part of rosin resin, continue heating, keep stirring until melting, and obtain molten rosin resin A;

[0034] (2) Continue heating the molten rosin resin A obtained in step (1) at 100-120° C. for 1-2 minutes, add montan wax, and keep stirring until completely melted to obtain mixture B;

[0035] (3) Continue heating the mixture B obtained in step (2) at 110-120°C for 1-2 minutes, add ethylene-vinyl acetat...

Embodiment 2

[0041] A medium-temperature modulation wax for precision casting according to Example 1, which includes the following raw materials in parts by mass: 44 parts of microcrystalline wax, 2.5 parts of montan wax, 34 parts of rosin resin, 3.5 parts of ethylene-vinyl acetate copolymer, pure 12 parts of monomer resin.

[0042] The preparation method of the above-mentioned medium temperature modulation wax for precision casting comprises the following steps:

[0043] (1) Divide the rosin resin into two parts, heat one part at 120° C., keep stirring until melting, then add another part of rosin resin, continue heating, keep stirring until melting, and obtain molten rosin resin A;

[0044] (2) Continue heating the molten rosin resin A obtained in step (1) at 100° C. for 1 minute, add montan wax, and keep stirring until completely melted to obtain mixture B;

[0045] (3) Continue heating the mixture B obtained in step (2) at 110° C. for 1 minute, add ethylene-vinyl acetate copolymer, an...

Embodiment 3

[0051]A medium-temperature modulation wax for precision casting according to Embodiment 1, which includes the following raw materials in parts by mass: 46 parts of microcrystalline wax, 3.5 parts of montan wax, 36 parts of rosin resin, 4.5 parts of ethylene-vinyl acetate copolymer, pure 14 parts of monomer resin.

[0052] The preparation method of the above-mentioned medium temperature modulation wax for precision casting comprises the following steps:

[0053] (1) Divide the rosin resin into two parts, heat one part at 120° C., keep stirring until melting, then add another part of rosin resin, continue heating, keep stirring until melting, and obtain molten rosin resin A;

[0054] (2) Continue heating the molten rosin resin A obtained in step (1) at 120° C. for 2 minutes, add montan wax, and keep stirring until completely melted to obtain mixture B;

[0055] (3) Continue heating the mixture B obtained in step (2) at 120° C. for 2 minutes, add ethylene-vinyl acetate copolymer...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
drop melting pointaaaaaaaaaa
freezing pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a precise casting medium temperature modulated wax and a preparation method thereof. The precise casting medium temperature modulated wax is prepared from the following raw materials in part by mass: 44-46 parts of microcrystalline wax, 2.5-3.5 parts of lignite wax, 34-36 parts of rosin resin, 3.5-4.5 parts of ethylene-vinyl acetate copolymer, and 12-14 parts of pure monomer resin. The modulated wax disclosed by the invention is applied to the precise casting industry, and has the advantages of being strong in stability, high in strength, hard to deform, low in gray level, capable of reducing the pollution to the metal casting, easy to demold and easy to melt along with a wax pattern while demolding so as to flow out of a molding shell, and capable of effectively improving the production efficiency in the precise casting process.

Description

technical field [0001] The invention relates to the precision casting industry, in particular to a precision casting mid-temperature modulated wax used in the precision casting industry and a preparation method thereof. Background technique [0002] With the development of society, precision castings have been widely used in aviation, weapons and other industrial sectors, especially electronics, petroleum, chemical, transportation, light industry, textile, pharmaceutical, medical equipment, pump and valve components. [0003] The mold material used by most of the investment casting enterprises in my country is the modulated wax made by investment casting enterprises - stearic acid medium temperature mold material. The quality of the mold material is low, the cost is high, and it seriously affects the improvement of the casting quality. Little competition in the international market. However, many investment casting enterprises in my country hope to produce castings for expor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22C7/02B22C1/00
Inventor 邵斌
Owner 青岛新诺科新材料科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com