Wood-plastic type engineering plastic composition

A technology of engineering plastics and compositions, which is applied in the field of modified plastics and plastics, can solve the problems of poor elastic modulus and poor durability, and achieve good elastic modulus, long time and good compression resistance

Inactive Publication Date: 2016-06-08
SUZHOU NEW DISTRICT HUASHIDA ENG PLASTICS
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing wood-plastic composite materials have poor elastic modulus and poor durability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] A wood-plastic engineering plastic composition is provided, which includes polyvinyl chloride, wood powder, acrylic polymer ACR-401, plasticizer, anti-aging additive and titanium dioxide, the wood-plastic The engineering plastic composition is calculated in parts by weight, and includes the following components: 105 parts of polyvinyl chloride, 55 parts of wood flour, 14 parts of acrylic polymer copolymer ACR-4014, 7 parts of plasticizer, and 2 parts of anti-aging additives , 6 parts of titanium dioxide. The plasticizer is dioctyl sebacate. The anti-aging additive is 2-hydroxyl-4-n-octyloxybenzophenone, and the 2-hydroxyl-4-n-octyloxybenzophenone can absorb ultraviolet light of 240-340nm.

Embodiment 2

[0013] A wood-plastic engineering plastic composition is provided, which includes polyvinyl chloride, wood powder, acrylic polymer ACR-401, plasticizer, anti-aging additive and titanium dioxide, the wood-plastic The engineering plastic composition is calculated in parts by weight, and includes the following components: 100 parts of polyvinyl chloride, 60 parts of wood flour, 3 parts of acrylic polymer ACR-4013 parts, 9 parts of plasticizer, and 1 part of anti-aging additive , 7 parts of titanium dioxide. The plasticizer is dioctyl sebacate. The anti-aging additive is 2-hydroxyl-4-n-octyloxybenzophenone, and the 2-hydroxyl-4-n-octyloxybenzophenone can absorb ultraviolet light of 240-340nm.

Embodiment 3

[0015] A wood-plastic engineering plastic composition is provided, which includes polyvinyl chloride, wood powder, acrylic polymer ACR-401, plasticizer, anti-aging additive and titanium dioxide, the wood-plastic The engineering plastic composition is calculated in parts by weight, and includes the following components: 110 parts of polyvinyl chloride, 50 parts of wood flour, 15 parts of acrylic polymer ACR-4015 parts, 6 parts of plasticizer, and 3 parts of anti-aging additives , 5 parts of titanium dioxide. The plasticizer is dioctyl sebacate. The anti-aging additive is 2-hydroxyl-4-n-octyloxybenzophenone, and the 2-hydroxyl-4-n-octyloxybenzophenone can absorb ultraviolet light of 240-340nm.

[0016] The beneficial effects of the present invention are:

[0017] 1. The wood-plastic engineering plastic composition is used for a long time, and its properties will not change after a long time of use, so it does not need to be replaced;

[0018] 2. The wood-plastic engineering p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses wood-plastic type engineering plastic composition. The composition comprises components in parts by weight as follows: 100-110 parts of polyvinyl chloride, 50-60 parts of wood flour, 3-5 parts of an acrylate type macromolecular copolymer ACR-401, 6-9 parts of a plasticizer, 1-3 parts of an anti-ageing aid and 5-7 parts of titanium dioxide. Through the scheme, the wood-plastic type engineering plastic composition is long in service life, properties are not changed after long-term use, replacement is not required, the cost can be reduced, and the composition has the very good elasticity modulus and very good physical and mechanical properties such as compression resistance, bending resistance and the like.

Description

technical field [0001] The invention relates to the field of modified plastics, in particular to a wood-plastic engineering plastic composition. Background technique [0002] Wood-plastic, that is, wood-plastic composite material, is a new type of composite material that has been booming at home and abroad in recent years. It refers to the use of polyethylene, polypropylene and polyvinyl chloride, etc. Powder, rice husk, straw and other waste plant fibers are mixed into new wood materials, and then processed by extrusion, molding, injection molding and other plastic processing techniques to produce plates or profiles, which are mainly used in building materials, furniture, logistics packaging and other industries. Existing wood-plastic composite materials have poor elastic modulus and poor durability. Contents of the invention [0003] The technical problem mainly solved by the present invention is to provide a wood-plastic engineering plastic composition, which can be us...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L97/02C08L33/10C08K3/22C08K5/11C08K5/132
CPCC08L27/06C08L2205/03C08L97/02C08L33/10C08K2003/2237C08K5/11C08K5/132
Inventor 徐春华
Owner SUZHOU NEW DISTRICT HUASHIDA ENG PLASTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com