Reduced metal transmutation glaze, ceramic product prepared from same and preparation method

A technology of ceramic products and kiln-changing glaze, which is applied in the field of ceramics, can solve the problem of no metal spot glaze, etc., and achieve the effect of pure and bright color, favorable control and operation, and high yield

Active Publication Date: 2015-12-30
FUJIAN DEHUA HUAMAO CERAMICS CO LTD
View PDF2 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, metal spot glazes have not yet appeared, and the pursuit of the diversity and stability of ceramic glazes has become the goal pursued by many researchers in the field of ceramics in my country. Therefore, the research on reducing metal kiln variable spot glazes has great research value and market expectation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Reduced metal kiln glaze, including the following components in parts by mass: 35 parts of nepheline orthoclase, 5 parts of kyanite, 10 parts of barium carbonate, 25 parts of frit, 15 parts of quartz, 10 parts of kaolin, calcium carbonate 5 parts, 3 parts of cerium oxide, 30 parts of manganese oxide, 3.5 parts of copper oxide, and 1.5 parts of nickel oxide. The frit includes the following components in parts by mass: 50 parts of borax, 25 parts of quartz, 5 parts of kaolin, 15 parts of calcium carbonate, and 5 parts of potassium carbonate.

[0022] The method for preparing reduced metal kiln-changing glaze ceramic products with the reduced metal kiln-changing glaze comprises the following steps:

[0023] Step 1, grinding: according to the mass ratio of the frit, mix the raw materials evenly, and set aside; according to the mass ratio of the glaze, after mixing the raw material components, add water with 70% of the total weight of the raw materials for ball milling, ball...

Embodiment 2

[0028] Reduced metal kiln glaze, including the following components in parts by mass: 30 parts of nepheline orthoclase, 4 parts of kyanite, 8 parts of barium carbonate, 22 parts of frit, 14 parts of quartz, 7 parts of kaolin, calcium carbonate 2 parts, 2 parts of cerium oxide, 28 parts of manganese oxide, 3 parts of copper oxide, and 1 part of nickel oxide; wherein, the frit includes the following components in parts by mass: 48 parts of borax, 23 parts of quartz, kaolin 3 parts, calcium carbonate 13 parts, potassium carbonate 3 parts.

[0029] The method for preparing reduced metal kiln-changing glaze ceramic products with the reduced metal kiln-changing glaze comprises the following steps:

[0030] Step 1, grinding: according to the mass ratio of the frit, mix the raw materials evenly, and set aside; according to the mass ratio of the glaze, after mixing the raw material components, add water with 60% of the total weight of the raw materials for ball milling, ball milling T...

Embodiment 3

[0035] Reduced metal kiln glaze, including the following components in parts by mass: 40 parts of nepheline orthoclase, 7 parts of kyanite, 12 parts of barium carbonate, 27 parts of frit, 17 parts of quartz, 12 parts of kaolin, calcium carbonate 7 parts, 4 parts of cerium oxide, 32 parts of manganese oxide, 4 parts of copper oxide, 2 parts of nickel oxide; 7 parts, calcium carbonate 17 parts, potassium carbonate 7 parts.

[0036] The method for preparing reduced metal kiln-changing glaze ceramic products with the reduced metal kiln-changing glaze comprises the following steps:

[0037] Step 1, grinding: According to the mass ratio of the frit, mix the raw materials evenly and set aside; according to the mass ratio of the glaze, after mixing the raw material components, add water with 75% of the total weight of the raw materials for ball milling, ball milling The rotating speed at the time is 450r / min, and the ball mill is 50h, and then the slurry is discharged for subsequent ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a reduced metal transmutation glaze, a ceramic product prepared from the same and a preparation method and belongs to the technical field of ceramic. The reduced metal transmutation glaze comprises components in parts by mass as follows: 30-40 parts of nepheline-syenite, 4-7 parts of kyanite, 8-12 parts of barium carbonate, 22-27 parts of a frit, 14-17 parts of quartz, 7-12 parts of kaolin, 2-7 parts of calcium carbonate, 2-4 parts of cerium oxide, 28-32 parts of manganese oxide, 3-4 parts of copper oxide and 1-2 parts of nickel oxide, wherein the frit comprises components in parts by mass as follows: 48-52 parts of borax, 23-27 parts of quartz, 3-7 parts of kaolin, 13-17 parts of calcium carbonate and 3-7 parts of potassium carbonate. The reduced metal transmutation glaze ceramic product has reddish brown ground coat on the surface, gold spots flush with the glaze surface are formed on the glaze coat, and the color of the glaze is pure, bright and dazzling.

Description

technical field [0001] The invention belongs to the technical field of ceramics, and in particular relates to a reduced metal kiln-transformed glaze, ceramic products prepared therefrom and a preparation method. Background technique [0002] With the continuous development of ceramic glazes, more and more ceramic glazes are well known to the public. At present, the existing glazes are gradually developing in the direction of environmentally friendly lead-free, fritted glazes, and the firing of glazes There are mainly oxidation firing and reduction firing, and the use of different firing methods also has a great influence on the firing effect of the glaze. Metal glaze is a special glaze with a metallic texture. The reason why the metal glaze is metallic is that metal elements, such as iron oxide and copper oxide, are added to the glaze. At present, most of the existing metal glazes are metal glazes with smooth surface, and have good wear resistance and corrosion resistance, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/00C04B41/86
Inventor 陈能谨
Owner FUJIAN DEHUA HUAMAO CERAMICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com