Seamless hard wallpaper and preparation method thereof

A hard and wallpaper technology, applied in the direction of paper, papermaking, special paper, etc., can solve the problems of easy discoloration, resistance to scrubbing, easy moisture absorption and mildew, etc., and achieve excellent anti-discoloration effect

Inactive Publication Date: 2018-03-13
凌清明
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Wallpaper is a very common material in existing interior decoration. It is mainly set on the wall by glue and splicing. Although the quality of the existing wallpaper is relatively good, there are still shortcomings: easy to change color, not resistant to scrubbing , easy to absorb moisture and mildew
Due to the above-mentioned defects, the promotion of decoration in decoration has been greatly limited, and it has brought great industry obstacles for the wallpaper industry.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0012] The invention provides a method for preparing seamless hard wallpaper, comprising:

[0013] 1) mixing polyacrylic acid with a pigment, then printing on the surface of the base layer and drying to form a printing layer;

[0014] 2) mixing and foaming the hard resin, calcium carbonate, titanium dioxide, water, thickener and leveling agent, then transferring to the surface of the printing layer for curing and drying to form a process layer;

[0015] Wherein, the base layer is a non-woven fabric base layer, a cloth base layer or a paper base layer, and the hard resin is selected from polyacrylic acid and / or epoxy resin.

[0016] In step 1) of the present invention, the consumption of the raw material in the printing layer can be selected in a wide range, but in order to make the prepared wallpaper have more excellent anti-tarnish, scrub resistance, moisture-proof and anti-mildew properties; preferably Specifically, based on the total weight of the printing layer, the conte...

Embodiment 1

[0031] 1) Mix polyacrylic acid (weight-average molecular weight 1000) and pigments at a weight ratio of 92:8 at 25°C for 15 minutes, then print on the surface of the base layer (thickness 25 filaments, width 3m, non-woven fabric base layer) and Dry at 170°C for 1 min to form a printing layer (thickness is 3 filaments);

[0032] 2) Mix hard resin (weight average molecular weight 8000, polyacrylic acid), calcium carbonate, titanium dioxide, water, thickener (methyl cellulose) and leveling agent (silicone oil) according to 100:15:30:10: The weight ratio of 3:3 was mixed at 25°C for 0.8h, and foamed at 180°C for 0.8h, then transferred to the surface of the printing layer, cured at 130°C for 8min, and dried at 160°C for 8min to form a process layer (thickness: 35 silk) to make wallpaper A1.

Embodiment 2

[0034] 1) Mix polyacrylic acid (weight-average molecular weight 500) and pigments at a weight ratio of 90:10 at 15°C for 5 minutes, then print on the surface of the base layer (thickness: 20 filaments, width: 2m, cloth base layer) and place on Dry at 120°C for 0.5min to form a printing layer (thickness is 1 wire);

[0035] 2) Mix hard resin (weight average molecular weight 7000, epoxy resin), calcium carbonate, titanium dioxide, water, thickener (gelatin) and leveling agent (silicon urea-formaldehyde resin) according to 100:10:25:8: The weight ratio of 2.5:2.5 was mixed at 15°C for 0.5h, and foamed at 170°C for 0.5h, then transferred to the surface of the printing layer, cured at 120°C for 5min, and dried at 120°C for 5min to form a process layer (thickness: 25 silk) to make wallpaper A2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
Login to view more

Abstract

The invention discloses seamless hard wallpaper and a preparation method thereof. The preparation method comprises the following steps of (1) mixing polyacrylic acid and pigment agents, then printing on the surface of a base layer and drying to form a printing layer; (2) mixing hard resin, calcium carbonate, titanium dioxide, water, thickening agents and flatting agents, foaming, then transferring to the surface of the printing layer, curing and drying to form a process layer, wherein the base layer is a non-woven base layer, a cloth base layer or a paper base layer; the hard resin is selected from the polyacrylic acid and / or epoxy resin. The wallpaper prepared through the method has the characteristics of fastness, scrub resistance, dampproofness and mildew prevention.

Description

technical field [0001] The present invention relates to wallpaper, in particular to seamless rigid wallpaper and a preparation method thereof. Background technique [0002] Wallpaper is a very common material in existing interior decoration. It is mainly set on the wall by glue and splicing. Although the quality of the existing wallpaper is relatively good, there are still shortcomings: easy to change color, not resistant to scrubbing , easy to absorb moisture and mildew. Due to the above-mentioned defects, the promotion of decoration in decoration has been greatly limited, which has brought great industry obstacles for the wallpaper industry. Contents of the invention [0003] The object of the present invention is to provide a seamless hard wallpaper and its preparation method. The wallpaper prepared by the method has the characteristics of resistance to discoloration, scrubbing, moisture and mildew. [0004] In order to achieve the above object, the invention provides...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): E04F13/077D21H27/20D21H27/28D06M15/263D06M15/55D06M11/76D06M11/46
CPCD06M11/46D06M11/76D06M15/263D06M15/55D21H27/20D21H27/28E04F13/0866
Inventor 凌清明周玉斌吴中建莫秀斌
Owner 凌清明
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap