Composite scale and corrosion inhibitor, and applications thereof in circulated cooling water treatment

A technology of scale and corrosion inhibitors and corrosion inhibitors, which can be used in complex/solubilizer treatment, water/sludge/sewage treatment, scale removal and water softening, etc. and other problems, achieve good scale and corrosion inhibition performance, meet the requirements of scale and corrosion inhibition, and avoid environmental problems

Active Publication Date: 2016-06-01
CHINA PETROLEUM & CHEM CORP +1
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] There is no research on the corrosion inhibition performance of carboxymethyl inulin and the research on the application of carboxymethyl inulin in the treatment of circulating cooling water to form a composite corrosion and scale inhibitor compounded with other water treatment agents in the existing literature

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite scale and corrosion inhibitor, and applications thereof in circulated cooling water treatment

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Weigh 30.0g carboxymethyl inulin (substitution degree is 1.0), 12.0g sodium tungstate and 30.0g acrylic acid / acrylamide / 2-methyl-2'-acrylamidopropanesulfonic acid copolymer (purchased from Luoyang Qianglong Industrial Co., Ltd.’s brand name is ZF322, the active substance content is 30% by weight, and the limiting viscosity number is 0.078dl / g at 30°C), add 28.0g of water, shake well, and obtain the composite scale and corrosion inhibitor stock solution S1 .

[0042] Take 1g of the prepared composite scale and corrosion inhibitor stock solution S1 and add it to 10L of test water 2 or 10L of test water 3, so that carboxymethyl inulin, sodium tungstate and acrylic acid / acrylamide / 2-methyl-2' - The effective concentrations of the acrylamido propane sulfonic acid copolymer were 6mg / L, 12mg / L and 9mg / L respectively, and then the calcium carbonate scale inhibition performance and corrosion inhibition performance were measured according to the method in the test example.

[00...

Embodiment 2

[0045] Take by weighing 3.14g zinc chloride, be dissolved in 23.3g acrylic acid / hydroxypropyl acrylate / methyl acrylate copolymer (purchased from Luoyang Qianglong Industrial Co., Ltd. The trade mark is the commodity of T-225, and active material content is 30% by weight, 30 ℃, the limiting viscosity number is 0.074dl / g), then add 15.0g of carboxymethyl inulin raw material (substitution degree is 0.6) and 18.0g of sodium molybdate, then add 20.56g of water, shake well to get composite scale inhibitor Etch agent stock solution S2.

[0046] Take 0.8g of the prepared composite scale and corrosion inhibitor stock solution S2 and add it to 10L of test water 2 or 10L of test water 3 to make carboxymethyl inulin, sodium molybdate, acrylic acid / hydroxypropyl acrylate / methyl acrylate copolymerized The effective concentrations of ions and zinc ions were 3mg / L, 18mg / L, 7mg / L and 1.5mg / L respectively, and then the calcium carbonate scale inhibition performance was measured according to the...

Embodiment 3

[0049] Weigh 1g of benzotriazole, dissolve it in 20g of acrylic acid / hydroxypropyl acrylate copolymer (purchased from Luoyang Qianglong Industrial Co., Ltd., the trade mark is T-225, the active substance content is 30% by weight, at 30°C The limiting viscosity is 0.079dl / g), then add 80.0g carboxymethyl inulin (substitution degree is 0.8) and 16.0g sodium silicate, then add 3g water, shake well, and get the stock solution of compound scale and corrosion inhibitor S3.

[0050] Take 1.2g of the prepared composite scale and corrosion inhibitor stock solution S3 and add it to 10L of test water 2 or 10L of test water 3, so that carboxymethyl inulin, sodium silicate, acrylic acid / hydroxypropyl acrylate copolymer and benzo The effective concentrations of triazole were 16mg / L, 16mg / L, 6mg / L and 1mg / L respectively, and then the calcium carbonate scale inhibition performance and corrosion inhibition performance were measured according to the method in the test example.

[0051] Use sul...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Ultimate viscosityaaaaaaaaaa
Ultimate viscosityaaaaaaaaaa
Ultimate viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a composite scale and corrosion inhibitor. The composite scale and corrosion inhibitor contains carboxymethylinulin, a soluble inorganic salt corrosion inhibitor, and a carboxylic acid-containing polymer scale inhibitor dispersing agent at a weight ratio of (12-100):(2-25):(10-50). The invention also discloses applications of the composite scale and corrosion inhibitor in circulated cooling water treatment. The composite scale and corrosion inhibitor possesses excellent corrosion and scale inhibition comprehensive performance; and when the composite scale and corrosion inhibitor is applied to circulated cooling water treatment, requirements of circulated cooling water on scale and corrosion inhibition are satisfied, and environmental problems caused by phosphorus-containing chemicals in phosphorus-containing circulated cooling water are avoided.

Description

technical field [0001] The invention relates to the fields of scale and corrosion inhibition and circulating water treatment, in particular to a composite scale and corrosion inhibitor and its application in circulating cooling water treatment. Background technique [0002] In the circulating cooling water system, there are mainly scaling and corrosion problems. In order to prevent system scaling and corrosion, the most convenient and effective method is to add corrosion and scale inhibitors to the circulating cooling water. However, during the use of cooling water, with the continuous circulation and concentration, the mineral content in the water will continue to increase, which will intensify the corrosion and scaling of pipes and equipment. Therefore, it is necessary to add corrosion and scale inhibitors to improve the quality of cooling water and ensure The equipment operates safely. These chemicals will eventually be released into the environment as waste. However, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C02F5/08C02F5/10
Inventor 秦会敏郦和生李博伟张化冰杨玉谢文州楼琼慧
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com