High-arc resistance epoxy insulating material and preparation method thereof and insulator

A technology of epoxy insulation and arc resistance, which is applied in the direction of organic insulators, inorganic insulators, plastic/resin/wax insulators, etc., can solve the problems of easy flashover, arc resistance performance and low voltage operation times, and achieve improvement The number of hot-pressed operations, excellent electric strength and arc resistance, and the effect of excellent electric strength

Active Publication Date: 2016-04-20
PINGGAO GRP +2
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a high-arc-resistant epoxy insulating material, so as to solve the problems in the prior art that the arc-resistant performance of the epoxy casting insulating parts inside the circuit breaker and the number of times of voltage operation are low, and flashover is prone to occur

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The high arc-resistant epoxy insulating material of the present embodiment is made of the following raw materials in parts by mass: 1 part of composite epoxy resin, 0.51 part of curing agent methyltetrahydrophthalic anhydride, and 3.25 parts of aluminum oxide; the composite epoxy resin is HE -A mixture of 4776 type bisphenol A epoxy resin, ER104 type bisphenol A epoxy resin, and CT200M type bisphenol A epoxy resin in a mass ratio of 3.5:3.5:1.5; aluminum oxide is 10-18 μm electrician α-Al 2 o 3 (A-F-3 type) and 200~400nm electrician α-Al 2 o 3 (XC-3 type) A mixture composed of a mass ratio of 1.6:1.

[0034] The preparation method of the high arc resistance epoxy insulation coating of the present embodiment may further comprise the steps:

[0035] 1) Preheat the composite epoxy resin at 135°C for 0.5h, preheat the mold at 135°C for 1.5h, and preheat the curing agent at a vacuum of 2mbar and 70°C for 0.5h; after preheating, put the composite epoxy resin Mix with alum...

Embodiment 2

[0040] The high arc-resistant epoxy insulating material of this embodiment is made of the following raw materials by mass: 1 part of composite epoxy resin, 0.53 parts of curing agent methyltetrahydrophthalic anhydride, and 3.35 parts of aluminum oxide; the composite epoxy resin is HE -A mixture of 4776 type bisphenol A epoxy resin, ER104 type bisphenol A epoxy resin, and CT200M type bisphenol A epoxy resin in a mass ratio of 4:4:1.8; aluminum oxide is 10-18 μm electrical engineering α-Al 2 o 3 (A-F-3 type) and 200~400nm electrician α-Al 2 o 3 (XC-3 type) A mixture composed of a mass ratio of 1.8:1.

[0041] The preparation method of the high arc resistance epoxy insulation coating of the present embodiment may further comprise the steps:

[0042] 1) Preheat the composite epoxy resin at 145°C for 1.5h, preheat the mold at 145°C for 2.5h, and preheat the curing agent at a vacuum of 5mbar and 80°C for 0.5h; after preheating, put the composite epoxy resin Mix with alumina at 1...

Embodiment 3

[0047] The high arc-resistant epoxy insulating material of this embodiment is made of the following raw materials by mass: 1 part of composite epoxy resin, 0.55 parts of curing agent methyltetrahydrophthalic anhydride, 3.45 parts of aluminum oxide; the composite epoxy resin is HE -A mixture of 4776 type bisphenol A epoxy resin, ER104 type bisphenol A epoxy resin, and CT200M type bisphenol A epoxy resin in a mass ratio of 4.5:5:2; alumina is 10-18 μm electrician α-Al 2 o 3 (A-F-3 type) and 200~400nm electrician α-Al 2 o 3 (XC-3 type) A mixture composed of a mass ratio of 2:1.

[0048] The preparation method of the high arc resistance epoxy insulation coating of the present embodiment may further comprise the steps:

[0049] 1) Preheat the composite epoxy resin at 140°C for 1 hour, preheat the mold at 140°C for 2 hours, and preheat the curing agent at a vacuum of 3mbar and 75°C for 0.5h; Aluminum is mixed at 145°C for 0.5h, after mixing, it is degassed at 145°C for 2h at a v...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
epoxy valueaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-arc resistance epoxy insulating material and a preparation method thereof and an insulator. The epoxy insulating material is prepared from the following raw materials in parts by mass: 1 part of composite epoxy resin, 0.51-0.55 part of curing agent methyl tetrahydrophthalic anhydride and 3.25-3.45 parts of aluminum oxide, wherein the composite epoxy resin is a mixture of phenolic aldehyde modified bisphenol A epoxy resin, polyethylene glycol modified bisphenol A epoxy resin and diphenolic acid modified bisphenol A epoxy resin. The epoxy insulating material is equivalent to traditional materials in glass-transition temperature, tensile strength and electric strength, the arc resistance reaches 237s, and after a 252kV circuit breaker is switched on / off under voltage for over 3243 times, flashover appears behind; and the epoxy insulating material has excellent arc resistance, the operation times of a high-voltage circuit breaker under voltage is remarkably increased, the service lives of internal epoxy insulating components are prolonged and reliability of the internal epoxy insulating components is improved, and the maintenance and overhauling cost of a power station is reduced.

Description

technical field [0001] The invention belongs to the technical field of electrical insulating materials, and in particular relates to a high-arc-resistant epoxy insulating material, a preparation method thereof, and an insulator. Background technique [0002] Epoxy cast insulating parts in AC high-voltage circuit breakers are generally used outside the arc extinguishing chamber and inside the circuit breaker. They are generally used as isolation parts between the arc extinguishing chamber and the two ends of the circuit breaker cylinder, and mainly play an important role in insulation and support. During the breaking process of the arc extinguishing chamber of the circuit breaker, a small amount of arc overflows to the area outside the arc extinguishing chamber and inside the circuit breaker, resulting in the rapid decline of the insulation performance of the epoxy cast parts exposed to the overflow arc for a long time after repeated breaking, and then Plus SF 6 Due to the c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L63/00C08K3/22H01B3/40H01B3/10
CPCC08K2201/003C08K2201/011C08L63/00C08L2205/02H01B3/10H01B3/40C08K2003/2227
Inventor 田浩李继承袁端鹏林生军吴明清杨保利侯亚峰
Owner PINGGAO GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com