Manufacturing method of self-adhesive butyl rubber waterproof coiled material

A technology of butyl rubber and waterproof membrane, which is applied in the direction of adhesives, polymer adhesive additives, film/sheet adhesives, etc., and can solve the problem of poor compatibility of non-body materials, high production costs, and high production costs. Complicated process and other issues, to achieve the effect of low comprehensive production cost, outstanding aging resistance, and good chemical stability

Active Publication Date: 2016-01-27
DANDONG SANGUAN WATERPROOF MATERIAL CO LTD
View PDF10 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Both the main waterproof layer and the self-adhesive layer of the waterproof membrane are made of butyl rubber, which can effectively solve the problems of poor bonding compatibility and poor weather resistance of non-body materials existing in the prior art
However, the main waterproof layer and the self-adhesive layer are made of butyl rubber as the main raw material, and there will be problems of complicated production process and high production cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] 1. Preparation of butyl rubber coarse compound

[0052] Waste butyl rubber to remove impurities, cut into small pieces, and set aside.

[0053] Add 50kg of waste butyl rubber cut into small pieces into a 55-liter pressurized kneader, control the temperature at about 90°C, and carry out rough mixing for about 6 minutes; then add 10kg of carbon black within 8 minutes and continue mixing refining, to obtain butyl rubber rough mix.

[0054] 2. Prepare the base layer of butyl rubber waterproof membrane

[0055] Add 15kg of butyl rubber rough mix, 12kg of 325 mesh light calcium carbonate, 0.045kg of paraffin, and 0.045kg of stearic acid into a high-speed mill with an automatic feeding device. The speed ratio of the high-speed mill is 1 : more than 1.575, the temperature is blended into a butyl rubber sheet I with a thickness of about 0.5mm at about 70°C.

[0056] Use a three-roller calender to make butyl rubber sheets I into butyl rubber waterproof membrane bases of differ...

Embodiment 2

[0063] 1. Preparation of butyl rubber coarse compound

[0064] Waste butyl rubber to remove impurities, cut into small pieces, and set aside.

[0065] Add 45kg of waste butyl rubber cut into small pieces into a 55-liter pressurized kneader, control the temperature at about 90°C, and carry out rough mixing for about 6 minutes; then add 8kg of carbon black within 8 minutes and continue mixing refining, to obtain butyl rubber rough mix.

[0066] 2. Prepare the base layer of butyl rubber waterproof membrane

[0067] Add 19kg of butyl rubber rough mix, 17kg of 325 mesh light calcium carbonate, 0.04kg of paraffin, and 0.06kg of stearic acid into a high-speed mill with an automatic feeding device. The speed ratio of the high-speed mill is 1 : Above 1.575, the temperature is blended into butyl rubber sheet I at about 75°C.

[0068] Use a three-roller calender to make butyl rubber sheets I into butyl rubber waterproof membrane bases of different thicknesses, with a line speed of 17-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a manufacturing method of a self-adhesive butyl rubber waterproof coiled material. Solid waste butyl rubber is utilized, high-temperature desulfurization is not needed, a high shearing force is applied, the operating temperature is controlled below 100 DEG C, and a butyl rubber waterproof coiled material base course is prepared directly and is used as a main waterproof layer; a butyl rubber self-adhesive layer in the middle is a paste-shaped self adhesive which is also prepared from waste butyl rubber and is used as an auxiliary waterproof layer; and the lower surface can be isolated by using removable anti-adhesive paper. The waterproof coiled material provided by the invention has excellent water resistance and outstanding aging resistance, and is energy-saving and environment-friendly.

Description

technical field [0001] The invention relates to a method for manufacturing self-adhesive butyl rubber waterproof coiled material. Background technique [0002] Waterproof membrane is a commonly used material in building construction. It is mainly used for waterproof construction of building roofs and underground works, and plays a vital role in resisting the leakage of rainwater and groundwater. Today, due to the pollution of the atmosphere and underground, waterproofing membranes must not only have excellent weather resistance, but also have corrosion resistance and chemical stability. [0003] Self-adhesive butyl rubber waterproof membrane, including the main waterproof layer, butyl rubber self-adhesive layer and anti-adhesive film, wherein the main waterproof layer and butyl rubber self-adhesive layer are combined together, and the anti-adhesive film is arranged on the butyl rubber The lower surface of the self-adhesive layer. Most of the main waterproof layers of self-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J7/02C09J123/22C09J11/08C09J11/04C08L23/22C08L91/06C08K3/26C08K5/09
Inventor 刘华静
Owner DANDONG SANGUAN WATERPROOF MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com