Scratch-resistant waterborne UV curing coating and preparation method thereof

A curing coating, scratch-resistant technology, applied in the coating field, can solve the problems of poor water resistance, scratch resistance, low adhesion of water-based UV coatings, etc.

Active Publication Date: 2016-06-15
JIAXING UNIV
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, water-based UV coatings also have disadvantages such as low adhesion, scratch resistance, and poor water resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Scratch-resistant waterborne UV curing coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0016] Step 1: Add 82ml of ethanol and 13g of aluminum nitrate nonahydrate into a 250ml beaker at room temperature, stir magnetically until completely dissolved, then add 13ml of propylene oxide, seal with a plastic film, and stir for 5 minutes to form a viscous transparent sol, weight About 78g.

[0017] The second step: Put the sol obtained in the first step into the barrel, start stirring, and at a speed of 400-600r / min, add 4.5g of vinyltriethoxysilane, 25g of water, aliphatic water-based polyurethane acrylate (solid Content 95%) 85g, 2-hydroxy-4'-(2-hydroxyethoxy)-2-methylpropiophenone 5g, sebacic acid bis(1,2,2,6,6-pentamethylpiperidine Alcohol) ester 4.5 grams. Keep the rotation speed of 400-600r / min to disperse for 30min, and then use an emulsifier to disperse at 3000-4000r / min for 10min to obtain the coating. The whole process is protected from light.

[0018] Above-mentioned coating is coated on paper and leather surface (roller coating, coating amount 8-10g / m 2 )...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a scratch-resistant waterborne UV curing coating which is prepared from, by weight, 40-45 parts of aliphatic waterborne polyurethane acrylate, 2-2.5 parts of vinyltriethoxysilane, 38-40 parts of alumina sol, 2-3 parts of 2-hydroxy-4'-(2-hydroxyethoxy)-2-methylpropiophenone, 2-2.5 parts of bis(1,2,2,6,6-pentamethyl-4-piperidyl) sebacate and 10-15 parts of water. The water-soluble aliphatic polyurethane acrylate is used as the main material, the vinyltriethoxysilane is used as a modifying additive, and the water-soluble aliphatic polyurethane acrylate and the vinyltriethoxysilane are mixed with the alumina sol to prepare the organic-inorganic hybrid coating. The surface of paper or leather is coated with the coating, after UV curing, Si-O-Si and Si-O-Al bonds are formed in a coating film and formed between the coating film and a base material, and therefore the adhesive force of the coating film for the base material and the scratch resistance of the surface of the film are improved.

Description

technical field [0001] The invention belongs to the field of coatings, in particular to a scratch-resistant water-based UV curing coating and a preparation method thereof. Background technique [0002] UV curing coatings refer to a new type of coatings that can be rapidly cross-linked and cured to form a film under ultraviolet light irradiation. It has the advantages of no or low VOC emission, energy saving, fast curing rate, high production efficiency, suitable for assembly line production, low curing temperature, suitable for coating heat-sensitive or flammable substrates, etc. At present, UV curing coatings have been widely used in paper, leather, wood, metal, plastic and so on. [0003] The main component used in traditional oil-based UV-curable coatings, namely prepolymer, generally has a relatively high viscosity. Organic solvents, reactive diluents or reactive monomers must be added to adjust the viscosity and improve its rheology when coating. Most of these organic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D175/14C09D7/12
CPCC08K3/22C08K5/132C08K5/3435C08K2003/2227C09D7/61C09D7/63C09D175/14
Inventor 王玲汪蔚孟晨洁许汝南邵文君
Owner JIAXING UNIV
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com