Composite carburizing and quenching heat treatment method of gear

A heat treatment method and compound infiltration technology, applied in the field of heat treatment, can solve the problems of reducing wear resistance, toughness and comprehensive mechanical properties of gears, low surface hardness of gears, and high austenite content, so as to improve comprehensive mechanical properties and improve Wear resistance, effect of refining martensitic needles

Active Publication Date: 2016-01-13
CRRC QISHUYAN INSTITUTE CO LTD
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although this method can effectively reduce the internal oxidation of the gear and reduce the deformation of the gear, and improve the contact fatigue performance of the gear, in-depth research shows that there are the following deficiencies: after carburizing and quenc

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite carburizing and quenching heat treatment method of gear
  • Composite carburizing and quenching heat treatment method of gear
  • Composite carburizing and quenching heat treatment method of gear

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0039] The purpose, advantages and characteristics of the present invention will be illustrated and explained through the following non-limiting description of preferred embodiments. These embodiments are only typical examples of applying the technical solutions of the present invention, and any technical solutions formed by equivalent substitutions or equivalent transformations fall within the protection scope of the present invention.

[0040] The compound carburizing and quenching heat treatment method of locomotive traction gear disclosed in this embodiment is as follows figure 2 As shown, it includes the following steps:

[0041] S1, carburizing step: put the locomotive traction gear into a carburizing furnace with an initial temperature of about 900°C, heating to 920°C, and passing carburizing agent into the carburizing furnace to form a carburizing atmosphere. The carburizing agent is methanol, ethane , Propane, ethanol, propanol, ethyl acetate, any one or a combination of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a composite carburizing and quenching heat treatment method of a gear, and belongs to the technical field of heat treatment. The method comprises the steps of carburization, cooling, heating, quenching and tempering. The composite carburizing and quenching heat treatment method can effectively refine grains and martensite needles, improves the gear surface hardness, further improves the wear resistance, the fatigue strength and the corrosion resistance of the gear, and improves comprehensive mechanical performance of the gear.

Description

technical field [0001] The invention relates to a heat treatment method, in particular to a compound carburizing and quenching heat treatment method for locomotive traction gears, and belongs to the technical field of heat treatment. Background technique [0002] For high-speed trains, gears are crucial parts directly related to train safety. In recent years, the speed increase of trains has posed new challenges to the performance of locomotives, and thus put forward higher requirements for the performance of locomotive traction gears. Specifically, the gear is required not only to have sufficient strength and impact toughness to ensure absolute safety and reliability under the highest speed and load; but also to have excellent hardness and wear resistance on the surface of the gear to ensure good contact fatigue performance and Long life. [0003] At present, the heat treatment of locomotive traction gears basically adopts the process of carburizing and quenching surface ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C8/22C21D1/18C21D9/32
CPCC21D1/18C21D9/32C21D2211/008C23C8/22
Inventor 刘聪敏黄星谭小明石磊
Owner CRRC QISHUYAN INSTITUTE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap