Alkali-free glass fiber reinforcing modified polypropylene composite material and preparing method thereof

An alkali-free glass fiber and composite material technology, applied in the field of modified materials, can solve the problems of poor material fluidity, floating fibers on the surface, and low heat-resistant temperature, so as to improve processing fluidity, surface smoothness, and interface bonding Effect

Inactive Publication Date: 2016-04-20
ZHEJIANG PINNUO NEW MATERIALS
View PDF4 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In ordinary glass fiber-reinforced modified polypropylene (PP) materials, due to the material polarity compatibility between PP materials and alkali-free glass fibers, surface floating fibers, poor material fluidity, and product Phenomena such as partial warping

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Alkali-free glass fiber reinforcing modified polypropylene composite material and preparing method thereof
  • Alkali-free glass fiber reinforcing modified polypropylene composite material and preparing method thereof
  • Alkali-free glass fiber reinforcing modified polypropylene composite material and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0036] The preparation method of the described alkali-free glass fiber reinforced modified polypropylene composite material is mainly characterized in that the preparation method comprises the following steps:

[0037] Step (1): Put homopolymerized PP resin, alkali-free glass fiber, talcum powder, compatibilizer, antioxidant, anti-floating fiber agent and lubricant into a high-speed mixer and mix for 2 to 5 minutes before discharging.

[0038] Step (2): Put the material discharged in step (1) into the main feed inlet of the twin-screw extruder at a temperature of 180-220°C and a screw speed of 350-400 RPM, and undergo melt-extruded alkali-free glass fiber reinforcement modification Polypropylene composite.

[0039] Obtain following embodiment according to above-mentioned raw material:

Embodiment 1

[0041] Adopt the raw material of following weight portion proportioning:

[0042]

[0043] Put the homopolymerized PP resin, compatibilizer, antioxidant, anti-floating fiber agent, and lubricant into the high mixer according to the above mass parts and mix them for 2 to 5 minutes, then the mixed materials are passed through the twin-screw extruder Put the main feed port of the extruder into the extruder, add the alkali-free glass fiber, and finally form the PP composition through melt extrusion and granulation. 350~400RPM.

Embodiment 2

[0045] Adopt the raw material of following weight portion proportioning:

[0046]

[0047]

[0048] Put the homopolymerized PP resin, 3000 mesh superfine talc powder, compatibilizer, antioxidant, anti-floating fiber agent, and lubricant into the high mixer according to the above mass parts and mix for 2 to 5 minutes, then mix the mixed The material is put into the extruder from the main feed port of the twin-screw extruder, added with alkali-free glass fiber, and finally melted and extruded to form PP composition. The temperature during the whole granulation process should be controlled at 180~ 220°C, the screw speed is controlled at 350-400RPM.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an alkali-free glass fiber reinforcing modified polypropylene composite material and a preparing method thereof. The alkali-free glass fiber reinforcing modified polypropylene composite material comprises, by mass, 45-55 parts of homopolymerized PP resin, 28-32 parts of alkali-free glass fibers, 13-17 parts of talcum powder, 4-6 parts of compatilizer, 0.5-2 parts of antioxidant, 0.5-2 parts of anti-fiber-floating agent and 0.5-2 parts of lubricating agent. The alkali-free glass fiber reinforcing modified polypropylene composite material has the advantages that the superfine talcum powder is added into a PP glass fiber reinforcement material for replacement, the talcum powder with the length-diameter ratio smaller than that of the glass fibers is used, the large-particle lubricating dispersion effect can be achieved in the mixture of the formula, the alkali-free glass fibers with the large length-diameter ratio can be better and evenly dispersed in the material accordingly, the surface bright-clean performance and the processing fluidity of a nylon composition can be effectively improved, and therefore a product with the bright and clean surface can be better processed.

Description

technical field [0001] The invention relates to the field of modified materials, in particular to the field of modified polypropylene materials, in particular to an alkali-free glass fiber reinforced modified polypropylene composite material and a preparation method thereof. Background technique [0002] In ordinary glass fiber-reinforced modified polypropylene (PP) materials, due to the material polarity compatibility between PP materials and alkali-free glass fibers, surface floating fibers, poor material fluidity, and product Partial warping and deformation. Compared with glass fiber-reinforced modified polypropylene composites, mineral-filled modified polypropylene composites have fine and smooth surfaces and good fluidity, but have problems such as large product shrinkage and low heat-resistant temperature. [0003] In the application of electronic appliances, automobiles, home appliances and household appliances, it is often required that the applied materials have go...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08L51/06C08K13/04C08K7/14C08K5/134C08K5/526C08K5/20
CPCC08L23/12C08L2201/08C08L51/06C08K13/04C08K7/14C08K5/1345C08K5/526C08K5/20C08K3/34
Inventor 林杰林继炎
Owner ZHEJIANG PINNUO NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap