Tile-seam filling

A sealant and ceramic tile technology, applied in the field of tile sealant, can solve the problems of low strength, powder falling, easy to dirty and black, etc., and achieve the effect of good waterproof, low cost and high adhesion

Inactive Publication Date: 2015-12-30
DONGGUAN WEIYE CEMENT CO LTD
View PDF1 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The grout that is commonly used to fill the gaps between tile

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0008] Example 1. This example discloses a caulking agent. The weight ratio of raw materials is: ordinary Portland cement (P.042.4R) 43, quartz sand 40, mineral oil type defoamer 0.1, and Dispersed latex powder 10, hydroxypropyl methylcellulose 0.2, organosilicon water repellent 0.2, anti-efflorescence agent 0.5, anhydrous gypsum 1, iron oxide series pigment 5.

[0009] This embodiment discloses a joint sealant, which has good water resistance, is not easy to turn black, has high adhesion, is alkali-resistant, and has low cost, and is a good joint sealant for tile paving.

Example Embodiment

[0010] Example 2. This example discloses a caulking agent. The weight ratio of raw materials is: ordinary Portland cement (P.042.4R) 40, quartz sand 36, mineral oil type defoamer 0.05, and Dispersed latex powder 15, hydroxypropyl methylcellulose 0.25, organosilicon water repellent 0.3, anti-efflorescence agent 0.6, anhydrous gypsum 1.8, iron oxide series pigment 6.

[0011] This embodiment discloses a joint sealant, which has good water resistance, is not easy to turn black, has high adhesion, is alkali-resistant, and has low cost, and is a good joint sealant for tile paving.

Example Embodiment

[0012] Example 3, this example discloses a caulking agent, the weight ratio of raw materials is: ordinary Portland cement (P.042.4R) 46, quartz sand 32, mineral oil type defoamer 0.2, re Dispersed latex powder 15, hydroxypropyl methyl cellulose 0.3, silicone water repellent 0.2, anti-efflorescence agent 0.3, anhydrous gypsum 2, iron oxide series pigment 4.

[0013] This embodiment discloses a joint sealant, which has good water resistance, is not easy to turn black, has high adhesion, is alkali-resistant, and has low cost, and is a good joint sealant for tile paving.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of construction materials, and relates to tile-seam filling which is prepared from the following raw materials in parts by weight: 35 to 60 percent of ordinary Portland cement (P.042.4R), 30 to 65 part of quartz sand, 0.01 to 0.2 parts of mineral oil type deformer, 10 to 30 parts of redispersible latex powder, 0.1 to 0.5 parts of HPMC (hydroxypropyl methyl cellulose), 0.2 to 1 part of organosilicon water repellent, 0.2 to 1 part of anti-whiskering agent, 1 to 3 parts of anhydrite, and 3 to 10 parts of ferric oxide series pigment. The tile-seam filling has the characteristics of being good in waterproofness, not liable to blacken, high in adhesive force, alkali-resistant and low in cost, capable of applying to decorating and seam filling of materials such as various ceramic tiles, floor tiles, wall tiles, mosaic tiles, marble and granite, and cultured stones.

Description

technical field [0001] The invention belongs to the technical field of building materials, and relates to a ceramic tile caulking agent. Background technique [0002] The laying of ceramic tiles has become a common decoration in daily life. From home to hotels and other public places, from the ground to the wall, the decorative effect brought by ceramic tiles is beautiful. However, in the process of laying and laying, bricks and The gaps between the bricks require special treatment. The sealants commonly used to fill the gaps between tiles are easy to get dirty and black, low in strength, and powdery. Contents of the invention [0003] The object of the present invention is to provide a tile grout that has good water resistance, is not easy to turn black, has high adhesion, alkali resistance and low cost, so as to solve the deficiencies in the prior art. [0004] The technical scheme adopted in the present invention is: a kind of ceramic tile caulking agent, the weight r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/04
Inventor 谢浩贤
Owner DONGGUAN WEIYE CEMENT CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products