A kind of trivalent chromium complex compound for hot-dip aluminum-zinc plate and preparation method thereof

A hot-dip aluminum-zinc plate and trivalent chromium technology, which is applied in the coating process of metal materials, can solve the problems of poor corrosion resistance and cannot meet the corrosion resistance requirements of aluminum-zinc plates, and achieve good corrosion resistance and environmental protection Requirements, overcoming destabilizing effects

Active Publication Date: 2018-04-27
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This patent is a passivation treatment method for a hot-dip galvanized sheet, but since the surface of the aluminum-zinc sheet also contains a large amount of aluminum (about 55%), after the use of the aluminum-zinc sheet, the corrosion resistance is very poor (NSST / 72h already more than 5%), which cannot meet the user's corrosion resistance requirements for aluminum-zinc panels

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of trivalent chromium complex compound for hot-dip aluminum-zinc plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Prepare trivalent chromium complexes for hot-dip galvanized sheets according to the raw materials numbered as 1-9 groups of trivalent chromium complexes in Table 1 below. The preparation method is roughly as follows: first, add hexavalent chromium into water, dissolve and stir Add the reducing agent after it is uniform, and after it is completely dissolved, add the acidic substance, and react for 1 to 6 hours under constant stirring.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of a trivalent chrome complex, in particular to a passivation processing solution for an environment-friendly hot dip aluminum-zinc plate and a passivation processing solution with excellent corrosion resistance. The trivalent chrome complex for the hot dip aluminum-zinc plate is prepared from water, hexavalent chromium, reducing agents and acidic materials according to the molar ratios of 100:0.2-1.5:0.1-4.5:0.2-7.5. The trivalent chrome complex for the hot dip aluminum-zinc plate has excellent corrosion resistance. Corrosion resistance of a solidified coating reaches the passivation level of hexavalent chromium, the requirement for environmental friendliness can be met, harmful elements like hexavalent chromium are not contained, and the trivalent chrome complex does not harm the environment or human bodies.

Description

technical field [0001] The invention relates to a preparation method of a trivalent chromium complex, in particular to an environment-friendly passivation treatment solution for hot-dip galvanized sheets, in particular to a passivation treatment solution with excellent corrosion resistance. Background technique [0002] The coating composition of hot-dip aluminum-zinc sheet combines the physical protection, high durability and electrochemical protection characteristics of Zn. It has formability, heat resistance and high reflectivity. Embossed and embossed, it is mainly used in the construction industry and electrical cabinets. At present, however, aluminum alloys are prone to damage in the form of pitting corrosion, crevice corrosion, stress corrosion and corrosion fatigue when used in humid, industrial gas, fuel gas, salt and dust atmospheres. The surface treatment of aluminum alloy is the key to expand its application range and prolong its service life. Hot-dip aluminum-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C22/46C23C22/34C23C22/53
Inventor 董学强郭太雄冉长荣岳安宏徐权常军张爱萍
Owner PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP