Wear-resistant wood finish paint

A technology for topcoat and woodware, applied in the field of coatings, can solve the problems of easy yellowing construction surface gloss, insufficient transparency, poor wear resistance, etc., and achieve the effects of fast drying, clear wood grain and hard paint film

Inactive Publication Date: 2015-11-04
DRAGON FISH PAINT
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, although there are many kinds of wood topcoats sold in the market, most of the wood topcoats generally have the problems of poor wear resistance, brittleness, easy yellowing, poor surface gloss and insufficient transparency.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] This wear-resistant wood finish consists of the following raw materials:

[0015] 40 parts of cellulose nitrate, 10 parts of modified rosin resin, 1 part of alkyd resin, 3 parts of acrylic resin, 1 part of amino resin, 2 parts of dibutyl phthalate plasticizer, 5 parts of acetone solvent, isobutyl 1 part of alcohol co-solvent, 1 part of xylene diluent, 20 parts of inorganic aluminum oxide;

[0016] Its preparation method comprises the following steps:

[0017] A, cellulose nitrate and acetone are put into reactor and mix, carry out reaction;

[0018] B, the product that inorganic aluminum sesquioxide and A step make are put into grinder, grind to fineness less than 10 microns;

[0019] C. Pour the product obtained in step B into a high-speed disperser, add modified rosin resin, alkyd resin, acrylic resin and amino resin, butanol co-solvent and xylene diluent to disperse at a speed of 1000 rpm 2 Hours, that's it.

Embodiment 2

[0021] This wear-resistant wood finish consists of the following raw materials:

[0022] 50 parts of cellulose nitrate, 5 parts of modified rosin resin, 3 parts of alkyd resin, 2 parts of acrylic resin, 2 parts of amino resin, 1 part of dioctyl ester plasticizer, 8 parts of acetone solvent, 2 parts of isobutanol co-solvent 2 parts, 2 parts of xylene diluent, 30 parts of inorganic aluminum oxide;

[0023] Its preparation method is identical with embodiment 1.

Embodiment 3

[0025] This wear-resistant wood finish consists of the following raw materials:

[0026] 45 parts of cellulose nitrate, 2 parts of modified rosin resin, 2 parts of alkyd resin, 1 part of acrylic resin, 3 parts of amino resin, 3 parts of oxidized castor oil plasticizer, 10 parts of acetone solvent, 2 parts of isobutanol co-solvent 2 parts, 2 parts of xylene diluent, 40 parts of inorganic aluminum oxide;

[0027] Its preparation method is identical with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a wear-resistant wood finish paint, belonging to the technical field of paints. The wear-resistant wood finish paint is prepared from 40-50 parts of cellulose nitrate, 2-10 parts of modified rosin resin, 1-3 parts of alkyd resin, 1-3 parts of acrylic resin, 1-3 parts of amino resin, 1-3 parts of plasticizer, 5-10 parts of solvent, 1-2 parts of cosolvent, 1-3 parts of diluter and 20-40 parts of inorganic aluminum oxide. Compared with the prior art, by using the reasonable component matching, the wear-resistant wood finish paint has the advantages of high drying speed, hard paint film, high wear resistance and clear wood grains.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a wear-resistant wood finish paint. Background technique [0002] At present, although there are various types of wood topcoats sold in the market, most wood topcoats generally have the problems of poor wear resistance, brittleness, easy yellowing, poor surface gloss and insufficient transparency. Contents of the invention [0003] The problem to be solved by the present invention is to provide a wear-resistant wood topcoat with good wear resistance and clean wood grain. [0004] In order to solve the problems of the technologies described above, the technical solution adopted in the present invention is: [0005] It is made from the following raw materials in parts by weight: [0006] 40-50 parts of cellulose nitrate, 2-10 parts of modified rosin resin, 1-3 parts of alkyd resin, 1-3 parts of acrylic resin, 1-3 parts of amino resin, 1-3 parts of plasticizer, 5 parts of solv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D101/18C09D193/04C09D7/12
Inventor 韦光南
Owner DRAGON FISH PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com