Epoxy resin curing material system for high-temperature mixed epoxy asphalt and preparation method thereof

A technology of epoxy resin curing and epoxy asphalt, which is applied in the direction of building insulation materials, building components, buildings, etc., can solve the problems of high cost, long retention time, poor toughness, etc., and achieve high strength, good toughness, and high strength. Effect

Active Publication Date: 2016-03-23
CHANGAN UNIV
View PDF15 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The defects of low mixing temperature and extremely tight retention time of this kind of warm-mixed epoxy asphalt make it difficult to construct, poor paving compaction, poor stability, etc. The service performance of the bridge is degraded or even seriously damaged, which seriously affects the normal use of the bridge.
The mixing temperature of TAF epoxy asphalt produced by Dayou Construction Company in Japan is about 160-170°C, and the retention time is long, which solves this technological problem better, but its compatibility is poor, toughness is poor, and the cost is too high. High, which is the key factor limiting its mass application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Epoxy resin curing material system for high-temperature mixed epoxy asphalt and preparation method thereof
  • Epoxy resin curing material system for high-temperature mixed epoxy asphalt and preparation method thereof
  • Epoxy resin curing material system for high-temperature mixed epoxy asphalt and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] This example provides a kind of epoxy resin curing material system for high temperature mixing epoxy asphalt, including resin component and curing component; wherein the mass ratio of resin component and curing component is 100:80;

[0028] The resin component is composed of the following materials in parts by mass: 90 parts of hydroquinone diglycidyl ether resin, 10 parts of epoxidized soybean oil;

[0029] The curing component is composed of the following materials in parts by mass: 60 parts of cyanoethylated dodecanediamine, 10 parts of styrene-butadiene-styrene terpolymer, 30 parts of dodecyl alcohol .

[0030] The preparation method of the epoxy resin cured material system for the high temperature mixed epoxy asphalt of the present embodiment is as follows:

[0031] 1) First, mix the epoxy resin and diluent at a mass ratio of 90:10 at 60°C to obtain the resin component;

[0032] 2) Next, take 60 parts by mass of curing agent, 10 parts of toughening agent and 30 p...

Embodiment 2

[0039] This example provides a kind of epoxy resin curing material system for high temperature mixing epoxy asphalt, including resin component and curing component; wherein the mass ratio of resin component and curing component is 100:65;

[0040] The described resin component consists of the following materials in parts by mass: 88 parts of epoxidized polybutadiene resin, 12 parts of epoxidized linseed oil;

[0041] The curing component is expressed in parts by mass, consisting of 70 parts of cyanoethylated isophorone diamine, 20 parts of styrene-isoprene-styrene terpolymer, 10 parts of stearyl alcohol share.

[0042] The preparation method of the epoxy resin cured material system for the high temperature mixed epoxy asphalt of the present embodiment is as follows:

[0043] 1) First, mix the epoxy resin and the diluent at a mass ratio of 88:12 at 60°C to obtain the resin component;

[0044] 2) Secondly, take 70 parts by mass of curing agent, 20 parts of toughening agent and...

Embodiment 3

[0048]This example provides an epoxy resin cured material system for high temperature mixed epoxy asphalt, including a resin component and a cured component; wherein the mass ratio of the resin component to the cured component is 100:70;

[0049] The resin component is calculated in parts by mass and consists of the following materials: 80 parts of a mixture of hydroquinone diglycidyl ether resin and epoxidized polybutadiene resin, linoleic acid dimer diglycidyl ether 20 copies;

[0050] The curing component is composed of the following materials in parts by mass: 80 parts of cyanoethylated menthane diamine, 10 parts of EPDM rubber, and 10 parts of dodecylpropylene diamine.

[0051] The preparation method of the epoxy resin cured material system for the high temperature mixed epoxy asphalt of the present embodiment is as follows:

[0052] 1) First, mix the epoxy resin and the diluent at a mass ratio of 80:20 at 60°C to obtain the resin component;

[0053] 2) Next, take 80 pa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
tensile strengthaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention provides an epoxy resin curing material system for high-temperature mixed epoxy asphalt and a preparation method thereof. The preparation method comprises the following steps: firstly, mixing epoxy resin with a diluting agent to obtain a resin ingredient; secondly, uniformly mixing a curing agent, a toughening agent and a compatibilizer to obtain a curing ingredient; and finally, uniformly mixing the resin ingredient with the curing ingredient to obtain the epoxy resin curing material system. The epoxy resin curing material system and asphalt have a long holding time at a high temperature, and the viscosity of the epoxy resin curing material system and the asphalt can be maintained to be lower than 600mPa.s in 180 minutes at 170 DEG C; quick curing can be achieved under the condition of room temperature, and a curing degree of over 90 percent can be achieved in 1-2 days after the epoxy resin curing material system and asphalt are mixed; an epoxy asphalt material prepared by the epoxy resin curing material system has very high strength, and a casting body of the epoxy asphalt material at 23 DEG C has tensile strength of over 3MPa and elongation at break of over 300 percent, and has good toughness; and the concrete of the epoxy asphalt material has Marshall strength of over 70kN, and has high strength.

Description

technical field [0001] The invention belongs to the field of asphalt materials, and in particular relates to an epoxy resin curing material system for high-temperature mixed epoxy asphalt and a preparation method thereof. Background technique [0002] Epoxy asphalt has excellent high temperature stability, low temperature crack resistance, super fatigue resistance and excellent durability, and is widely used in steel bridge deck pavement, airport runway pavement, tunnel pavement pavement, etc. High traffic pavement. In 2001, epoxy asphalt was first applied on the Second Yangtze River Bridge in Nanjing, my country, and it still shows excellent application effect more than ten years later. But at present, the epoxy asphalt used in our country is mainly imported from American ChemCoSystem Company and Japan Dayou Construction Company, which is not only expensive (about 10 to 20 times that of ordinary asphalt), but also has a single product variety, which cannot be adjusted acco...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L63/00C08L95/00C08L53/02C08G59/50
Inventor 许培俊丛培良
Owner CHANGAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap