Flame retardant polypropylene plastic film

A flame-retardant polypropylene and plastic film technology, applied in the field of plastic film, can solve the problems of flammability and other problems, and achieve the effect of light weight, good flame-retardant performance and high hardness of plastic

Inactive Publication Date: 2016-08-24
ANHUI HUILONG PACKAGING CO LTD
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As a general-purpose material, polypropylene is widely used for its small specific gravity, easy processing, corrosion resistance, non-toxicity and excellent comprehensive performance. Now most polypropylene films have the problem of flammability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A flame-retardant polypropylene plastic film, the plastic film is composed of the following components in parts by weight: 55 parts of polypropylene resin, 17 parts of polypropylene, 5 parts of polyacryl alcohol, 4 parts of methyl methacrylate, stearic acid 4 parts of magnesium, 5 parts of propylene-based thermoplastic elastomer, 3 parts of plasticizer, 3 parts of toughening agent, and 4 parts of flame retardant.

[0014] Further, the polypropylene resin is a low-density polypropylene resin, and the weight average molecular weight of the polypropylene resin is 9000-12000.

[0015] Further, the plasticizer is dibutyl phthalate.

[0016] Further, the toughening agent is corn fiber.

[0017] Further, the flame retardant is zinc borate.

Embodiment 2

[0019] A flame-retardant polypropylene plastic film, the plastic film is composed of the following components in parts by weight: 58 parts of polypropylene resin, 12 parts of polypropylene, 6 parts of polypropylene alcohol, 5 parts of methyl methacrylate, stearic acid 4 parts of magnesium, 5 parts of propylene-based thermoplastic elastomer, 3 parts of plasticizer, 3 parts of toughening agent, and 4 parts of flame retardant.

[0020] Further, the polypropylene resin is a low-density polypropylene resin, and the weight average molecular weight of the polypropylene resin is 9000-12000.

[0021] Further, the plasticizer is dibutyl phthalate.

[0022] Further, the toughening agent is corn fiber.

[0023] Further, the flame retardant is zinc borate.

Embodiment 3

[0025] A flame-retardant polypropylene plastic film, the plastic film is composed of the following components in parts by weight: 60 parts of polypropylene resin, 11 parts of polypropylene, 6 parts of polypropylene alcohol, 4 parts of methyl methacrylate, stearic acid 4 parts of magnesium, 5 parts of propylene-based thermoplastic elastomer, 3 parts of plasticizer, 3 parts of toughening agent, and 4 parts of flame retardant.

[0026] Further, the polypropylene resin is a low-density polypropylene resin, and the weight average molecular weight of the polypropylene resin is 9000-12000.

[0027] Further, the plasticizer is dibutyl phthalate.

[0028] Further, the toughening agent is corn fiber.

[0029] Further, the flame retardant is zinc borate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of plastic products and discloses a flame retardant polypropylene plastic film. The flame retardant polypropylene plastic film is composed of the following components in parts by weight: 55-65 parts of polypropylene resin, 10-25 parts of polypropylene, 5-8 parts of polypropylene glycol, 3-8 parts of methyl methacrylate, 4 parts of magnesium stearate, 5 parts of a propenyl thermoplastic elastomer, 3 parts of a dibutyl phthalate plasticizer, 3 parts of a corn fiber toughening agent and 4 parts of a zinc borate flame retardant. The flame retardant polypropylene plastic film is added with the inorganic zinc borate flame retardant, so that a thin film has good flame retardant property and also has the advantages of light plastic, stable chemical properties, high hardness and good impact resistance.

Description

technical field [0001] The invention relates to a plastic film, in particular to a flame-retardant polypropylene plastic film. Background technique [0002] At present, with the development of the economy, plastics have been widely used in industry and life. China's plastic film industry is in a stage of vigorous development. It is reported that the demand for China's plastic film will grow at a rate of more than 9% every year. Moreover, with the continuous emergence of various new materials, new equipment and new processes, China's plastic films will be developed in the direction of diversified, specialized and multifunctional composite films. As a general-purpose material, polypropylene is widely used due to its small specific gravity, easy processing, corrosion resistance, non-toxicity and excellent comprehensive performance. Most polypropylene films now have the problem of flammability. Contents of the invention [0003] The object of the present invention is to prov...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L29/06C08L23/10C08K13/02C08K5/101C08K5/098C08K5/12C08K3/38
CPCC08L23/12C08J5/18C08J2323/12C08J2423/12C08L2201/02C08L2203/16C08L2205/025C08L2205/035C08L2207/04
Inventor 陈晖
Owner ANHUI HUILONG PACKAGING CO LTD
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com