Thin-coat metal composite plate and production method thereof

A metal composite board and production method technology, applied in the direction of metal layered products, layered products, chemical instruments and methods, etc., can solve the problems of large equipment investment, high cost, difficult production, etc., and achieve simple production process and low production input little effect

Inactive Publication Date: 2015-08-26
杜双双
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are very few composite materials with a total thickness greater than 6mm and a cladding of less than 2mm on the market, mainly because it is difficult to produce or the cost is too high by conventional methods
The rolling composite method can produce metal composite materials with a cladding layer of less than 2mm, but generally the total thickness does not exceed 3mm. If it is necessary to produce a composite plate with a thickness of 6-8mm, the initial equipment investment is very large; the explosive composite method can produce composite materials with a total thickness greater than 6mm. , but the minimum coating thickness can only reach 2mm

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A method for producing an ultra-thin clad metal composite board, comprising the following steps: 1) preparation of clad boards; at least two layers of clad layers are rolled and clad, sprayed or electroplated to make clad boards; wherein the thickness of the clad layers is less than 2mm , The cladding thickness is 2-4mm. II) Explosive welding of cladding plate and base plate; after heat treatment and leveling of cladding plate and base plate, the cladding plate and base plate are stacked and explosively welded to form a thin-layer metal composite plate. III) The thin-layer metal composite plate is made into a product by quenching and tempering heat treatment and forming process. Among them, the tempering heat treatment adopts a temperature of 300°C to 1000°C, and a holding time of 10min to 4h. The forming process includes grinding, leveling, cutting and other processes. Wherein, as a preferred technical solution, the above-mentioned cladding layer is one of two layers ...

Embodiment 2

[0021] A method for producing an ultra-thin clad metal composite board, comprising the following steps: 1) preparation of the clad board; the clad layer is made of three or more clad layers by rolling composite, spraying or electroplating to make the clad board, The cladding material is selected from one or more of titanium, tantalum, niobium, zirconium, stainless steel, copper, and aluminum. Among them, the thickness of the cladding is less than 2mm, and the thickness of the cladding is 2-4mm. II) Explosively welded cladding plate and base plate, the base plate material is one of stainless steel, carbon steel, copper, aluminum. After heat treatment and leveling of the cladding plate and the base plate, the cladding plate and the base plate are laminated and explosively welded to form a thin-layer metal composite plate. III) The thin-layer metal composite plate is made into a product by quenching and tempering heat treatment and forming process. Among them, the tempering hea...

specific Embodiment 3

[0022] Produce TA2 / 316L / 316L titanium stainless steel clad plates with a thickness of 0.1mm+2mm+48mm, and prepare TA2 / 316L titanium stainless steel clad plates with a thickness of 0.1mm+2mm by rolling and compounding. The stainless steel composite plate is composited on the 48mm thick 316L base layer by explosive method, and finally a 0.1mm+50mm titanium stainless steel composite plate is obtained. The heat treatment temperature is 300℃~1000℃, and the holding time is 10min~4h. The forming process includes grinding burrs, leveling, cutting and other processes.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a composite plate and a production method thereof, and relates to the field of novel materials. With the method provided by the invention, a composite plate with a coating layer thickness lower than 2mm can be prepared, such that a metallurgically bonded ultra-thin-coat metal composite plate can be obtained. The production method comprises the steps of coating material preparation, composite material preparation and heat treatment. According to the ultra-thin-coat metal composite material, the coating material is prepared through the metal composition methods of rolling composition, explosive cladding, spray coating, electroplating, and the like. The composition of the coating and a substrate is realized with an explosion or rolling method. The thickness of the coating of the ultra-thin metal composite material is lower than 2mm, and the total material thickness of the composite material can be set to any thickness. Therefore, a vacancy of the composite plate with the coating thickness within this range is filled.

Description

technical field [0001] The invention relates to a production method of a thin-clad metal composite board. The final cladding thickness of the thin metal composite material of the invention is less than 2mm, and the total thickness of the material is not limited, which fills the blank of the cladding thickness cladding board in this range. Background technique [0002] At present, most of the metal composite materials that have achieved metallurgical bonding in China are produced by rolling cladding and explosive cladding. The thickness of the cladding of the rolled cladding is about 1mm, and the total thickness is about 3mm; the thickness of the cladding of the explosive cladding is greater than 2mm. There are very few composite materials with a total thickness of more than 6mm and a cladding of less than 2mm on the market, mainly because it is difficult to produce or the cost is too high by conventional methods. The rolling composite method can produce metal composite mater...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B15/01B32B37/00
Inventor 杜双双
Owner 杜双双
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap