Ultrasonic vibration assisted welding method

An auxiliary welding and ultrasonic technology, applied in the direction of welding equipment, non-electric welding equipment, metal processing equipment, etc., can solve the problems such as difficult to completely eliminate welding hot cracks, reduce pores and slag defects, reduce residual stress, and uniform composition Effect

Active Publication Date: 2016-07-06
ACADEMY OF ARMORED FORCES ENG PLA
View PDF9 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the depth of the ultrasonic shock treatment layer is generally within 1.5mm, so for welds with large cross-sectional dimensions, it is difficult t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultrasonic vibration assisted welding method
  • Ultrasonic vibration assisted welding method
  • Ultrasonic vibration assisted welding method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0046] The technical solutions of the present invention will be clearly and completely described below in conjunction with the accompanying drawings. Apparently, the described embodiments are some of the embodiments of the present invention, but not all of them. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0047] In the description of the present invention, it should be noted that the terms "center", "upper", "lower", "left", "right", "vertical", "horizontal", "inner", "outer" etc. The indicated orientation or positional relationship is based on the orientation or positional relationship shown in the drawings, and is only for the convenience of describing the present invention and simplifying the description, rather than indicating or implying that the referred device or element must have a specific orientation, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of welding and in particular relates to an ultrasonic vibration assisted welding method. The method comprises the following steps: in a welding process of fusion welding, providing an ultrasonic vibration force through an ultrasonic excitation vibration device; introducing ultrasonic frequency stress wave into a welding fusion tank; finally, transmitting vibration to a welding part. With the adoption of the configuration, the quantity of crystal nucleuses can be effectively increased, the size of crystal grains is prevented from growing, dendritic crystals are crushed and a crystal shape is changed, so that condensed welding line metal crystal grains are thinned; gas, impurities and the like in the fusion tank are prompted to rapidly float up, and defects of air pores and slag adding are reduced; welding residual stress and welding deformation are reduced; components are more uniform so that a welding line metal structure is improved; a fusion region becomes narrow and is uniformly transited, and non-fusion defects are reduced; comprehensive mechanical properties of welding lines are improved through the effects above.

Description

technical field [0001] The invention relates to the field of welding, in particular to an ultrasonic vibration-assisted welding method. Background technique [0002] Welding is an important material joining process, widely used in petrochemical, aerospace, marine engineering, vehicles, ships, and various metal structures and other industrial sectors. Welding cracks (cold cracking, hot cracking), welding residual stress, weld defects and welding deformation are common problems in welding production. The existence of these problems will greatly affect the service performance of the welded connection structure. For this reason, a variety of technological methods for strengthening welded joints have been developed. For example, heat treatment, hammering, ultrasonic impact, rolling strengthening, etc., and have been applied in actual production. [0003] Among them, post-weld heat treatment is a process in which the metal weldment is heated to a certain temperature in a furnac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23K20/10
CPCB23K20/10
Inventor 朱有利刘开亮黄元林谢俊峰侯帅李占明许艺
Owner ACADEMY OF ARMORED FORCES ENG PLA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap