High-strength oil-resistant storage battery case material and preparation method thereof

A battery and high-strength technology, applied in the field of polymer materials and lead-acid battery shell materials, can solve the problems of acid leakage, battery cracking, corrosion, etc., to improve the ability to resist organic solvent corrosion, strength, impact resistance, strength beautiful effect

Inactive Publication Date: 2016-06-15
山东同道电源科技股份有限公司
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the commonly used ABS resin is sensitive to engine oil, and the surface of the battery case is easily corroded after being stained with engine oil, and cracks under the action of internal stress.
In the environment where the battery is used, especially in the environment of the car, it is inevitable that it will be stained with engine oil, which will cause the battery to crack, fail, leak acid, and corrode other equipment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength oil-resistant storage battery case material and preparation method thereof
  • High-strength oil-resistant storage battery case material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Embodiment 1: Weigh 88 kilograms of ABS resin, 10 kilograms of polybutylene terephthalate PBT and 2 kilograms of methyl methacrylate-glycidyl methacrylate-ethyl acrylate terpolymer (MGE) in stainless steel Mix evenly on the mixer, then send it into the twin-screw extruder, and go through six-zone reaction molding. Set the temperature at 250°C, set the temperature in the fifth zone to 245°C, and set the temperature in the sixth zone to 240°C. The whole process lasts for 1 minute, the speed of the main machine is 280 rpm, and the pressure is 15MPa. After the material is discharged, it is cooled, dried, and pelletized . Among them, the ABS resin includes 30 kg of acrylonitrile, 20 kg of butadiene, and 38 kg of styrene.

Embodiment 2

[0016] Embodiment 2: Weigh 93 kilograms of ABS resin, 5 kilograms of polybutylene terephthalate PBT and 2 kilograms of styrene-maleic anhydride copolymer (SMA) and mix them uniformly on a stainless steel mixer, then send them into a twin-screw extruder Out of the machine, after six zones of reaction molding, the temperature of the first zone is set to 220°C, the temperature of the second zone is set to 230°C, the temperature of the third zone is set to 240°C, the temperature of the fourth zone is set to 240°C, and the temperature of the fifth zone is set The temperature of the six zones is set at 230°C, the temperature of the six zones is set at 240°C, the duration of the whole process is 1 minute, the speed of the main machine is 380 rpm, and the pressure is 16MPa. After the material is discharged, it is cooled, dried, and pelletized. Among them, the ABS resin includes 50 kg of acrylonitrile, 25 kg of butadiene, and 18 kg of styrene.

Embodiment 3

[0017] Embodiment 3: Weigh 90 kilograms of ABS resin, 4 kilograms of butylene terephthalate PBT and 6 kilograms of methyl methacrylate-glycidyl methacrylate-ethyl acrylate terpolymer (MGE) in stainless steel and mix Mix evenly on the machine, then send it into the twin-screw extruder, and undergo six-zone reaction molding. The temperature is set at 245°C, the temperature in the fifth zone is set at 245°C, and the temperature in the sixth zone is set at 240°C. The duration of the whole process is 2 minutes, the speed of the main machine is 280 rpm, and the pressure is 17MPa. After the material is discharged, it is cooled, dried, and pelletized. Among them, the ABS resin includes 45 kg of acrylonitrile, 20 kg of butadiene, and 25 kg of styrene.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a high-strength oil-resistant storage battery case material and a preparation method thereof. The technical scheme is as follows: the preparation method comprises the following steps: uniformly mixing 83-93 parts by weight of ABS (acrylonitrile-butadiene-styrene) resin, 4-10 parts by weight of polyester material and 2-8 parts by weight of compatilizer, sending into a double screw extruder, carrying out six-region reaction molding, cooling, drying and granulating to obtain the plastic alloy. The plastic alloy maintains the advantages of high impact resistance and beautiful appearance in the ABS resin, greatly enhances the organic solvent corrosion resistance, and is very suitable for lead-acid storage battery cases in organic oil and other organic solvent environments.

Description

Technical field: [0001] The invention relates to the technical field of polymer materials, in particular to the field of lead-acid storage battery shell materials. Background technique: [0002] After more than 150 years of development, lead-acid batteries have mature technology, low cost, and excellent performance. They are widely used in many economic fields such as transportation, communication, electric power, military, navigation, and aviation, and have become an indispensable and important chemical power source. As one of the three major parts of lead-acid batteries, the battery case is used to carry all the constituent materials such as the plate, separator, electrolyte, etc., and requires good acid and alkali resistance, high strength and good processability. ABS resin is the most commonly used raw material for battery cases, which is cheap, beautiful and strong. However, the commonly used ABS resin is sensitive to engine oil substances. The surface of the battery c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L67/02C08L33/12C08L35/06B29B9/06B29C47/92B29C48/92
CPCC08L55/02B29B9/06B29C48/92B29C2948/92514B29C2948/92561B29C2948/9258B29C2948/92704C08L2203/20C08L2205/03C08L2205/08C08L67/02C08L33/12C08L35/06
Inventor 蔡光义熊正林
Owner 山东同道电源科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More