Chlorine fastness improver, and preparation method and application thereof

A booster and chlorine-resistant technology, which is applied in the field of textile dyeing and finishing, can solve the problems of fabric hand feeling and shade negative impact, fabric color change, and poor washability, etc., to improve chlorine color fastness, fabric color change, Good washing resistance

Active Publication Date: 2016-08-10
东莞市中纺化工有限公司 +1
View PDF7 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These methods are very effective in improving the color fastness to chlorine, but because most of the chlorine-resistant color-fixing agents used in these methods are water-soluble rigid polymers with aromatic rings, they have a negative impact on the feel and shade of the fabric. Problems such as fabric color change, hard hand feeling and poor washability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Chlorine fastness improver, and preparation method and application thereof
  • Chlorine fastness improver, and preparation method and application thereof
  • Chlorine fastness improver, and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] Embodiment 1, preparation and application of chlorine-resistant promotion agent

[0053] 1. Preparation

[0054] Add 2 parts of sodium dodecylbenzenesulfonate to 81 parts of deionized water, stir and dissolve, then add 15 parts of dodecyl dicarboxylic acid dihydrazide, stir evenly, then transfer to a sand mill, and use 600 Sanding at a speed of rev / min for 10 hours, then adding 2 parts of polyacrylate, stirring at a speed of 150 rev / min for 2 hours. After discharging, the chlorine-resistant enhancer is obtained.

[0055] The appearance of the chlorine-resistant enhancer prepared in this example is: a milky white dispersion, which consists of: 2% polyacrylate, 15% hydrazide derivatives, 2% dispersant, and 81% deionized water.

[0056] 2. Application

[0057] Continue dyeing and finishing the chlorine-resistant enhancer nylon and spandex swimsuit fabric prepared above, the steps are as follows:

[0058] (1) padding: the chlorine-resistant promoting agent prepared by t...

Embodiment 2

[0060] Embodiment 2, the preparation and application of chlorine resistance promoting agent

[0061] 1. Preparation

[0062] Mix 1 part of dispersant NNO, 6 parts of isonicotinic acid hydrazide and 10 parts of suberic acid dihydrazide, and then add 1 part of fatty alcohol polyoxyethylene ether [C 13 h 27 (CH 2 CH 2 O) 9 H] and 79.5 parts of deionized water solution, after stirring evenly, then transferred to a sand mill, sanded at a speed of 800 rpm for 8 hours, then added 2.5 parts of polyacrylate, at a speed of 100 rpm Stir at speed for 3 hours. After discharging, the chlorine-resistant enhancer is obtained.

[0063] The appearance of the chlorine-resistant enhancer prepared in this example is: a milky yellow dispersion liquid, and its composition is: 2.5% of polyacrylate, 16% of hydrazide derivatives, 2% of dispersant, and 79.5% of deionized water.

[0064] 2. Application

[0065] Continue dyeing and finishing the chlorine-resistant enhancer nylon and spandex swimsu...

Embodiment 3

[0068] Embodiment 3, the preparation and application of chlorine resistance promoting agent

[0069] 1. Preparation

[0070] Add 0.5 parts of fatty alcohol polyoxyethyl ether sodium sulfate and 2.5 parts of coconut oil fatty acid diethanolamide into 78 parts of deionized water, stir and dissolve, then add 5 parts of azelaic acid dihydrazide and 13 parts of isophthalic dihydrazide, After stirring evenly, it was transferred to a sand mill and sanded at a speed of 400 rpm for 20 hours, then 1.5 parts of polyacrylate was added and stirred for 1.5 hours at a speed of 200 rpm. After discharging, the chlorine-resistant enhancer is obtained.

[0071] The appearance of the chlorine-resistant enhancer prepared in this example is: a milky white dispersion, which consists of: 1.5% polyacrylate, 18% hydrazide derivatives, 2.5% dispersant, and 78% deionized water.

[0072] 2. Application

[0073] Continue dyeing and finishing the chlorine-resistant enhancer nylon and spandex swimsuit fab...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a chlorine fastness improver, and a preparation method and an application thereof. The chlorine fastness improver comprises, by mass, 1-5% of polyacrylate, 5-48% of a hydrazide derivative, 0.5-6% of a dispersant, and the balance of water. The hydrazide derivative concretely is one or more of octanedioic dihydrazide, azelaic dihydrazide, sebacic dihydrazide, dodecanedioic dihydrazide, isonicotinoylhydrazine, 1,2-diisonicotinic acid hydrazide, 1,2-dimethyl-1,2-dibenzoylhydrazine and isophthalic dihydrazide. The preparation method of the chlorine fastness improver is simple, and the chlorine fastness improver makes chinlon and spandex swimming suit dyed fabrics have the advantages of effectively improved chlorine fastness, small color change, good handle, good chlorine fastness and good water wash resistance.

Description

technical field [0001] The invention relates to a chlorine-resistant enhancer and its preparation method and application, belonging to the technical field of textile dyeing and finishing. Background technique [0002] Swimming pools must add a certain amount of chlorine water to sterilize and disinfect. Swimming suits will fade and change color after being soaked in chlorine-containing swimming pool water for a long time, resulting in a great change in the color and light of swimsuits, which deviates from the original style and affects the wearing experience of consumers. . Therefore, the color fastness to chlorine water is an important performance index of swimwear fabrics, and its color fastness to chlorine is usually required to reach level 4 or above (up to level 5). In order to improve the chlorine-resistant color fastness of polyamide spandex swimwear fabric, post-treatment with chlorine-resistant color-fixing agent is required. [0003] Patent CN201420041092.3 discl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M13/256D06M13/422D06M15/263D06M15/53D06P1/642D06P1/52D06P1/62D06P1/39D06P1/48D06P3/24D06P1/613
CPCD06M13/256D06M13/422D06M15/263D06M15/53D06M2101/34D06M2101/38D06P1/39D06P1/48D06P1/525D06P1/6133D06P1/625D06P1/6425D06P3/241
Inventor 罗灯洪袁东邓燕张继斌朱立太王亚静
Owner 东莞市中纺化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap