Preparation process of a cast steel material with high temperature resistance of 620°C
A preparation process and high-temperature-resistant technology, which is applied to the improvement of process efficiency, furnace type, furnace, etc., can solve the problems of large investment in infrastructure costs, harsh specifications, and difficult production in factories, so as to achieve effective and economical process means and improve cleanliness degree of effect
Inactive Publication Date: 2018-02-27
上海宏钢电站设备铸锻有限公司
View PDF5 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
The chemical composition of this material is very complex and the specifications are strict, and the control in the production process is very difficult. If you rely on imports, it will put a huge pressure on the company's cost
The production and smelting of the same type of materials at home and abroad must be equipped with corresponding vacuum smelting equipment, and the investment in infrastructure is large. Due to the limitations of equipment and venues, it is difficult for factories without conditions to carry out production.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0062] Products in the following examples
[0063] material as target ingredient
[0064]
[0065] A preparation process for a high temperature 620°C cast steel material, the cast steel material is ZG13Cr9Mo2Co1NiVNbNB, the preparation process includes an electric arc furnace melting process and a ladle refining furnace melting process, characterized in that:
[0066] The described electric arc furnace smelting process comprises:
[0067] a, Lime is laid on the bottom of the furnace before the charge of low-sulfur phosphorus-carbon steel plate is fed;
[0068] b. In order to ensure the amount of decarburization, waste electrode blocks are added along with the furnace charge, and when the molten carbon reaches the range of 0.39% to 0.59%, all chemical elements are fully analyzed;
[0069] c. When the temperature of the molten pool reaches 1580°C, oxygen blowing is started, the furnace body is tilted forward, and the oxidized slag is discharged from the furnace door, and fr...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention discloses a preparation process of a cast steel material capable of resisting a high temperature of 620 DEG C. The cast steel material is ZG13Cr9Mo2Co1NiVNbNB; the preparation process comprises a unique electric arc furnace smelting process and a ladle refining furnace smelting process; according to the preparation process, nitrogen is blown in the LF furnace smelting process to take the place of the process of adding a chromium nitride alloy to the electric arc furnace in the prior art, and therefore, the process performance is stabilized and the cost is greatly reduced. The electric arc furnace and the ladle refining furnace are taken as the basic smelting devices for the preparation process; the electric arc furnace smelting process is strengthened, and on the basis of obtaining good-quality primary smelting liquid steel, the control of the ladle refining furnace is refined; a unique, complete and exquisite preparation process is obtained by virtue of lots of experimental summary; the existing production equipment can be utilized without increasing investment to produce steel castings having the performance indices completely satisfying the use of high-efficiency ultra-supercritical units, and the steel castings have been successfully applied to the operation of high-efficiency ultra-supercritical turbine units.
Description
technical field [0001] The invention relates to a preparation process of a cast steel material, in particular to a preparation process of a high temperature resistant cast steel material. Background technique [0002] With people's increasing concern about environmental pollution and the increasing shortage of fossil fuels such as coal, how to further reduce energy consumption and reduce CO 2 Emissions have become a problem that the whole society pays more and more attention to and needs to be solved urgently. Improving the efficiency of coal-fired power plants can achieve the goals of energy saving and emission reduction at the same time, which is the most basic development direction of the power industry. Higher ultra-supercritical steam parameters, unique structure and thermal system optimization are the main measures to improve efficiency. Therefore, ultra-supercritical power generation technology has also received more and more attention from the power industry in vario...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): C22C33/04C21C5/52C21C7/06C21C7/072C21C7/076
CPCY02P10/20
Inventor 戴月良王强吴铁明陈红来曾海明蔡娟朱广忠任朝阳徐德民
Owner 上海宏钢电站设备铸锻有限公司