Preparation method of fluorescent sericite cosmetics

A technology of sericite and cosmetics, which is applied in the field of preparation of fluorescent sericite cosmetics, can solve the problems of less development and utilization, and achieve the effects of low cost, simple preparation method and consistent operation

Inactive Publication Date: 2016-06-08
ANHUI HENGHAO SCI & TECH
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

my country's sericite ore reserves are large and widely distributed, but few are worthy of development and utilization

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A kind of preparation method of fluorescent sericite cosmetic that the present invention proposes comprises the following steps:

[0019] S1, Pulping: select the mineral raw materials required for the preparation of sericite, manually select high-quality mineral raw materials, roughly peel the mineral raw materials, and then reprocess the sericite through wet stripping and grading processes. This obtains the sericite slurry;

[0020] S2, Metallurgy: The first wet method is superfine, put the sericite slurry into the mixer, and then add the aqueous solution of acidic medium or alkaline medium to the mixer for chemical treatment, or add organic solvents for extraction, separation of impurities, extraction Metals and their compounds, and keep the temperature at 20 ° C, fully stirred for 1 hour, so that the sericite slurry is classified twice to obtain high-purity sericite, and then the high-purity sericite is subjected to the second wet method ultrafine After three classi...

Embodiment 2

[0024] A kind of preparation method of fluorescent sericite cosmetic that the present invention proposes comprises the following steps:

[0025] S1, Pulping: select the mineral raw materials required for the preparation of sericite, manually select high-quality mineral raw materials, roughly peel the mineral raw materials, and then reprocess the sericite through wet stripping and grading processes. This obtains the sericite slurry;

[0026] S2, Metallurgy: The first wet method is superfine, put the sericite slurry into the mixer, and then add the aqueous solution of acidic medium or alkaline medium to the mixer for chemical treatment, or add organic solvents for extraction, separation of impurities, extraction Metals and their compounds, and keep the temperature at 25 ° C, fully stirred for 1.5 hours, so that the sericite slurry is classified twice to obtain high-purity sericite, and then the high-purity sericite is subjected to secondary wet ultrafine processing After the th...

Embodiment 3

[0030] A kind of preparation method of fluorescent sericite cosmetic that the present invention proposes comprises the following steps:

[0031] S1, Pulping: select the mineral raw materials required for the preparation of sericite, manually select high-quality mineral raw materials, roughly peel the mineral raw materials, and then reprocess the sericite through wet stripping and grading processes. This obtains the sericite slurry;

[0032] S2, Metallurgy: The first wet method is superfine, put the sericite slurry into the mixer, and then add the aqueous solution of acidic medium or alkaline medium to the mixer for chemical treatment, or add organic solvents for extraction, separation of impurities, extraction Metals and their compounds, and keep the temperature at 35 ° C, fully stirred for 2 hours, so that the sericite slurry is classified twice to obtain high-purity sericite, and then the high-purity sericite is subjected to the second wet superfine process After three clas...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of fluorescent sericite cosmetics. The method includes the following steps that S1, paste is prepared, wherein mineral raw materials needed for preparing sericite are selected, high-quality mineral raw materials are selected manually, rough stripping is performed on the mineral raw materials, sericite is re-processed through wet process stripping and classification technologies, and therefore the sericite paste is obtained; S2, metallurgy is performed, wherein wet untrafine grinding is performed for the first time, the sericite paste is placed in a stirrer, an aqueous solution of acid media or alkali media is added into the stirrer for chemical processing, or organic solvents are added for extraction, impurity separation, metal extraction and extraction of compounds of metal, temperature is kept at 20-40 DEG C, full stirring is performed for 1-2 h, secondary classification is performed on the sericite paste, and high-purity sericite is obtained. The preparation method is simple, not only are the purity and the glossiness of the prepared fluorescent sericite high, but also cost is low, and the fluorescent sericite is very practical.

Description

technical field [0001] The invention relates to the technical field of sericite powder, in particular to a preparation method of fluorescent sericite cosmetics. Background technique [0002] Sericite is a kind of mica, which belongs to silicate minerals with a layered structure. Sericite has a wide range of uses, such as rubber, plastics, coatings, paints, ceramics, thermal insulation, cosmetics, pigments, In papermaking, metallurgy and other industries, the appearance of sericite is translucent, rich in texture and silky luster. It has a unique high-diameter-thickness ratio structure and excellent ultraviolet shielding performance, especially the fine scale-like thin-layer structure has soft and smooth characteristics. . my country's sericite ore reserves are large and widely distributed, but few are worthy of development and utilization. According to the origin of the deposit, sericite deposits can be divided into: schist type (Chuzhou, Anhui), porphyry alteration type (...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09C1/42C09C3/06C09C3/04A61K8/26A61Q19/00
CPCA61K8/26A61K2800/10A61Q19/00C09C1/42C09C3/006C09C3/04C09C3/06
Inventor 万斌关洪勇陈静金瑞
Owner ANHUI HENGHAO SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More