Stable-temperature medium-temperature-sintering microwave dielectric ceramic and preparation method thereof

A microwave dielectric ceramic and temperature-stable technology, which is applied in the field of temperature-stable medium-temperature sintering low-loss microwave dielectric ceramics and their preparation, can solve the problems of high sintering temperature, low dielectric constant, poor temperature stability and the like, and achieve a simple preparation process. , The effect of saving energy cost and low loss

Inactive Publication Date: 2015-09-30
TIANJIN UNIV
View PDF1 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, MgTiO 3 As a traditional microwave dielectric material, ceramics still have excellent microwave dielectric properties such as low dielectric constant and u

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Stable-temperature medium-temperature-sintering microwave dielectric ceramic and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The present invention uses MgO and TiO with a purity greater than 99% 2 , CaCO 3 、Al 2 o 3 , ZnO and La with a purity greater than 99.5% 2 o 3 , B 2 o 3 As the starting material, microwave dielectric ceramics were prepared by a simple solid-state method. The specific implementation plan is as follows:

[0023] (1) MgO, TiO 2 and CaCO 3 According to the stoichiometric formula 0.93MgTiO 3 -0.07CaTiO 3 For batching, the ratio of raw materials is: 3.08992g MgO, 6.558647g TiO 2 , 0.57756g CaCO 3 . Put about 10g of mixed powder into a polyester tank, add 200ml of deionized water, add 150g of zirconium balls, and mill on a planetary ball mill for 12 hours at a speed of 400 rpm;

[0024] (2) Put the ball-milled raw materials in step (1) into a drying oven, dry them at 100-120° C., and pass through a 40-mesh sieve;

[0025] (3) Put the dried and sieved powder into a medium-temperature furnace, pre-fire at 1100°C, and keep it warm for 4 hours;

[0026] (4) La 2 o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a stable-temperature medium-temperature-sintering microwave dielectric ceramic and a preparation method thereof. The preparation method comprises the following steps: proportioning MgO, TiO2 and CaCO3 according to the stoichiometric formula 0.93MgTiO3-0.07CaTiO3, carrying out ball milling, drying, screening and presintering at 900-1150 DEG C; proportioning La2O3 and Al2O3 according to the stoichiometric formula LaAlO3, carrying out ball milling, drying, screening and presintering at 1100-1300 DEG C; and mixing the two presintered powders in a mole ratio of 99:1, adding 1-3 wt% of ZnO and 1-3 wt% of B2O3, carrying out ball milling, drying, screening, granulating, compacting into a green compact, and sintering at 1075-1175 DEG C to prepare the stable-temperature medium-temperature-sintering microwave dielectric ceramic. The Qf value is up to 33000-57000 GHz, tau<f> reaches -9.1 to -2.6 ppm/DEG C, and the optimal sintering temperature is lowered to 1125 DEG C. The stable-temperature medium-temperature-sintering microwave dielectric ceramic has the advantages of simple preparation technique and excellent microwave dielectric properties, and has wide application prospects.

Description

technical field [0001] The invention belongs to the field of electronic information materials and components, in particular to a temperature-stable medium-temperature sintered low-loss microwave dielectric ceramic and a preparation method thereof. Background technique [0002] With the continuous development of modern communication technology, the requirements for miniaturization, integration and modularization of components are increasingly urgent, and higher requirements are put forward for microwave dielectric materials. Microwave dielectric ceramics have become one of the most active research fields of functional ceramics in recent years. one. Among them, MgTiO 3 As a traditional microwave dielectric material, ceramics still have excellent microwave dielectric properties such as low dielectric constant and ultra-high quality factor in the millimeter wave band, but they have poor temperature stability (τ f ~-50ppm / ℃), the disadvantage of high sintering temperature (>...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/465C04B35/64
Inventor 李玲霞李赛高正东吕笑松孙浩
Owner TIANJIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap