Method for improving calotropis gigantea fiber elastic modulus

A technology of croissant melon fiber and elastic modulus, which is applied in fiber processing, plant fiber, textiles and papermaking, etc. It can solve the problems of unfavorable fiber spinning and high rigidity of croissant melon fiber, and achieve the increase of elastic modulus and elongation at break The effect of rate increase and simple operation

Inactive Publication Date: 2016-02-17
DONGHUA UNIV
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The horn melon fiber is a natural plant fiber grown from the horn melon seeds. Its basic component is composed of cellulose. The longitudinal surface of the fiber is smooth without distortion, and the hollowness of...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The croissant melon fiber is pre-washed with anionic and nonionic surfactants at a temperature of 90°C for 60 minutes and a pH value of 9-10, then washed with water and dried. Immerse the pretreated croissant melon fiber in a polyurethane solution with a concentration of 10%, immerse it at room temperature for 5 minutes, and the bath ratio is 1:40, and finally use a centrifuge to remove excess treatment solution, and dry it in an oven at 70°C Dry. The processed croissant melon fiber increases in weight by 8.5%, the elongation at break increases by 3%, and the modulus of elasticity increases by 4%.

Embodiment 2

[0025] The croissant melon fiber is pre-washed with anionic and nonionic surfactants at a temperature of 90°C for 60 minutes and a pH value of 9-10, then washed with water and dried. Immerse the pretreated croissant melon fibers in a 3% polyvinyl alcohol solution for 5 minutes at room temperature with a bath ratio of 1:50. Finally, use a centrifuge to remove excess treatment solution and dry it. The processed croissant melon fiber increases in weight by 3.5%, the elongation at break increases by 2.5%, and the modulus of elasticity increases by 3%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A related method for improving calotropis gigantea fiber elastic modulus comprises performing washing pretreatment on calotropis gigantea fiber; dipping the pretreated calotropis gigantea fiber into a processing agent solution; and taking out calotropis gigantea fiber dipped in the processing agent solution, centrifuging and drying. The method is simple to operate, the processed calotropis gigantea fiber is increased in both breaking elongation and elastic modulus, and the method possesses certain meaning for alleviating the situation that cotton and other natural fiber resource is limited and exploiting a new ecological environment-friendly fiber material.

Description

technical field [0001] The invention belongs to the field of finishing fiber of horned melon, and in particular relates to a method for improving the elastic modulus of the fiber of horned melon. Background technique [0002] Croissant melon is one of the plants with potential utilization discovered in recent years. It is distributed in tropical and subtropical regions of Asia and Africa. It will become another new green natural plant fiber with extensive planting and application significance after cotton fiber. , The resulting industry has broad development potential and space. The horn melon fiber is a natural plant fiber grown from the horn melon seeds. Its basic component is composed of cellulose. The longitudinal surface of the fiber is smooth without distortion, and the hollowness of the cross section is as high as 80%-90%. It is an urgent development and The natural fiber is used, but the croissant melon fiber has high rigidity and no natural curl, which is unfavorab...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M15/564D06M15/333D06M101/06
CPCD06M15/333D06M15/564D06M2101/06
Inventor 赵涛罗江玲
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products