Environment-friendly building material formed by shell powder and preparation method

A building material and environment-friendly technology, applied in the field of building materials, can solve the problems of oil consumption, bacteria breeding, discoloration, etc., and achieve the effect of simple transportation and construction

Inactive Publication Date: 2016-07-27
韩泽龙
View PDF6 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Latex paints generally have disadvantages such as soft paint film, long drying time, and poor storage stability. After being damp, latex paints are prone to breed bacteria, cause shedding, discoloration, etc., which seriously affect the s

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] The present invention also provides a kind of preparation method of described building material, it comprises the following steps:

[0026] A. Fully mix the above-mentioned substances according to parts by weight, and fully stir to obtain a mixed powder for subsequent use;

[0027] B. According to the production process requirements of different products, take clear water with a weight of 0.5 to 1 times the weight of the mixed powder for use;

[0028] C. Add 80% of the weight of all clear water into the mixing container;

[0029] D. Add the mixed powder in step A into the mixing container, stir, and add the remaining clear water into the mixing container; after stirring, the building material paste slurry is obtained.

[0030] Furthermore, the stirring speed in step A and step D is 280-600 rpm, and the stirring time is 3-5 min.

Embodiment 1

[0033] The building materials include the following components in parts by weight: 50 parts of shell powder, 30 parts of diatomite, 15 parts of kaolin, 2 parts of nano-scale titanium dioxide, 10 parts of quartz powder, 6 parts of talcum powder, 15 parts of sepiolite powder, and 10 parts of bentonite powder 15 parts of fine vermiculite powder, 5 parts of paris plaster powder, 2 parts of negative ion powder, 10 parts of photocatalyst, 20 parts of heavy calcium powder, 30 parts of white carbon black, 15 parts of white cement, 10 parts of Shuangfei powder and 3 parts of cellulose . Stir the above components to disperse evenly, and pack to obtain a powder product. That is, the above-mentioned substances are fully mixed and stirred according to the weight part, and the mixed powder is obtained for use; according to the production process requirements of different products, clear water with a weight of 0.5 to 1 times the weight of the mixed powder is taken for use; add 80% of the tot...

Embodiment 2

[0035] The building materials include the following components in parts by weight: 40 parts of shell powder, 50 parts of diatomaceous earth, 12 parts of kaolin, 1 part of nano-scale titanium dioxide, 15 parts of quartz powder, 10 parts of talcum powder, sea 10 parts of foam stone powder, 15 parts of bentonite powder, 10 parts of fine vermiculite powder, 10 parts of paris plaster powder, 3 parts of negative ion powder, 15 parts of photocatalyst, 15 parts of heavy calcium powder, 20 parts of white carbon black, 10 parts of white cement, double fly 20 parts of powder and 6 parts of cellulose. Stir the above components to disperse evenly, and pack to obtain a powder product. That is, the above-mentioned substances are fully mixed and stirred according to the weight part, and the mixed powder is obtained for use; according to the production process requirements of different products, clear water with a weight of 0.5 to 1 times the weight of the mixed powder is taken for use; add 80...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an environment-friendly building material formed by shell powder and a preparation method. The building material comprises the following components by weight: 20 to 50 parts of the shell powder, 20 to 50 parts of diatomite, 10 to 20 parts of kaolin, 1 to 5 parts of nanoscale titanium dioxide, 5 to 20 parts of quartz powder, 5 to 10 parts of talcum powder, 1 to 5 parts of cellulose, 10 to 15 parts of sepiolite powder, 10 to 20 parts of bentonite powder, 10 to 15 parts of vermiculite fine powder, 5 to 10 parts of calcined gypsum powder, 1 to 5 parts of negative ion powder, 10 to 20 parts of a photocatalyst, 10 to 20 parts of ground calcium carbonate powder and 10 to 30 parts of white carbon black. The building material provided by the invention does not use any harmful matter, is insusceptible to emitting harmful gases like formaldehyde, benzene, ammonia gas and total volatile organic compounds (TVOC), has functions of adsorbing and decomposing the harmful gases and a certain breathing humidity-adjusting function, and can effectively kill a variety of bacteria.

Description

technical field [0001] The invention relates to building materials, in particular to an environmentally friendly building material made of shell powder and a preparation method. Background technique [0002] The architectural interior wall coatings used in the market are mainly latex paints. Latex paints generally have disadvantages such as soft paint film, long drying time, and poor storage stability. After the latex paint is damp, it is easy to breed bacteria, cause peeling, discoloration, etc., which seriously affects the service life and indoor appearance. At the same time, latex paints consume a lot of oil. Due to the lack of oil resources in my country, a large amount of imports is required, and the cost of raw materials increases year by year. The development of my country's social economy has increased the demand for coatings and raised people's requirements for the performance of coatings. In the interior decoration process, a large number of decoration materials ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/04C04B14/28
Inventor 韩泽龙
Owner 韩泽龙
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap