UV cured strippable water-based coating and preparing method thereof

A water-based coating, water-based technology, applied in anti-corrosion coatings, polyurea/polyurethane coatings, coatings, etc., can solve the problems of long curing time, easy to rust, etc., and achieve the effect of short drying time, simple process and excellent water resistance

Inactive Publication Date: 2016-01-06
SHANGHAI APPLIED TECHNOLOGIES COLLEGE
View PDF2 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the above-mentioned technical problems in the prior art, the invention provides a UV curable strippable water-based coating and a preparation method thereof, which solves the problems in the prior art. The technical problems of long curing time and easy rusting of strippable coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0085] A kind of UV curable strippable water-based paint, calculated by weight parts, its raw material composition and content are as follows:

[0086] 60 parts of UV curing water-based polyurethane resin,

[0087] Leveling agent 0.05 parts,

[0088] 1 part of wetting agent,

[0089] 1 part thickener,

[0090] 0.2 parts of defoamer,

[0091] 2 parts of film-forming aids,

[0092] 3 parts of photoinitiator,

[0093] 3 parts of anti-rust and anti-corrosion agent,

[0094] 0.10 parts of anti-mildew and antibacterial agent,

[0095] Functional filler 10 parts,

[0096] 10 parts of water-based stripping agent,

[0097] Wherein said UV curable waterborne polyurethane resin is the JAZO emulsion of Nanjing Jiazhong Chemical Technology Co., Ltd.;

[0098] Described antirust corrosion inhibitor is the zinc phosphate of Shanghai Chemical Reagent Company;

[0099] Described photoinitiator is the water-based photoinitiator 819-DW that Tianjin Heinz Technology Development Co., Ltd...

Embodiment 2

[0115] A kind of UV curable strippable water-based paint, calculated by weight parts, its raw material composition and content are as follows:

[0116] 70 parts of UV curing water-based polyurethane resin,

[0117] Leveling agent 0.1 part,

[0118] 10 parts of wetting agent,

[0119] 3 parts of thickener,

[0120] 1 part of defoamer,

[0121] 5 parts of film-forming aids,

[0122] 6 parts of photoinitiator,

[0123] 8 parts of anti-rust and anti-corrosion agent,

[0124] 0.30 parts of anti-mildew and antibacterial agent,

[0125] Functional filler 20 parts,

[0126] 20 parts of water-based stripping agent,

[0127] Wherein said UV curable waterborne polyurethane resin is the JAZO emulsion of Nanjing Jiazhong Chemical Technology Co., Ltd.;

[0128] Described antirust resist is the aluminum tripolyphosphate of Shanghai Chemical Reagent Company;

[0129] Described photoinitiator is the water-based photoinitiator 819-DW that Tianjin Heinz Technology Development Co., Ltd....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a UV cured strippable water-based coating. The UV cured strippable water-based coating is prepared from, by weight, 60-70 parts of UV cured water-based polyurethane resin, 0.05-0.1 part of flatting agent, 1-10 parts of wetting agents, 1-3 parts of thickening agents, 0.2-1 part of antifoaming agent, 2-5 parts of film coalescing agents, 3-6 parts of photoinitiator, 3-8 parts of rust-proof resist, 0.10-0.30 part of mould-proof antibacterial agent, 10-20 parts of functional filler and 10-20 parts of water-based stripping agents. The invention further provides a preparing method of the coating. The preparing method includes the steps that a part of the wetting agents, the antifoaming agent, the rust-proof resist and deionized water are added into a high-speed dispersion machine and dispersed through stirring, the functional filler is added and dispersed through stirring, and the UV cured water-based polyurethane resin, the remaining antifoaming agent, the remaining wetting agents, the flatting agent, the film coalescing agents, the water-based stripping agents, the photoinitiator and the mould-proof antibacterial agents are added and uniformly stirred, continue to be dispersed and are filtered after being mixed to obtain the UV cured strippable water-based coating.

Description

technical field [0001] The invention belongs to the field of macromolecular materials, and in particular relates to a UV-curable peelable water-based paint and a preparation method thereof. Background technique [0002] Peelable paint is a temporary protective material with polymer as the main film-forming substance. It is sprayed on the surface of the object when it is used, and it will protect the object for a short time after the film is formed; The film layer is gently peeled off from the surface of the object to be coated by hand, which will not only cause no damage to the surface of the object to be coated, but also make the appearance of the original device as clean as new. Strippable coatings are widely welcomed by industries such as instruments, meters, home appliances, machinery, automobiles, and electronic appliances due to their convenient coating and easy peeling, and are developing rapidly. [0003] At present, there are mainly two types of solvent-based strip...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D175/14C09D5/20C09D5/08C09D7/12
Inventor 张英强梁华丽李烨
Owner SHANGHAI APPLIED TECHNOLOGIES COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More