Vanadium-contained TAM steel and manufacturing method thereof

A technology of weight percentage and chemical composition, applied in the field of vanadium-containing TAM steel and its manufacturing process, can solve problems such as inability to meet requirements, and achieve the effects of improving comprehensive mechanical properties, high strength and plasticity, and stable steel structure and properties

Inactive Publication Date: 2015-11-11
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Most of the research on TRIP steel in the prior art uses ordinary steel without adding vanadium, and the process only uses traditional technology. The comprehensive mechanical properties of the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Vanadium-contained TAM steel and manufacturing method thereof
  • Vanadium-contained TAM steel and manufacturing method thereof
  • Vanadium-contained TAM steel and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0029] The preparation method of vanadium-containing TAM steel includes the following steps:

[0030] a. Mechanical rolling process: the steel billet is smelted and cast into a slab, heated at 1150~1250℃ for 70~90min, then hot rolled into a 3~5mm thick hot rolled steel plate, and then cold rolled to 1~ 1.5mm, the cold rolling reduction ratio is 65-75%, and the ferrite + pearlite structure is obtained; among them, the finishing temperature of hot rolling is 750-850℃, and the coiling temperature is 650-700℃;

[0031] b. Q&P process: The cold-rolled sheet obtained in step a is first heated to austenitizing temperature of 900-920°C at 10°C / s, held for 600s, and then cooled to room temperature at 50°C / s; then at 10°C / s s Reheat it to the annealing temperature of 760-850℃, keep it for 600s, then reduce the temperature at 50℃ / s to the distribution temperature of 150-450℃, keep it for 50-200s, and finally reduce the temperature to room temperature at 50℃ / s to get it.

[0032] Further, as a ...

Example Embodiment

[0038] Example 1

[0039] The composition percentage of each component of the vanadium-containing TAM steel of the present invention is shown in Table 1:

[0040] Table 1 Composition percentage of vanadium-containing TAM steel

[0041]

[0042]

[0043] According to the composition percentage of each component of vanadium-containing TAM steel in Table 1, traditional mechanical rolling process smelting, hot rolling, cold rolling and new process Q&P process are carried out. The specific process parameters of the traditional mechanical rolling process are shown in Table 2:

[0044] Table 2 Specific process parameters of mechanical rolling process

[0045]

[0046] The specific process parameters of the new process Q&P process are shown in Table 3:

[0047] Table 3 Q&P process specific process parameters

[0048]

[0049] According to the composition percentage of each component of the vanadium-containing TAM steel in Table 1, the mechanical rolling process in Table 2, and the Q&P process in ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Yield strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Strong plastic productaaaaaaaaaa
Login to view more

Abstract

The invention relates to vanadium-contained TAM steel and a manufacturing method thereof, and belongs to the technical field of metal composition design and heat machining. The vanadium-contained TAM steel comprises, by weight percentage, 0.18%-0.21% of C, 1.48%-1.55% of Si, 1.90%-2.20% of Mn, not larger than 0.020% of P, not larger than 0.015% of S, 0.04%-0.06% of V, not larger than 0.04% of Al and the balanced Fe and inevitable impurities. An appropriate amount of vanadium is added in a vanadium alloying manner, the obdurability of the TAM steel is improved through precipitation of carbide of the vanadium and the like, and the comprehensive mechanical property of the vanadium-contained TAM steel is improved; and a steel plate has the higher strength and the higher plasticity, and the vanadium-contained TAM steel particularly has the excellent hydrogen-embrittlement-resistant delay breakage performance. A new technology, namely a Q&P process, is adopted in production of the vanadium-contained TAM steel, and therefore the steel structure property is more stable.

Description

technical field [0001] The invention relates to a vanadium-containing TAM steel and a manufacturing process thereof, belonging to the technical field of metal composition design and thermal processing. Background technique [0002] TAM steel, also known as TRIP type annealed martensitic steel (TRIP-aided Annealed Martensite Matrix), is a kind of Q&P steel. As the third-generation AHSS (Advanced High Strength Steels) steel, Q&P (Quenching and Partitioning) steel for automobiles has natural advantages and has achieved a good match between strength and plasticity. Laboratory data shows that the strength of Q&P steel for automobiles is above 1000 MPa, and the elongation reaches 18 % or more, fully capable of meeting the requirements of bumpers (anti-collision beams), side anti-collision beams (W-type) and other components. The biggest feature of TAM steel is that it breaks through the polygonal ferrite matrix or bainite matrix structure of traditional TRIP steel, and uses the a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/12C22C33/04
Inventor 蔡晓文杨雄飞唐静杨小琴
Owner PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap