Cu-reinforced Co-free secondary-hardening ultrahigh-strength steel and preparation method thereof

An ultra-high-strength steel and secondary hardening technology, applied in the field of alloy steel, can solve the problems of poor economy, the price is vulnerable to the impact of the international situation, and reduce the Co content, so as to achieve high economy, good heat treatment process, and save Co The effect of element content

Active Publication Date: 2015-09-16
CENT IRON & STEEL RES INST
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] Although the AerMet series materials have excellent performance, due to the large amount of precious alloying elements such as cobalt and nickel, there are problems such as poor economy. Although M54 tries to solve the economic problems of the AerMet series materials, it relies on relatively high W and Mo compound additions to obtain corresponding precipitation. The driving force and strengthening effect reduce the Co content, but still contain up to 7% Co element, especially for Co as a strategic resource, the price is very vulnerable to the impact of the international situation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cu-reinforced Co-free secondary-hardening ultrahigh-strength steel and preparation method thereof
  • Cu-reinforced Co-free secondary-hardening ultrahigh-strength steel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0041] According to the chemical composition scope of steel of the present invention, adopt 25 kilograms of vacuum induction furnaces to prepare 21 kilograms of alloy ingots, its concrete chemical composition is shown in Table 3, and furnace number is 1 # ~13 # .

[0042] After 13 batches of steel were smelted and cast into steel ingots, the high-temperature homogenization treatment system was first carried out before forging: after holding at 1200°C for 10 hours, the temperature was lowered for forging, and the forging heating temperature was 1150°C. The dimensions of forged test rods are: φ15×2000mm, 15×15×2000mm and 25×45×L.

[0043] After forging, the test bar is firstly subjected to normalizing and annealing heat treatment: normalizing treatment at 1050°C×1h, air cooling, annealing treatment at 680°C×6h, and air cooling. Then send the sample section to process the tensile, impact and fracture toughness sample blanks. The final heat treatment is quenching, deep cooling ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses Cu-reinforced Co-free secondary-hardening ultrahigh-strength steel and a preparation method, belonging to the technical field of alloy steel. The steel comprises the following chemical components in percentage by weight: 0.20-0.50% of C, 1.0-5.0% of Cr, 8.0-30.0% of Ni, 1.0-5.0% of Mo, 1.0-5.0% of Cu, 0-3.0% of Al, 0-2.0% of W, less than or equal to 0.30% of V, less than or equal to 0.20% of Nb and the balance of Fe and unavoidable impurities. According to the preparation method, the vacuum induction and vacuum consumable remelting technology or the vacuum induction and electroslag remelting technology can be adopted. Compared with the prior art, the Cu-reinforced Co-free secondary-hardening ultrahigh-strength steel has the advantages of good comprehensive performance, higher strength, good plasticity and toughness, good heat treatment process performance and higher tempering resistance and overaging resistance; the content of strategic resource Co element is saved and the economical efficiency is remarkably improved.

Description

technical field [0001] The invention belongs to the technical field of alloy steel, in particular to a Cu-strengthened Co-free secondary hardening ultra-high-strength steel Air350 and its preparation method. With the strategic element Co, the economy is strong. Background technique [0002] With the development of the aviation and aerospace industry, especially after the durability / damage tolerance design criteria are adopted for aerospace components, higher requirements are put forward for materials, which require materials to have higher strength, toughness and reasonable yield / strength ratio , and economical, suitable for mass production and application. With the development of new aircraft, there is an increasingly urgent demand for ultra-high-strength steels of 2000 MPa and above that can be used for durability damage tolerance design. The latest application achievement is AerMet100 steel in the United States, an ultra-high-strength steel that adopts secondary hardeni...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/44C22C38/46C22C38/48C21D8/00
Inventor 王春旭厉勇刘少尊黄顺喆韩顺邢峰刘宪民田志凌赵博赵志国李建新庞学东
Owner CENT IRON & STEEL RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com