A refractory material, basic technology, applied in the field of new basic refractory materials, can solve the problem of short service life and other problems
Inactive Publication Date: 2016-01-27
SINOMA CHENGDU ENERGY TECH
View PDF5 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] In this field, there are still few refractory materials under alkaline environment, and the existing refractory materials under alkaline environment basically do not have long service life
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0029] A new type of alkaline refractory material, characterized by the following components: quartz sand, phenolic resin, magnesium silicate, sodium silicate, magnesium oxide and calcium oxide.
[0030] A new type of alkaline refractory material, which is described, is characterized by: a new type of alkaline resistance material contains the following components, and the weight of each component is:
[0038] A new type of alkaline refractory material, which is described, is characterized by: a new type of alkaline resistance material contains the following components, and the weight of each component is:
[0046] A new type of alkaline refractory material, which is described, is characterized by: a new type of alkaline refractory material contains the following components, and the weight of each component is:
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Technical field [0001] The invention is a high -temperature technology field in pipelines, involving the manufacture of new alkaline refractory materials, and especially involves a new type of alkaline refractory material. Background technique [0002] A type of inorganic non -metal material with a fire resistance of not less than 1599 ° C.The refractory resistance refers to the tainer sample of the refractory material cone -shaped samples to resist the high temperature effect without softening the melting temperature.However, it is not possible to comprehensively describe the refractory material by defining it alone, and 1599 ° C is not absolute.It is now defined as the material that the physical chemistry allows it to use in high temperature environments is called refractory material.Refractory materials are widely used in industrial fields such as metallurgy, chemical industry, petroleum, mechanical manufacturing, silicate, and power. The most dosage in the metallurgical indus...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More