A gear grease and self-repairing technology, which is applied in the field of gear grease and anti-pitting corrosion self-repairing gear grease, can solve the problems of not being able to effectively prevent pitting on the gear surface and weak anti-oxidation effect, and improve the anti-oxidation performance , prevent oxidation failure, good self-healing performance

Active Publication Date: 2016-07-06
东莞太平洋博高润滑油有限公司
View PDF15 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] 现有技术CN103254976A、CN104194889A、CN104312693A、CN104312677A、CN104164277A、CN104312697A、CN104830424A、CN103045334A、CN103602447A、CN104830496A、CN103805325A分别公开了一种齿轮润滑脂,上述现有的齿轮润滑脂虽然具有较好的极压抗磨性能 and anti-rust performance, but the anti-oxidation effect at high temperature is not strong, and there is no self-healing effect of the friction pair, it cannot effectively prevent pitting corrosion on the surface of the gear, and needs further improvement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-pitting self-repairing gear grease
  • Anti-pitting self-repairing gear grease
  • Anti-pitting self-repairing gear grease

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] The anti-pitting self-repairing gear grease of this embodiment contains a gear grease body and a self-repairing additive. Wherein the weight percentage of the gear lubricating grease body is 94%, and the weight percentage of the self-repairing additive is 6%. Its NLGI consistency grade is 00#.

[0058] The gear grease body of the present embodiment contains the following components in parts by weight:

[0059]

[0060] Wherein, the base oil is the mixture of 1-150BS and PB-2400, the total mass of the base oil is 100%, the mass fraction of 1-150BS is 66.1%, the mass fraction of PB-2400 is 33.9%; the thickener is Lithium soap; extreme pressure agent is sulfurized isobutylene T321; antirust agent is calcium dinonyl naphthalene sulfonate.

[0061] The self-healing additive of the present embodiment is made up of the following components by weight percentage:

[0062]

[0063] Among them, the antioxidant is a mixture of three antioxidants, based on the total mass of...

Embodiment 2

[0069] The anti-pitting self-repairing gear grease of this embodiment contains a gear grease body and a self-repairing additive. Wherein the mass fraction of the gear grease body and the self-repairing additive is the same as in Example 1. Its NLGI consistency grade is 0#.

[0070] Wherein, the gear grease body contains the following components in parts by weight:

[0071]

[0072] Wherein the kind and ratio of base oil, the kind of thickener, extreme pressure agent and antirust agent are the same as embodiment 1.

[0073] The self-healing additive of the present embodiment is made up of the following mass fraction components:

[0074]

[0075]

[0076] Among them, the specific substances of antioxidant, antiwear agent A, extreme pressure agent, organic zinc and organic molybdenum are the same as in Example 1; in addition, the preparation method of the self-repairing additive in this example refers to Example 1.

[0077] The self-repairing additive of this embodiment...

Embodiment 3

[0079] The anti-pitting self-repairing gear grease of this embodiment contains a gear grease body and a self-repairing additive. Wherein the mass fraction of the gear grease body and the self-repairing additive is the same as in Example 1. Its NLGI consistency grade is 1#.

[0080] Wherein, the gear oil body contains the following components in parts by weight:

[0081]

[0082] Wherein the kind and ratio of base oil, the kind of thickener, extreme pressure agent and antirust agent are the same as embodiment 1.

[0083] The self-healing additive of the present embodiment is made up of the following components by weight percentage:

[0084]

[0085]

[0086] Wherein, the organic molybdenum is oxymolybdenum dialkyldithiocarbamate; the specific substances of the antioxidant, antiwear agent A, extreme pressure agent and organic zinc are the same as in Example 1.

[0087] Refer to Example 1 for the preparation method of the self-healing additive in this embodiment.

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to view more

Abstract

The invention relates to anti-pitting self-repairing gear grease. The anti-pitting self-repairing gear grease comprises, by weight, 92-97% of a gear grease body and 3-8% of a self-repairing addition agent. According to calculation of the total mass of 100%, the self-repairing addition agent comprises, by weight, 50-70% of antioxidant, 10-25% of an anti-wear agent, 5-10% of an extreme pressure agent and 5-20% of organic molybdenum. The anti-pitting self-repairing gear grease has excellent antioxygen performance and extreme pressure wear resisting performance at different temperatures, can effectively prevent the surface of a gear from generating pitting, and can have a function of repairing the worn surface of the gear to a certain degree, so that the service life of the gear is prolonged.

Description

technical field [0001] The invention belongs to the technical field of fine chemicals, in particular to a gear lubricating grease, in particular to an anti-pitting self-repairing gear lubricating grease. Background technique [0002] Gear transmission is one of the most important and widely used transmission forms in modern machinery. In order to reduce the friction and wear during the working process of the gears and prolong the service life of the gears, lubricants are needed. Closed industrial gears generally use industrial gear oil, and open gears generally use gear grease. Asphalt lubricants were often used in the early open gear lubrication. With the improvement of equipment development requirements for lubrication, many new and high-performance gear greases have been developed and used in industrial production. [0003] The current mainstream gear grease is composed of thickener, base oil and various additives. Thickeners include non-soap-based thickeners such as b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C10M169/04C10N30/06C10N30/10C10N30/12C10N40/04
CPCC10M169/045C10M2207/026C10M2207/126C10M2207/281C10M2219/022C10M2219/024C10M2219/044C10M2223/041C10M2223/08C10M2227/06C10M2227/066C10N2030/06C10N2030/10C10N2030/12C10N2040/04C10N2010/02C10N2010/04
Inventor 曾志丁欧博明银敏黄伟聪潘露君
Owner 东莞太平洋博高润滑油有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap