Preparation method of polystyrene composite material for wrapping plates

A technology of polystyrene and composite materials, which is applied in the field of packaging materials, can solve the problems of not having the ability to absorb waves and not being able to resist electromagnetic radiation, and achieve good hysteresis loss, strong eddy current loss, and radiation resistance.

Active Publication Date: 2015-09-09
汕头市华麟塑化有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the board basically does not have the ability to

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of polystyrene composite material for wrapping plates

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A preparation method of polystyrene composite material for packaging board, comprising the following steps:

[0025] (1) After the polycrystalline iron fiber is soaked in water, the speed is 800 rpm and stirred and dispersed for 40 minutes. After sieving, the sieve is extracted with acetone for 24 hours to remove surface impurities, washed with deionized water and placed at a temperature of Dry in an oven at 70°C for 4 hours to obtain purified polycrystalline iron fibers;

[0026] (2) After acrylic acid and AIBN are mixed uniformly, the grafting solution is prepared, and the purified polycrystalline iron fiber obtained in step (1) is cut into a length of 10mm and dissolved in thionyl chloride, and the suspension is obtained after stirring. Put the suspension in an ultrasonic cleaner after adding the grafting liquid, the weight ratio of acrylic acid, AIBN, and purified polycrystalline iron fiber is 1:9:24, ultrasonically vibrate for 40 minutes, distill the material under...

Embodiment 2

[0029] A preparation method of polystyrene composite material for packaging board, comprising the following steps:

[0030] (1) After the polycrystalline iron fiber is soaked in water, the speed is 800 rpm and stirred and dispersed for 40 minutes. After sieving, the sieve is extracted with acetone for 24 hours to remove surface impurities, washed with deionized water and placed at a temperature of Dry in an oven at 70°C for 4 hours to obtain purified polycrystalline iron fibers;

[0031] (2) After acrylic acid and AIBN are mixed uniformly, the grafting solution is prepared, and the purified polycrystalline iron fiber obtained in step (1) is cut into a length of 10mm and dissolved in thionyl chloride, and the suspension is obtained after stirring. Put the suspension in an ultrasonic cleaner after adding the grafting liquid, the weight ratio of acrylic acid, AIBN, and purified polycrystalline iron fiber is 1:9:24, ultrasonically vibrate for 40 minutes, distill the material under...

Embodiment 3

[0034] A preparation method of polystyrene composite material for packaging board, comprising the following steps:

[0035] (1) After the polycrystalline iron fiber is soaked in water, the speed is 800 rpm and stirred and dispersed for 40 minutes. After sieving, the sieve is extracted with acetone for 24 hours to remove surface impurities, washed with deionized water and placed at a temperature of Dry in an oven at 70°C for 4 hours to obtain purified polycrystalline iron fibers;

[0036] (2) After acrylic acid and AIBN are mixed uniformly, the grafting solution is prepared, and the purified polycrystalline iron fiber obtained in step (1) is cut into a length of 10mm and dissolved in thionyl chloride, and the suspension is obtained after stirring. Put the suspension in an ultrasonic cleaner after adding the grafting liquid, the weight ratio of acrylic acid, AIBN, and purified polycrystalline iron fiber is 1:9:24, ultrasonically vibrate for 40 minutes, distill the material under...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a preparation method of a polystyrene composite material for wrapping plates, which comprises the following steps: (1) immersing polycrystalline iron fibers in water, dispersing by stirring, screening, extracting the oversize to remove surface impurities, washing, and drying to obtain purified polycrystalline iron fibers; (2) uniformly mixing acrylic acid and AIBN (2,2'-azobisisobutyronitrile) to obtain a grafting solution, shearing the purified polycrystalline iron fibers, dissolving in thionyl chloride, stirring to obtain a suspension, adding the suspension into the grafting solution, putting in an ultrasonic cleaner, carrying out ultrasonic vibration, carrying out vacuum distillation on the material, filtering, washing, and drying to obtain modified polycrystalline iron fibers; and (3) mixing a polystyrene resin, an antioxidant and polythiophene in toluene to obtain a mixed solution, impregnating the modified polycrystalline iron fibers in the mixed solution until all the toluene is volatilized, spreading in a mold, heating and carrying out compression molding to obtain the polystyrene composite material for wrapping plates. The composite material has favorable wave-absorbing capacity, and can effectively resist electromagnetic wave radiation.

Description

Technical field: [0001] The invention relates to a packaging material, in particular to a preparation method of a polystyrene composite material for a packaging board. Background technique: [0002] Packaging board is the board used for packaging products, including the following functions: 1. Protection function: protect the content, shape, quality, performance of the product, and protect consumers from using the product safely; 2. Convenient function: easy to open and use, open the packaging board The product can be consumed immediately. At this stage, packaging boards are made of various materials, including paper, plastic, metal, glass and other materials. With the rapid development of science and technology, the requirements for packaging board materials are getting higher and higher. Among them, plastic boards with excellent cushioning performance, compression resistance and durability are generally used when packaging electronic products. For some special electronic ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L25/06C08L65/00C08L51/10C08F292/00C08F220/06
Inventor 矫磊
Owner 汕头市华麟塑化有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap