Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A kind of high partial discharge voltage solar battery back plate base film and preparation method thereof

A technology for solar cells and backplane base films, which can be used in chemical instruments and methods, lamination, electronic equipment, etc., and can solve problems such as insufficient

Active Publication Date: 2017-07-11
四川东方绝缘材料股份有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Regardless of the blending or foaming technology of the third material, although the partial discharge performance of the solar backplane PET polyester base film is improved to a certain extent (the partial discharge voltage of the solar backplane PET backplane base film with a thickness of 250 μm reaches 1100V ), but it is far from enough to require a higher partial discharge voltage for the solar backplane PET polyester base film (the partial discharge voltage of the solar backplane PET backplane base film with a thickness of 250 μm reaches 1500V)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high partial discharge voltage solar battery back plate base film and preparation method thereof
  • A kind of high partial discharge voltage solar battery back plate base film and preparation method thereof
  • A kind of high partial discharge voltage solar battery back plate base film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0079] Part VI Preparation of Hydrolysis-resistant PET Resin

[0080] Basic process: Mix 1 mass part of the hydrolysis-resistant PET masterbatch prepared in Examples 3-1 to 3-10 and 9 to 99 mass parts of PET polyester resin with an intrinsic viscosity of 0.60dl / g to 0.85dl / g, and mix evenly in After drying at a drying temperature of 150°C to 170°C for 2h to 4h, extrude through twin-screw extruder 4# at a temperature of 265°C to 285°C, pelletize, and set aside.

[0081] The formulation and dosage of the hydrolysis-resistant PET resin prepared in Examples 5-1 to 5-10 are shown in Table 6 below:

[0082] Table 6: Formulation table of the hydrolysis-resistant PET resin of Examples 5-1 to 5-10 (unit: ㎏)

[0083]

[0084] Note: The hydrolysis-resistant PET masterbatches in Examples 3-1 to 3-10 are used in sequence for each example in Examples 5-1 to 5-10 in the above table.

[0085] Part VII Preparation of Base Film for High PD Voltage Solar Cell Backplane

[0086] Basic proce...

Embodiment 7

[0095] A high partial discharge voltage solar battery backplane base film, the high partial discharge voltage solar battery backplane base film is composed of A-layer polyester film with high partial discharge voltage function and B-layer polyester film with hydrolysis resistance function , the mass ratio of the A-layer polyester film to the B-layer polyester film is 400:100, and the thickness of the base film of the high partial discharge voltage solar cell backplane is 100 μm;

[0096] The high partial discharge voltage solar battery backplane base film is made by passing 400 parts by mass of the high partial discharge voltage PET resin for the A layer and 100 parts by mass of the hydrolysis-resistant PET resin for the B layer through two extruders at 260° C. After melting, it is layered and co-extruded through a resin melt distributor, cast on a cold drum at 15°C, stretched longitudinally by 2.9 times, stretched transversely by 3.0 times, and heat-set at 190°C to obtain (PET...

Embodiment 8

[0103] A high partial discharge voltage solar battery backplane base film, the high partial discharge voltage solar battery backplane base film is composed of A-layer polyester film with high partial discharge voltage function and B-layer polyester film with hydrolysis resistance function , the mass ratio of the A-layer polyester film to the B-layer polyester film is 900:100, and the thickness of the base film of the high partial discharge voltage solar cell backplane is 350 μm;

[0104] The high partial discharge voltage solar battery backplane base film is made by passing 900 parts by mass of the high partial discharge voltage PET resin for the A layer and 100 parts by mass of the hydrolysis-resistant PET resin for the B layer through two extruders at 290° C. After melting, it is layered and co-extruded through a resin melt distributor, cast on a cold drum at 25°C, stretched longitudinally by 3.5 times, stretched transversely by 3.5 times, and heat-set at 230°C to obtain (PET...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high partial discharge voltage solar battery back board base film and a preparation method of the high partial discharge voltage solar battery back board base film. The high partial discharge voltage solar battery back board base film is characterized by consisting of an A-layer polyester film which has a high partial discharge voltage function and a B-layer polyester film which has a hydrolysis resisting function in a compounding way. The preparation method is characterized in that the A-layer polyester film and the B-layer polyester film can be extruded in a layered co-extrusion way by a resin melt distributor after being respectively molten through an extruder under 260 to 290 DEG C according to (400 to 900) : 100 of a mass ratio of the A-layer polyester film and the B-layer polyester film, sheet casting can be carried out on a cold drum of which the temperature is 15 to 25 DEG C, then 2.9 to 3.5 times of longitudinal stretching and 3.0 to 3.5 times of transverse two-way stretching can be carried out, heat setting can be carried out under 190 to 230 DEG C, and then the high partial discharge voltage solar battery back board base film of which the thickness is 100 mum to 350 mum can be obtained. According to the high partial discharge voltage solar battery back board base film disclosed by the invention, the partial discharge voltage of the high partial discharge voltage solar battery back board base film is 800 to 1800 V; the good performance of the partial discharge voltage, the long-term UV (Ultra Violet) resistance and the like can be obtained; the high partial discharge voltage solar battery back board base film is applied to manufacturing of solar photovoltaic battery back board materials.

Description

technical field [0001] The invention belongs to a functional thin film made of polyester and its preparation, and relates to a high partial discharge voltage solar cell back plate base film and a preparation method thereof. The high partial discharge voltage solar battery backplane base film of the invention is suitable for the manufacture of solar photovoltaic battery backplane materials. Background technique [0002] In recent years, with the improvement of the voltage level of power equipment and the wide application of various organic insulating materials, the problem of partial discharge (referred to as PD) of power equipment has become more and more prominent. Partial discharge will gradually corrode and damage the insulating material, and the discharge area will continue to expand, eventually leading to the breakdown of the entire insulator. Therefore, it is very important to study the partial discharge of the solar battery backplane base film; in the prior art, the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B27/06B32B27/16B32B27/36B32B37/06B32B37/10B32B37/15C08L67/02C08G63/183C08K13/02C08K3/22C08K3/36C08K3/30
CPCB32B27/06B32B27/16B32B27/36B32B37/06B32B37/10B32B37/15B32B2250/02B32B2250/244B32B2307/21B32B2307/212B32B2457/12C08G63/183C08J5/18C08J2367/02C08J2467/02C08K2201/011C08L67/02C08L2203/16C08L2205/025C08L2205/03C08K13/02C08K2003/2241C08L75/00C08K5/29
Inventor 张世明周柯罗春明唐安斌
Owner 四川东方绝缘材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com