Preparation method of polyurethane heating radiator

A radiator and polyurethane technology, applied in the field of polyurethane, can solve the problems of no polyurethane radiator reported in literature, metal radiators are easy to rust, and have a short service life, and achieve the effects of light quality, low production cost, and stable physical properties.

Inactive Publication Date: 2015-10-14
ZIBO DEXIN LIANBANG CHEM IND
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Radiators are indispensable in the north of collective heating. Traditional metal radiators are easy to rust, easy to block, and have a short service life, heavy, difficult to carry, and high production costs.
[0003] In the prior art, there are no literature reports related to polyurethane radiators

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The preparation method of the present embodiment polyurethane radiator comprises the following steps:

[0021] (1) Preparation of prepolymer A component:

[0022] Mix polyether polyol A and polyether polyol B evenly at a mass ratio of 1:2, heat up to 110°C, dehydrate under high vacuum -0.08±0.01MPa for 3 hours, then cool down to 50°C, add 0.3 times the mass of poly The diphenylmethane diisocyanate of the total mass of the ether polyol was stirred evenly, and the temperature was raised to 85° C. for 3 hours, and the mass content of the isocyanate was 9.5% by sampling to obtain the prepolymer component A;

[0023] (2) Preparation of component B: the chain extender MOCA and the tin catalyst T9 were mixed uniformly at a mass ratio of 300:1 to obtain component B;

[0024] (3) Production of polyurethane elastomer: Mix components A and B evenly at a mass ratio of 5:1, pour them into a mold at 60°C, and react under a pressure of 13MPa to obtain a test piece. The test piece is ...

Embodiment 2

[0026] The preparation method of the present embodiment polyurethane radiator comprises the following steps:

[0027] (1) Preparation of prepolymer A component:

[0028] Mix polyether polyol A and polyether polyol B evenly at a mass ratio of 1:1.5, heat up to 105°C, dehydrate under high vacuum -0.08±0.01MPa for 4 hours, then cool down to 40°C, add 0.2 times the mass of poly The diphenylmethane diisocyanate of the total mass of the ether polyol was stirred evenly, and the temperature was raised to 80° C. for 4 hours, and the mass content of the isocyanate was 14.5% by sampling to obtain the prepolymer A component;

[0029] (2) Preparation of component B: the chain extender MOCA and the tin catalyst T9 were uniformly mixed in a mass ratio of 300:2 to obtain component B;

[0030] (3) Production of polyurethane elastomer: Mix components A and B evenly at a mass ratio of 4:1, pour them into a mold at 65°C, and react under a pressure of 12MPa to obtain a test piece. The test piece ...

Embodiment 3

[0032] The preparation method of the present embodiment polyurethane radiator comprises the following steps:

[0033] (1) Preparation of prepolymer A component:

[0034] Mix polyether polyol A and polyether polyol B evenly at a mass ratio of 1:1.8, heat up to 115°C, dehydrate under high vacuum -0.08±0.01MPa for 3.5h, then cool down to 45°C, add 0.4 times the mass The diphenylmethane diisocyanate of the total mass of polyether polyol was stirred evenly, and the temperature was raised to 90°C for 3 hours to react, and the mass content of isocyanate was detected to be 11% by sampling to obtain the prepolymer A component;

[0035] (2) Preparation of component B: chain extender MOCA and tin catalyst T9 are mixed evenly at a mass ratio of 300:1.5 to obtain component B;

[0036] (3) Production of polyurethane elastomer: Mix components A and B evenly at a mass ratio of 5:1, pour them into a mold at 70°C, and react and mold them under a pressure of 10MPa to obtain a test piece. The te...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of polyurethane and specifically relates to a preparation method of a polyurethane heating radiator. The preparation method of the polyurethane heating radiator comprises the following steps: uniformly mixing polyether polyol A and polyether polyol B, heating, dehydrating under high vacuum, cooling, adding diphenylmethane diisocyanate, uniformly stirring, heating and reacting, sampling and testing until mass content of isocyanate is 9-15% so as to obtain a prepolymer A component; uniformly mixing a chain extender and a tin catalyst to obtain a B component; uniformly mixing the A component and the B component, pouring the mixture into a mold, reacting to obtain a test piece, and vulcanizing the test piece to obtain a finished product. The prepared polyurethane heating radiator has good water resistance, is resistant to water seepage, is anti-rust, is not easy to block, has high hardness, is stretch-proof, is tear resistant, has high temperature resistance, will not deform, has stable physical properties, has more excellent heat dissipation performance than a metal product and is light. Production cost of the heating radiator is low. The preparation method is simple and easy to operate, and is easy to realize.

Description

technical field [0001] The invention belongs to the technical field of polyurethane, and in particular relates to a preparation method of a polyurethane radiator. Background technique [0002] Radiators are indispensable in the north of collective heating. Traditional metal radiators are prone to rust and blockage, and have a short service life. They are heavy, difficult to carry, and have high production costs. [0003] In the prior art, there are no literature reports related to polyurethane radiators. Contents of the invention [0004] The purpose of the present invention is to provide a method for preparing a polyurethane radiator. The obtained polyurethane radiator has good water resistance, no water seepage, no rust, no clogging, high hardness, stretch resistance, tear resistance, high temperature resistance, and no deformation , stable physical properties, better heat dissipation performance than metal products, light weight and low production cost. [0005] The p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G18/76C08G18/12C08G18/66C08G18/48C08G18/32
CPCC08G18/7671C08G18/12C08G18/4804C08G18/6685C08G18/3814
Inventor 耿佃勇荆晓东柴可军王帅董伟
Owner ZIBO DEXIN LIANBANG CHEM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap