Functional active purifying ceramic and preparation method and application thereof

A functional, enamel technology, applied in the field of ceramics, can solve problems such as inability to provide beneficial effects, and achieve the effect of promoting human health

Active Publication Date: 2016-09-28
陈源浩
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Ceramic products are now more and more used in daily life. In addition to being used as traditional decorations, they also provide a certain function of holding things. However, for the essence of ceramic products, they only provide a carrier and platform for holding, and cannot To provide more beneficial effects, how to improve the ceramic itself in order to provide more beneficial effects has become a research topic and mainstream direction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] A preparation method of functional active porcelain:

[0030] S1. Raw material pretreatment:

[0031] S11. Albite and potassium feldspar were calcined at 1020° C. for 5.5 hours, cooled to room temperature, ground, and passed through a 120-mesh sieve.

[0032] S12. Calcining quartz stone, medical stone, spinel, cordierite, and muyu stone at 870° C. for 8.5 hours, cooling to room temperature, grinding, and passing through a 120-mesh sieve.

[0033] S13. Calcining the clay at 600° C. for 10 hours, cooling to room temperature, grinding, and passing through a 120-mesh sieve.

[0034] S2. Raw material preparation

[0035] In terms of weight percentage, 13%-15% of quartz stone, 6%-8% of albite feldspar, 3%-5% of potassium feldspar, 5%-6% of medical stone, 5.9%-7% of rare earth elements, borax 2%-3%, 47%-59% clay, 1.5%-2.5% barium carbonate, 2.1%-3.2% spinel, 2.5%-3% cordierite are used as raw materials for ash, put into ball mill, add ash raw materials 80% to 100% of the t...

Embodiment approach

[0041] S1. Raw material pretreatment:

[0042] S11. Albite and potassium feldspar were calcined at 1020° C. for 5.5 hours, cooled to room temperature, ground, and passed through a 120-mesh sieve.

[0043] S12. Calcining quartz stone, medical stone, spinel, cordierite, and muyu stone at 870° C. for 8.5 hours, cooling to room temperature, grinding, and passing through a 120-mesh sieve.

[0044] S13. Calcining the clay at 600° C. for 10 hours, cooling to room temperature, grinding, and passing through a 120-mesh sieve.

[0045] S2. Raw material preparation

[0046] In terms of weight percentage, take 14% of quartz stone, 7% of albite feldspar, 4% of potassium feldspar, 5.5% of medical stone, 6.5% of rare earth elements, 2.5% of borax, 52.9% of clay, 2% of barium carbonate, spinel 2.8%, cordierite 2.8% as the raw materials of the raw material, put into the ball mill, add 80-100% water of the total weight of the raw materials, grind for 24 hours, stir at the same time, and let st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a functional active purifying ceramic and a preparation method and an application thereof, wherein a functional active purifying ceramic blank material is prepared from the following components by the weight percentage: 13%-15% of quartz stone, 6%-8% of albite, 3%-5% of potassium feldspar, 5%-6% of medical stone, 5.9%-7% of a rare earth element, 2%-3% of borax, 47%-59% of clay, 1.5%-2.5% of barium carbonate, 2.1%-3.2% of spinel, and 2.5%-3% of cordierite. A functional active purifying ceramic glaze material is prepared from the following components by the weight percentage: 4%-5% of nanosilver, 4%-4.8% of tourmaline, 7%-8% of medical stone, 5.5%-6.5% of Muyu-stone, 11%-13% of negative ions, 2%-3% of a germanium powder, 2.3%-3% of borax, and 56%-65% of clay. The invention has the beneficial effects that the functional active purifying ceramic and the preparation method and the application thereof are provided, and the active purifying ceramic material can play a role in purifying water quality, and can purify water quality while playing a container role when applied in ceramic products, so as to achieve an efficacy of promoting human body health.

Description

technical field [0001] The invention belongs to the technical field of ceramics, and relates to a functional living and clean porcelain and its preparation method and application. Background technique [0002] Ceramic products are now more and more used in daily life. In addition to being used as traditional decorations, they also provide a certain function of holding things. However, for the essence of ceramic products, they only provide a carrier and platform for holding, and cannot To provide more beneficial effects, how to improve the ceramic material itself in order to provide more beneficial effects has become a research topic and mainstream direction. Contents of the invention [0003] The object of the present invention is to provide a functional living porcelain to solve the above problems. [0004] Another object of the present invention is to provide a method for preparing the above-mentioned functional living porcelain. [0005] The third object of the presen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/13C03C8/14C02F1/30C02F1/50C02F1/00
CPCC02F1/00C02F1/30C02F1/50C03C8/14C04B33/131C04B2235/3418C04B2235/3427C04B2235/3472C04B2235/3481
Inventor 陈源浩
Owner 陈源浩
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com