Polypropylene transparent material for melting, depositing and forming and preparation method thereof

A fused deposition modeling, transparent material technology, applied in the field of 3D printing technology and plastic processing, can solve the problems of reducing the shrinkage and deformation of printed parts, expanding polypropylene materials, opacity, etc., to suppress the phenomenon of large-area crystallization, and improve light transmission. The effect of improving the properties, toughness, and light transmittance

Inactive Publication Date: 2016-02-03
HENAN INST OF ENG
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a polypropylene transparent material for fused deposition molding to overcome the opaque defects of existing polypropylene materials for fused deposition molding due to crystallization and inorganic fillers. The addition of a transparent agent can avoid the occurrence of large-area cr

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polypropylene transparent material for melting, depositing and forming and preparation method thereof
  • Polypropylene transparent material for melting, depositing and forming and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The polypropylene transparent material for fused deposition molding in this embodiment is made of the following raw materials: 99 g of polypropylene, 0.1 g of transparent agent, 1 g of compatibilizer, 0.9 g of plasticizer, and 0.2 g of stabilizer.

[0034] The polypropylene is a polymer obtained by the polymerization of propylene alone. The polypropylene material used is produced by Sinopec Yangzi Petrochemical Co., Ltd., the brand is M02-V, the transparent agent is 2,6-phthalic acid cyclohexylamide, and the compatibilizer is It is maleic anhydride grafted polypropylene, and the stabilizer is hindered phenol macromolecular antioxidant.

[0035] The preparation method of the polypropylene transparent material for fused deposition molding in this embodiment, the steps are as follows:

[0036] (1) Mixing of reagents and raw materials: first put polypropylene into the mixer, then add transparent agent, lubricant and plasticizer, and stir until the surface of the particles i...

Embodiment 2

[0040] The polypropylene transparent material for fused deposition molding in this embodiment is made of the following raw materials: 99g of polypropylene, 0.1g of transparent agent, 1g of compatibilizer, 0.9g of plasticizer, and 0.2g of stabilizer;

[0041] The polypropylene is a polymer obtained by copolymerization of propylene and other olefins, and the general chemical structure formula of the transparent agent is R2-NHCO-R1-CONH-R2, wherein the group R1 is One of the groups R2 is -CH 3 , another group R2 is -CH 2 CH 3 ; The compatibilizer is maleic anhydride grafted polypropylene; the plasticizer is a mixture of dioctyl phthalate and epoxy soybean oil; the stabilizer is antioxidant 1010 and four [β-(3,5- A mixture of di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester.

[0042]The preparation method of the polypropylene transparent material for fused deposition molding in this embodiment is the same as that in Embodiment 1.

Embodiment 3

[0044] The polypropylene transparent material for fused deposition molding in this embodiment is made of the following raw materials: 95g of polypropylene, 0.5g of transparent agent, 1.5g of compatibilizer, 0.1g of plasticizer, and 0.01g of stabilizer.

[0045] Wherein the polypropylene is a blend of a polymer obtained by the polymerization of propylene alone and a polymer obtained by copolymerization of propylene and other olefins; the general chemical formula of the transparent agent is R2-NHCO-R1-CONH-R2, wherein the group R1 is One of the groups R2 is Another group R2 is The compatibilizer is maleic anhydride grafted polypropylene; the plasticizer is epoxy soybean oil; the stabilizer is alkyl ester antioxidant.

[0046] The preparation method of the polypropylene transparent material for fused deposition molding in this embodiment is the same as that in Embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a polypropylene transparent material for melting, depositing and forming and a preparation method thereof. The material is prepared from the following materials: 70-99 parts of polypropylene, 0.1-1 part of clarifier, 1-2 parts of compatilizer, 0.1-5 parts of plasticizer, and 0.01-0.5 parts of stabilizer. After the clarifier is added, the phenomenon of large-area crystallizing during the cold molding of polypropylene is inhibited, the light transmission of the polypropylene material is greatly improved, a polypropylene product obtained by melting, depositing and molding has better tenacity, enhanced mechanical properties, higher practicability and greatly reduced material cost, and the application of the polypropylene material in the melting, depositing and molding field is favorably widened. The preparation method of the polypropylene transparent material is easy to operate, has lower requirement on process conditions and production equipment, can realize large-scale promotion and production, and has broad market prospect and excellent market benefits.

Description

technical field [0001] The invention belongs to the fields of 3D printing technology and plastic processing, and in particular relates to a polypropylene transparent material for fused deposition molding and a preparation method thereof. Background technique [0002] 3D printing technology, also known as additive manufacturing technology, is a technology that uses bondable materials such as powdered metal or plastic to construct objects by layer-by-layer printing based on digital model files. 3D printing technology has been applied in many fields such as information technology, material science, and precision machinery, and it is becoming more and more competitive in today's manufacturing industry, so it is called "manufacturing technology with industrial revolution significance". 3D printing technology breaks through the traditional material deformation molding and removal molding process, and can quickly manufacture three-dimensional solid parts of any complex shape withou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08L23/14C08L51/06C08L91/00C08K5/20C08K5/053B29C47/00
CPCC08L23/12B29C48/022C08L23/14C08L2201/10C08L2203/14C08L2205/03C08L2205/035C08L2205/24C08L51/06C08K5/20C08L91/00C08K5/12C08K5/053
Inventor 于翔王延伟王娜徐茜丁宁
Owner HENAN INST OF ENG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products