A low temperature resistant coating for porcelain and glass insulators

A glass insulator, anti-low temperature technology, applied in coatings and other directions, can solve the problems of high consumption of acid and alkali solutions, environmental pollution, and difficulty in reusing metal ions solutions.

Active Publication Date: 2018-03-13
PINGDINGSHAN POWER SUPPLY ELECTRIC POWER OF HENAN +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These methods need to consume a large amount of acid-base solution in the implementation process, and the solution in which the metal ions are dissolved is difficult to reuse, and the treatment of waste liquid will cause further environmental pollution.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A low-temperature resistant coating for porcelain and glass insulators, including Si0 disposed on the outer surface of the insulator 2 film layers and are provided on the Si0 2 The fluorine-containing organic film layer on the film layer is composed of C-Si0 2 Graphite film. The Si0 2 The film layer is made of Si0 2 film preparation solution, the Si0 2 The film layer preparation solution is made of Si0 2 Sol and Si0 2 Powder composition, Si0 2 Si0 in sol 2 The number of moles of Si0 2 Si0 in powder 2 The ratio of the moles is 3.15:1.

[0016] Among them, the Si0 2 The sol is an acidic silica sol, and its preparation method is: adding absolute ethanol and tetraethyl orthosilicate into a reaction vessel, then placing the reaction vessel in a cold water bath, stirring to mix the absolute ethanol and tetraethyl orthosilicate into a Homogeneous solution to obtain reaction solution A, then drop deionized water into reaction solution A to obtain reaction solution B...

Embodiment 2

[0025] A low-temperature resistant coating for porcelain and glass insulators, including Si0 disposed on the outer surface of the insulator 2 film layers and are provided on the Si0 2 The fluorine-containing organic film layer on the film layer is composed of C-Si0 2 Graphite film. The Si0 2 The film layer is made of Si0 2 film preparation solution, the Si0 2 The film layer preparation solution is made of Si0 2 Sol and Si0 2 Powder composition, Si0 2 Si0 in sol 2 The number of moles of Si0 2 Si0 in powder 2 The ratio of the number of moles is 3:1.

[0026] Among them, the Si0 2 The sol is an acidic silica sol, and its preparation method is: adding absolute ethanol and tetraethyl orthosilicate into a reaction vessel, then placing the reaction vessel in a cold water bath, stirring to mix the absolute ethanol and tetraethyl orthosilicate into a Homogeneous solution to obtain reaction solution A, then drop deionized water into reaction solution A to obtain reaction sol...

Embodiment 3

[0031] A low-temperature resistant coating for porcelain and glass insulators, including Si0 disposed on the outer surface of the insulator 2 film layers and are provided on the Si0 2 The fluorine-containing organic film layer on the film layer is composed of C-Si0 2 Graphite film. The Si0 2 The film layer is made of Si0 2 film preparation solution, the Si0 2 The film layer preparation solution is made of Si0 2 Sol and Si0 2 Powder composition, Si0 2 Si0 in sol 2 The number of moles of Si0 2 Si0 in powder 2 The molar ratio of 3.2:1.

[0032] Among them, the Si0 2 The sol is an acidic silica sol, and its preparation method is: adding absolute ethanol and tetraethyl orthosilicate into a reaction vessel, then placing the reaction vessel in a cold water bath, stirring to mix the absolute ethanol and tetraethyl orthosilicate into a homogeneous solution to obtain reaction solution A, then drop deionized water into reaction solution A to obtain reaction solution B, adjust...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a low-temperature-resistant coating of porcelain and a glass insulator. The low-temperature-resistant coating is composed of a Si02 membrane layer arranged on the outer surface of the insulator and a fluorine-containing organic matter membrane layer arranged on the Si02 membrane layer, and a C-Si02 graphite membrane layer is arranged outside the fluorine-containing organic matter membrane layer. The preparation method includes the following steps that the outer surface of an insulator body is coated with the Si02 membrane layer, and the membrane layer is coated with the fluorine-containing organic matter membrane layer and coated with a graphite and Si02 membrane layer; a two-layer structure is changed to be a three-layer structure, water drops at the temperature of 0 DEG C fall rapidly after knocking the surface of the coating, no water drop residues exist on the coating surface, the experiment process can continue for about 150 minutes, it is proved that the coating maintains a good hydrophobic property at a low temperature, freezing of freezing rain on the surface of the coating is effectively inhibited, and the coating has anti-frosting, freezing rain prevention and self-cleaning capacity.

Description

technical field [0001] The invention belongs to the technical field of insulator surface coatings, in particular to a low-temperature resistant coating for porcelain and glass insulators. Background technique [0002] my country is one of the most serious countries in the world where transmission lines suffer from icing disasters. In the cold winter, the heavy snow in the north and the sleet climate at 3-o°C in the central and southern regions can easily lead to the snow accumulation and freezing of the line hanging insulator strings, which will cause short-circuit tripping of the insulators and power outages. Since 1954, when there were records of ice disaster accidents on transmission lines, large-scale ice disaster accidents have occurred across the country one after another. [0003] The ice on the surface of the insulator will melt when the temperature rises. Due to the presence of conductive ions in the dirt on the ice layer, under the action of these conductive ions,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C17/34C04B41/89
CPCC03C17/38C03C2217/70C04B41/52C04B41/89C04B2111/2069C04B2111/27C04B2111/29C04B41/5035C04B41/4842C04B41/4933C04B41/522C04B41/5001
Inventor 张逸群王逸超郑福斌郭晓飞平林涛金会军张金光
Owner PINGDINGSHAN POWER SUPPLY ELECTRIC POWER OF HENAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com