A composite material and diamond technology, applied in metal material coating process, liquid chemical plating, coating, etc.

Active Publication Date: 2015-11-18
SHENZHEN RUN SUN CHEM TECH
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problems existing in the surface treatment of the above-mentioned existing diamond-copper composite materials, the present invention proposes a roughening solution for the diamond-copper composite material. To deal with the existing problem of copper bite reaction, it can also oxidize and dissolve the surface impurities of the diamond-copper composite material and adsorb various organic and inorganic substances, so that the surface of the diamond-copper composite material can be cleaned, roughened and hydrophilic, and the plating efficiency is improved. coverage efficiency and quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A roughening solution for diamond-copper composite materials, its preparation method is as follows: after mixing 1Kg sodium nitrite, 5Kg sodium hydroxide, 0.3Kg triethanolamine, 0.2Kg carbonamide peroxide and 93.2Kg water, add 0.3Kg Potassium ferrate is mixed evenly to obtain the coarsening liquid.

[0020] The method for plating nickel on the surface of a diamond-copper composite material comprises the following steps:

[0021] Put the diamond-copper composite material into the above-mentioned roughening solution for alkaline roughening, the reaction temperature is 40°C, and the reaction time is 30 minutes; then put the roughened diamond-copper composite material into a 10% by weight NaOH solution for alkaline Degreasing, reaction temperature 100°C, reaction time 10min, then wash the diamond-copper composite material with deionized water to neutrality; then put the diamond-copper composite material after pickling into the basic colloidal palladium activation solution f...

Embodiment 2

[0023] A roughening solution for diamond-copper composite materials, its preparation method is as follows: after mixing 5Kg sodium nitrite, 6Kg sodium hydroxide, 0.4Kg monoethanolamine, 0.3Kg carbonamide peroxide and 87.8Kg water, add 0.5Kg Potassium ferrate is mixed evenly to obtain the coarsening liquid.

[0024] The method for plating nickel on the surface of a diamond-copper composite material comprises the following steps:

[0025] Put the diamond-copper composite material into the above-mentioned roughening solution for alkaline roughening, the reaction temperature is 45°C, and the reaction time is 20 minutes; then put the roughened diamond-copper composite material into a 15% by weight NaOH solution for alkaline Degreasing, reaction temperature 100°C, reaction time 20min, then wash the diamond-copper composite material with deionized water until neutral; then put the pickled diamond-copper composite material into the saline-based colloidal palladium activation solution ...

Embodiment 3

[0027] A roughening solution for diamond-copper composite material, its preparation method is as follows: after mixing 3Kg potassium nitrite, 3Kg potassium hydroxide, 0.5Kg diethanolamine, 0.5Kg carbonamide peroxide and 92.7Kg water, add 0.3Kg After the sodium ferrate is mixed evenly, the roughened solution is obtained.

[0028] The method for plating nickel on the surface of a diamond-copper composite material comprises the following steps:

[0029] Put the diamond-copper composite material into the above-mentioned roughening solution for alkaline roughening, the reaction temperature is 50°C, and the reaction time is 15 minutes; then put the roughened diamond-copper composite material into a 20% by weight NaOH solution for alkaline Degreasing, reaction temperature 100°C, reaction time 20min, then wash the diamond-copper composite material with deionized water until neutral; then put the pickled diamond-copper composite material into the saline-based colloidal palladium activa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a roughing solution for a diamond-copper composite and a surface nickel plating method of the diamond-copper composite. The roughing solution is composed of, by weight, 1%-10% of nitrite, 1%-10% of strong base, 0.2%-0.6% of alcohol amine, 0.1%-0.8% of carbamide peroxide, 0.1%-0.6% of ferrate and 78%-97.6% of water. The surface nickel plating method comprises the steps that the surface of the diamond-copper composite is subjected to roughing, oil removal, activation, acid pickling and chemical nickel plating in sequence, and according to roughing, chemical roughing is carried out on the diamond-copper composite in the roughing solution. Strong oxidant and strong base are mixed in the roughing solution, so that the problem of a copper biting reaction existing in traditional acidic roughing solution treatment is solved, impurities on the surface of the diamond-copper composite can be oxidized and dissolved, and various organic substances and inorganic substances can be adsorbed; therefore, the effect that the surface of the diamond-copper composite is clean, roughed and hydrophilic can be achieved, and the plating efficiency and quality are improved.

Description

technical field [0001] The invention belongs to the technical field of surface treatment of diamond-copper composite materials, and in particular relates to a roughening solution for diamond-copper composite materials and a surface nickel plating method thereof. Background technique [0002] Diamond-copper composite material not only has good thermal conductivity and electrical conductivity of copper matrix, but also can give full play to the high thermal conductivity and low thermal expansion performance of diamond particles. It is an ideal high thermal conductivity and low expansion electronic packaging material. The thermal expansion coefficient of the diamond-copper composite material can be adjusted by controlling the diamond content, and the thermal expansion coefficient can be completely matched with semiconductor materials such as Si and GaAs in practice. Therefore, the diamond-copper composite material is a new type of electronic packaging material with very broad ap...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C18/18
Inventor 帅和平刘开喜杨红
Owner SHENZHEN RUN SUN CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap