Magnesium phosphate cement with good hydrolytic resistance and using method thereof

A magnesium phosphate cement, performance technology, applied in the field of building materials, can solve the problem of low overall utilization rate

Inactive Publication Date: 2016-07-27
TONGJI UNIV
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Many scholars in China have applied finely ground steel slag powder to building materials. There are three main ways to use steel slag powder in cement production: as a raw meal component mixed with fired

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Magnesium phosphate cement with good hydrolytic resistance and using method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042]Embodiment 1, a kind of magnesium phosphate cement with good water resistance performance, according to overburned magnesium oxide 100, potassium dihydrogen phosphate 31.8, coagulation regulator 2, desulfurization gypsum 6.0, fly ash 45, steel slag powder 20, limestone powder 0, reduce The water agent is 0.15, and the weight ratio of the defoamer is 0.10. According to the water-cement ratio of 0.30, add water and stir evenly before forming. The performance test results are shown in Table 1.

Embodiment 2

[0043] Embodiment 2, a kind of magnesium phosphate cement with good water resistance performance, according to overburned magnesium oxide 100, potassium dihydrogen phosphate 15.8, coagulation regulator 12, desulfurization gypsum 4.0, fly ash 20, steel slag powder 10, limestone powder 8.0, reduce The weight ratio of water agent 0.25 and defoamer 0.30 is prepared. According to the water-cement ratio of 0.30, add water and stir evenly before forming. The performance test results are shown in Table 1.

Embodiment 3

[0044] Embodiment 3, a kind of magnesium phosphate cement with good water resistance performance, according to overburned magnesium oxide 100, potassium dihydrogen phosphate 23.8, coagulation regulator 5, desulfurization gypsum 5.0, fly ash 30, steel slag powder 10.5, limestone powder 7.1, reduce The water agent is 0.22, and the weight ratio of the defoaming agent is 0.15. According to the water-cement ratio of 0.30, add water and stir evenly before forming. The performance test results are shown in Table 1.

[0045] Table 1 embodiment performance test result

[0046]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of building materials, and particularly relates to preparation of magnesium phosphate cement with good hydrolytic resistance and a using method thereof. The magnesium phosphate cement is prepared from calcined magnesia, monopotassium phosphate, retarder, desulphurization gypsum, coal ash, steel slag powder, limestone flour, a water reducing agent and a defoaming agent. The defects that traditional magnesium phosphate cement is insufficient in early strength, low in later strength, poor in water resistance, high in cost and the like can be overcome, and the additional value of the industrial byproducts such as the coal ash, the steel slag powder and the desulphurization gypsum can be improved. The magnesium phosphate cement with good hydrolytic resistance can be used as a rapid repair material, has the excellent properties that preparation technology is simple, fluidity is good, early strength development is fast, later strength is not reduced and permeability and erosion resistance is good, is applicable to rapid repair engineering of bridges, wharfs, municipal engineering and the like, and has good economic benefits and social benefits.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a magnesium phosphate cement with good water resistance and a using method thereof. Background technique [0002] Magnesium phosphate cement (MPC) is generally used in areas that are not in contact with water for a long time, but as a quick repair material for road surfaces, if it is in a humid or rainy area, it will inevitably have an adverse effect on its durability. limit its wide application. There have been many studies on the water resistance and modification of magnesium oxychloride cement at home and abroad, but there are relatively few studies on magnesium phosphate cement, which is also a magnesium cementitious material. Therefore, the present invention has certain practical significance for the research on the improvement of the water resistance of magnesium phosphate cement. [0003] Fly ash and steel slag are both solid wastes. If they are di...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B12/02C04B28/34
CPCC04B12/025C04B28/344
Inventor 孙振平张世杰水亮亮郭二飞蒋晓星唐晓博
Owner TONGJI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap