Reinforced fishing net

A technology for fishing nets and plasticizers, applied in the field of enhanced fishing nets, can solve the problems affecting the amount of fish caught, strength, insufficient wear resistance, easy tearing of fishing nets, etc., to achieve long service life, good wear resistance, and high fish catch increased effect

Inactive Publication Date: 2016-02-03
六安市沪渔网具有限公司
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Fishing nets are used for fishing. Currently, fishing nets are mainly made of nylon materials, which are not strong enough in terms of strength and wear resistance. If they are operated in complex sea areas, the fishing nets are easy to tear and affect the amount of fish caught.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A fishing net is composed of the following ingredients in parts by weight: polyethylene 120, nylon 80, titanium dioxide 3, ammonium tribromide 5, sodium stearate 4 and modified plasticizer 8.

[0013] The plasticizer is composed of the following components by weight: styrene 2.1, sodium borate 1.3, dioctyl ester 1.9, nano-titanium dioxide 1.6 and aluminum potassium sulfate 1.4; the preparation method of the plasticizer is: adding aluminum potassium sulfate and sodium borate Put it into the mixture of other ingredients, heat while stirring, stir for 35 minutes, and control the temperature at 100°C to prepare the modified plasticizer.

[0014] A method for preparing a reinforced fishing net, comprising the following preparation steps:

[0015] (1) Add above-mentioned polyethylene 120, nylon 80 and ammonium tribromide 5 together in the mixer and stir evenly, and the stirring time is 20 minutes;

[0016] (2) Put the uniformly stirred mixture into a reactor, add titanium di...

Embodiment 2

[0023] A fishing net is composed of the following ingredients in parts by weight: polyethylene 125, nylon 85, titanium dioxide 5, ammonium tribromide 5, sodium stearate 5 and modified plasticizer 9.

[0024] The plasticizer is composed of the following components by weight: styrene 2.2, sodium borate 1.4, dioctyl ester 1.9, nano-titanium dioxide 1.7 and aluminum potassium sulfate 1.6; the preparation method of the plasticizer is: adding aluminum potassium sulfate and sodium borate Put it into the mixture of other ingredients, heat while stirring, and stir for 45 minutes, the temperature is controlled at 110°C, and the modified plasticizer can be prepared.

[0025] A method for preparing a reinforced fishing net, comprising the following preparation steps:

[0026] (1) The above-mentioned polyethylene 125, nylon 85 and ammonium tribromide 5 are added together in the mixer and stirred evenly, and the stirring time is 25 minutes;

[0027] (2) Put the uniformly stirred mixture in...

Embodiment 3

[0035] A fishing net is composed of the following ingredients in parts by weight: polyethylene 130, nylon 90, titanium dioxide 6, ammonium tribromide 6, sodium stearate 5 and modified plasticizer 10.

[0036] The plasticizer is composed of the following components by weight: styrene 2.3, sodium borate 1.5, dioctyl 2.0, nano-titanium dioxide 1.8 and aluminum potassium sulfate 1.7; the preparation method of the plasticizer is: adding aluminum potassium sulfate and sodium borate Put it into the mixture of other ingredients, heat while stirring, and stir for 60 minutes, the temperature is controlled at 120°C, and the modified plasticizer can be prepared.

[0037] A method for preparing a reinforced fishing net, comprising the following preparation steps:

[0038] (1) Add the above-mentioned polyethylene 130, nylon 90 and ammonium tribromide 6 into the mixer and stir evenly, and the stirring time is 30 minutes;

[0039] (2) Put the uniformly stirred mixture into a reactor, add tit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention relates to a reinforced fishing net, and relates to the technical field of fishing net manufacturing. The reinforced fishing net is prepared from the following components in parts by weight: 120-130 parts of polyethylene, 80-90 parts of nylon, 3-6 parts of titanium dioxide, 5-6 parts of triammonium bromide, 4-5 parts of sodium stearate and 8-10 parts of a modified plasticizer. By adopting the reinforced fishing net, the problem that a conventional fishing net is insufficient in abrasion resistance is solved, a fishing net which is high in strength and good in abrasion resistance is provided, the fishing net is solid and resistant to abrasion, not easy to break and long in service life, and the fish catching amount can be greatly increased.

Description

technical field [0001] The invention relates to the technical field of fishing net production, in particular to a reinforced fishing net. Background technique [0002] Fishing nets are used for fishing. Now fishing nets are mainly made of nylon materials, which are not strong enough in terms of strength and wear resistance. If they are operated in complex sea areas, the fishing nets are easy to tear and affect the amount of fish caught. Contents of the invention [0003] The technical problem to be solved by the invention is to provide a fishing net with good abrasion resistance. [0004] In order to solve the above problems, a reinforced fishing net according to the present invention is composed of the following components by weight: polyethylene 120-130, nylon 80-90, titanium dioxide 3-6, ammonium tribromide 5-6, Sodium stearate 4-5 and modified plasticizer 8-10. [0005] The plasticizer is composed of the following components by weight: styrene 2.1-2.3, sodium borate ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L77/00C08K13/06C08K9/04C08K3/22C08K5/098C08K3/28C08K3/38
CPCC08L23/06C08K2201/011C08L77/00C08K13/06C08K9/04C08K2003/2237C08K5/098C08K3/28C08K2003/387
Inventor 汪卫东王修德许宏兵蒋传胜
Owner 六安市沪渔网具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com