Manufacturing technique for bearing

A production process and bearing technology, which is applied in the field of bearing production process, can solve the problems of radial dimension, large vibration and noise, low fatigue resistance and poor anti-corrosion performance, and achieve reduced deformation, high fatigue resistance and corrosion resistance Good wear resistance

Active Publication Date: 2016-04-06
南阳防爆(苏州)特种装备有限公司
View PDF7 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, the rolling bearing has been standardized and serialized, but compared with the sliding bearing, its radial size, vibration and noise are larger, and the price is also higher.
The current bearings have the disadvantages of poor anti-corrosion performance and low fatigue strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A production process of a bearing, comprising the steps of:

[0032] (1) degreasing water washing

[0033] Put the steel pipe into the degreasing solution for immersion degreasing, the temperature of the degreasing is 40°C, the time of the immersion degreasing is 10 minutes, and then the degreasing and clean metal parts are washed with water, the composition material and proportion of the steel pipe are Al The content is 8%, the content of Fe is 1%, the content of Mn is 0.1% and the content of Ni is 0.4%;

[0034] (2) pickling

[0035] Put the degreased water-washed steel pipe into CH2Cl2, ultrasonically treat it for 1 hour, then put the steel pipe into 4% dilute sulfuric acid for ultrasonic treatment for 20 minutes, and then rinse it once with distilled water;

[0036] (3) Steel pipe cutting

[0037] Cut the steel pipe after pickling through a cutting machine as required, and the operating speed of the cutting machine is 20m / min;

[0038] (4) heat treatment

[003...

Embodiment 2

[0053] A production process of a bearing, comprising the steps of:

[0054] (1) degreasing water washing

[0055] Put the steel pipe into the degreasing solution for immersion degreasing, the temperature of the degreasing is 45°C, the time of the immersion degreasing is 15 minutes, and then the degreasing and clean metal parts are cleaned with water, the composition material and proportion of the steel pipe are Al content of 8.5%, Fe content of 1.5%, Mn content of 0.2% and Ni content of 0.5%;

[0056] (2) pickling

[0057] Put the degreased water-washed steel pipe into CH2Cl2, ultrasonically treat it for 1.5h, then put the steel pipe into 5% dilute sulfuric acid for ultrasonic treatment for 30min, and then rinse it twice with distilled water;

[0058] (3) Steel pipe cutting

[0059] Cut the steel pipe after pickling through a cutting machine as required, and the operating speed of the cutting machine is 25m / min;

[0060] (4) heat treatment

[0061] The cut steel pipe is s...

Embodiment 3

[0075] A production process of a bearing, comprising the steps of:

[0076] (1) degreasing water washing

[0077] Put the steel pipe into the degreasing solution for immersion degreasing, the temperature of the degreasing is 50°C, the time of the immersion degreasing is 20min, and then clean the degreased metal parts with water, the composition material and proportion of the steel pipe are Al The content is 9%, the content of Fe is 2%, the content of Mn is 0.3% and the content of Ni is 0.6%;

[0078] (2) pickling

[0079] Put the degreased water-washed steel pipe into CH2Cl2, ultrasonically treat it for 2 hours, then put the steel pipe into 6% dilute sulfuric acid for ultrasonic treatment for 40 minutes, and then rinse it with distilled water for 3 times;

[0080] (3) Steel pipe cutting

[0081] Cut the steel pipe after pickling through a cutting machine as required, and the operating speed of the cutting machine is 30m / min;

[0082] (4) heat treatment

[0083] The cut st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a manufacturing technique for a bearing. Through control over the normalizing and heat preservation time and temperature in heat treatment, deformation of a metal part can be reduced, energy consumption is saved, and the production cost is reduced; through control over the speed and the power of a grinding machine, the accuracy and the abrasion resistance of the bearing are further improved; through acid dipping after degreasing, on one hand, oxide on the surface of a steel pipe can be removed, as aftertreatment is carried out after surface grinding, the antiseptic property of the bearing can be improved, and the service life of the bearing is accordingly prolonged. The bearing produced with the method has the advantages of being high in fatigue resistance and long in service life; and the market potential is huge, and the prospect is wide.

Description

technical field [0001] The invention belongs to the production field of bearings, and more specifically, the invention relates to a production process of bearings. Background technique [0002] Bearings are an important part of contemporary mechanical equipment. Its main function is to support the mechanical rotating body, reduce the friction coefficient during its movement, and ensure its rotation accuracy. According to the different friction properties of moving elements, bearings can be divided into two categories: rolling bearings and sliding bearings. Among them, the rolling bearing has been standardized and serialized, but compared with the sliding bearing, its radial dimension, vibration and noise are larger, and the price is also higher. The current bearings have the disadvantages of poor anti-corrosion performance and low fatigue resistance. Contents of the invention [0003] The problem to be solved by the present invention is to provide a production process o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23P15/00
CPCB23P15/003
Inventor 郑臣钏
Owner 南阳防爆(苏州)特种装备有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap